Semiconductor device, its manufacturing method and substrate...

Details Semiconductor device, its manufacturing method and substrate... Semiconductor device, its manufacturing method and substrate...

2000-11-14

2002-11-19

Chaudhuri, Olik (Department: 2814)

Semiconductor device manufacturing: process

Making device or circuit emissive of nonelectrical signal

Substrate dicing

C438S039000, C438S042000

Reexamination Certificate

active

06482666

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to a semiconductor device, its manufacturing method and a substrate for manufacturing a semiconductor device, and more particularly to a semiconductor device, like a semiconductor laser, having cavity edges made by cleavage, its manufacturing method, and a substrate, like a wafer, used for manufacturing such a semiconductor device.
2. Description of the Related Art
Nitride III-V compound semiconductors, such as GaN, AlGaN and GaInN, made of a group III element, such as gallium (Ga), aluminum (Al) and indium (In), and nitrogen as a group V element, are direct-transitional semiconductors, and they have larger band gaps than those of semiconductors such as AlGaInAs and AlGaInP used in currently available semiconductor lasers. Therefore, they are expected to be widely applicable as light sources of high-integrated, high-density optical disc reproducing apparatuses and optical elements for full-color display devices, in form of short-wavelength semiconductor lasers for emission wavelengths in the band of 400 nm, light emitting diodes (LED) and other semiconductor light emitting devices capable of emitting ultraviolet to green light. Moreover, these nitride III-V compound semiconductors exhibit large saturation electron velocities under a high electric field, and are remarked as materials of electron-mobility devices such as field-effect transistors (FET) for high powers and high frequencies.
Semiconductor lasers, light emitting diodes and FETs using these nitride III-V compound semiconductors are made by epitaxially growing nitride III-V compound semiconductors on a substrate such as sapphire (Al
2
O
3
) substrate, for example.
In semiconductor lasers, in general, cavity edges must be made. In AlGaInAs, AlGaInP or InP semiconductor lasers, substrates and semiconductor layers grown thereon are cleavable, and cleavable surfaces are normally used as cavity edges of the semiconductor lasers.
In case of nitride III-V compound semiconductors, however, it is usually difficult to make stable cleavable surfaces because their crystallographic structures are hexagonal system wurtzite structures. Moreover, since these semiconductor lasers using nitride III-V compound semiconductors are usually made by growing nitride III-V compound semiconductors on sapphire substrates which are not cleavable, it has been difficult to fabricate semiconductor lasers using cleavable surfaces as cavity edges.
Japanese Patent Laid-Open Publications Nos. hei 8-222807 and hei 9-172223, for example, disclose methods for manufacturing GaN semiconductor lasers in which cavity edges are made by cleaving a sapphire substrate and III-V compound semiconductor layers stacked thereon.
More specifically, as shown in
FIG. 1
, these conventional methods for manufacturing GaN semiconductor lasers sequentially grow a GaN buffer layer
102
, n-type GaN contact layer
103
, n-type AlGaN cladding layer
104
, active layer
105
of a GaN/GaInN multiquantum well structure, p-type AlGaN cladding layer
106
and p-type GaN contact layer
107
on a c-plane sapphire substrate
101
by metal organic chemical vapor deposition (MOCVD).
Next made on the p-type GaN contact layer
107
is a resist pattern (not shown) in form of a predetermined stripe. Using the resist pattern as a mask, reactive ion etching (RIE) is conducted to selectively remove upper layers including an upper part of the n-type GaN contact layer
103
. As a result, the upper-lying part of the n-type GaN contact layer
103
, n-type AlGaN cladding layer
104
, active layer
105
, p-type AlGaN cladding layer
106
and p-type GaN contact layer
107
are patterned into a predetermined mesa structure extending in a direction. Numeral
108
denotes the mesa portion.
After the resist pattern is removed, the p-side electrode (not shown) is made on the p-type GaN contact layer
107
, and the n-side electrode (not shown) is made on the n-type GaN contact layer
103
in the partly removed region.
After that, the wafer-shaped sapphire substrate
101
having formed the laser structure is lapped from its bottom surface to adjust the thickness of the sapphire substrate
101
to approximately 150 &mgr;m. Then, in locations of the bottom surface of the sapphire substrate
101
for making cavity edges, which may be locations corresponding to (
11
-
10
)-oriented surfaces, straight cleavage-assist grooves
109
are made to extend in parallel to the (
11
-
20
)-oriented surfaces. Thus, in the direction parallel to the lengthwise direction of the mesa portion
108
, that is, in the cavity direction, a plurality of cleavage-assist grooves
109
are made periodically in intervals approximately the same as the cavity length of the GaN semiconductor lasers to be finally made.
The sapphire substrate
101
is next cleaved into bars together with the semiconductor layers thereon along the cleavage-assist grooves
109
to make opposite cavity edges, and the bars are divided into chips. As a result, the intended GaN semiconductor laser is completed.
The conventional method for manufacturing a GaN semiconductor laser can make cavity edges of cleavable surfaces (quasi-cleavable surfaces) more excellent in optical characteristics than those of cavity edges made by etching semiconductor layers forming the laser structure.
However, the conventional method for manufacturing a GaN semiconductor laser involves the following problems.
In most semiconductor lasers, the optical cavity length is designed to 1 mm or less, more particularly, in the range of 0.2 to 0.7 mm, approximately. However, in order to minimize the optical cavity length to these values, the thickness of the sapphire substrate
101
must be reduced by lapping. For example, unless the thickness of the sapphire substrate
101
is 150 &mgr;m or less, the sapphire substrate
101
and overlying semiconductor layers do not readily divide along the cleavage-assist groove
109
, and it was difficult to make cavity edges acceptable in optical evenness at the desired position.
Moreover, since the sapphire substrate
101
is chemically stable, it is difficult to selectively etch semiconductor layers made of nitride III-V compound semiconductors layers, or insulating films such as SiO
2
film and SiN film, which are made on the sapphire substrate. It is therefore difficult to chemically process the sapphire substrate
101
alone while protecting a part of the crystal growth surface and bottom surface. Therefore, in order to make cleavage-assist grooves
109
in the sapphire substrate
101
, dicing, scribing or other mechanical processing was necessary, and there arose problems in pattern accuracy and micro processing of the cleavage-assist grooves
109
.
Since the sapphire substrate
101
decreases in strength with a reduction in thickness, if the sapphire substrate
101
is made thinner, then the sapphire substrate
101
is apt to crack to its surface or break while the cleavage-assist grooves
109
are made on the bottom surface of the sapphire substrate
101
by using a dicer or scriber, for example. In this case also, it was impossible to make acceptable cavity edges. For the purpose of preventing cracks of breakage of the sapphire substrate
101
, there arose the need for minimizing varieties in thickness of the sapphire substrate
101
by controlling the thickness of sapphire substrate
101
after lapping, and the thickness of the sapphire substrate
101
in locations of the cleavage-assist grooves
109
after being made. Furthermore, as the sapphire substrate
101
was made thinner and thinner, warp of the substrate became too large to handle the substrate due to thermal stress caused by a difference in thermal expansion coefficient between the sapphire substrate
101
and semiconductor layers grown thereon, and/or damages by lapping. or the like.
OBJECTS AND SUMMARY OF THE INVENTION
It is therefore an object of the invention to provide a semiconductor device, its manufacturing method and a substrate used for manufacturing a semiconductor device, ensuring excellent cleavable

Affiliated with

Also associated with

Rating

Semiconductor device, its manufacturing method and substrate... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Semiconductor device, its manufacturing method and substrate..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Semiconductor device, its manufacturing method and substrate... will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2985214