Semi solid TiB 2 precursor mixture

Details Semi solid TiB 2 precursor mixture Semi solid TiB 2 precursor mixture

2011-04-19

2011-04-19

Bell, Bruce F (Department: 1759)

Compositions

Electrically conductive or emissive compositions

Metal compound containing

C252S519500, C252S519520, C252S520200, C252S520220, C252S506000, C252S507000, C423S277000, C423S278000, C423S289000, C423S291000, C423S297000

Reexamination Certificate

active

07927518

ABSTRACT:
The invention relates to a metal boride precursor mixture comprising a metal oxide and a boric oxide combined in such a manner so as to produce intimately linked clusters wherein the boric oxide is found within the metal oxide. Furthermore, the invention discloses a carbon composite material made with the metal boride precursor mixture and a carbonaceous component. Finally, the invention also teaches the process for preparing the metal boride precursor mixture comprising steps of providing a metal oxide and a boron oxide, mechanically mixing the metal oxide and the boron oxide at a temperature that liquefies the boron oxide and may impregnate the metal oxide to produce an intimately linked cluster of metal oxide and boric oxide.

REFERENCES:
patent: 5160698 (1992-11-01), Khazai et al.
patent: 5194234 (1993-03-01), Weimer et al.
patent: 6001236 (1999-12-01), de Nora et al.
patent: 6616829 (2003-09-01), Keller et al.
patent: 7462271 (2008-12-01), Dionne et al.
patent: 0115745 (1984-08-01), None
patent: 1141446 (2001-10-01), None
patent: 0115702 (2008-05-01), None
patent: 1004585 (1965-09-01), None
International Search Report, PCT/CA2007/001951, dated Jan. 21, 2008.

Affiliated with

Also associated with

Rating

Semi solid TiB 2 precursor mixture does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Semi solid TiB 2 precursor mixture, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Semi solid TiB 2 precursor mixture will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2638120