Sealing glass composition

Details Sealing glass composition Sealing glass composition

2002-07-25

2004-08-17

Group, Karl (Department: 1755)

Compositions: ceramic

Ceramic compositions

Glass compositions, compositions containing glass other than...

C501S015000, C501S022000, C501S025000, C501S026000, C501S044000, C065S059100, C065S406000, C065S412000

Reexamination Certificate

active

06777358

ABSTRACT:

FIELD OF THE INVENTION
This invention relates to glass compositions for seals, to sealing compositions including the glass composition and fillers, to methods of manufacturing such compositions, to methods of manufacturing a seal, to optical components having such seals, and to methods of offering a data transmission service over a fiber having such a seal.
BACKGROUND TO THE INVENTION
Forming a good seal with a strong bond between an optical fiber and an optical component is important as many optical components are subject to harsh operating conditions including vibration, high humidity and temperature cycling. Several problems are associated with the bonding process between a glass material and a non-glass material generally, and the high design specifications for optical components exacerbate these problems.
For example, temperature variations require any bond formed ideally to match the thermal coefficients of expansion of the optical fiber and the bonded part to mitigate thermal stress on the optical fiber. Determining the composition of a glass fixative having a sufficiently low melting point to enable an optical fiber to be bonded to a non-glass material without deforming the optical fiber, having a desired thermal coefficient of expansion, and good adhesive properties to both the silica of the optical fiber and the non-glass material is a difficult and complex task. Alternative processes using solder compounds such as Sn/Pb alloys were employed instead.
Most optical components include parts which have a non-glass composition, for example, metallic materials such as Kovar. One known method of bonding glass to such metallic materials requires the glass fiber to be metalised. The metalisation process required a fiber to be stripped to its core and given a metallic coating consisting of a bonding layer and a soldering layer. This enables bonds between the metalised glass fiber and the Kovar material to be soldered.
Metalisation processes have several disadvantages. The fibers have to have their adhesion verified and any masking material used must be removed. Such metalisation processes are time consuming and the fiber strength can be significantly reduced as a result (typically for example by 30%). Other disadvantages include the extensive handling of fibers required by such processes and the associated high fiber breakage rate, and the capital expenditure on plant required by such processes. The preparation of the fibers for metalisation and soldering is moreover time-consuming Yet another disadvantage of fiber fixing using metalisation processes is that no reworking is possible during either the metalisation or soldering stages. A further disadvantage of metalisation processes for fiber fixing is that the soldering process can leave behind potentially corrosive fluxes. The soldering process usually involves the use of acidic, organic fluxes and the organic residues can adversely affect laser or optical performance if not cleaned off effectively.
The cleaning process itself can cause concerns for product performance which need addressing. These processes also have the effect of weakening the fiber because of the pre-cleaning required and because of stress concentrators associated with the metalisation. The softer solders can suffer creep and hence be detrimental to alignment stability. In complex optical components, a further problem is the necessity of preventing preexisting bonds from being degraded when subsequent bonds are formed in the near vicinity.
Alternatives have also been developed such as resin fixing-uvlight and/or heat curing. However, the resins have poor high temperature performance and lengthy cure cycles with messy dispensing and out gassing during processing.
The bonds must often be sufficiently strong and intact to form a hermetic seal between the optical fiber and the corresponding portion of the optical component to isolate the interior of the optical component from the external atmosphere. This enables the atmosphere within the optical component to be isolated and for non-air atmospheres or pure air atmospheres to be used. Moreover, the moisture content of the interior can then be controlled. It is thus important for any bond formed to be sufficiently strong to retain the hermeticity of the seal when subject to thermal stress and/or vibration and/or shock.
An example of a typical requirement is to provide a means for passing an optical fiber hermetically (<1×10−9 Atmos cc/s) through the wall of a package. At the same time the fiber should not be weakened and the optical performance of the fiber should be unimpaired. Another challenge is to provide a quick, simple and reliable means of fixing a fiber position very accurately (sometimes to less than 0.1 um) subsequent to alignment and keeping it there for the lifetime of the product. The fixing method should be clean in itself and the resultant assembly should be chemically, mechanically and optically stable.
One current technique for sealing fiber tails to optical components without metallising the fibers involves using a low melting point glass to make a hermetic seal between the fiber and a Kovar hypo tube. To carry out this operation a glass preform is heated to 450° C. approximately in an induction coil. The nominal sintering temperature to manufacture the glass preform is 310° C.
An example of a commercially available low melting point (LMP) glass usable for the hermetic seal, developed by NEG (Nippon Electric Glass), is shown in U.S. Pat. No. 5,346,863. It involves a PbO B
2
O
3
type glass matrix, mixed with a ceramic filler powder to reduce the temperature coefficient of expansion (TCE) to match the glass and metal materials being bonded. Due to environmental pressures there is a need for alternative or better glasses,
SUMMARY OF THE INVENTION
It is an object of the present invention to provide improved apparatus and methods. According to a first aspect of the present invention, there is provided a sealing glass composition consisting essentially of: 70-75 wt % of PbO, 3-7 wt % of PbF
2
, 5-8 wt % of Bi
2
O
3
, 5-7 wt % of B
2
0
3
, 2-5 wt % of ZnO, 1-7 wt % of Fe
2
O
3
, 0-2 wt % of CuO, 0-3% of TeO
2
, and a trace <0.2% of MnO
2
, the composition having a flow temperature of <350° C.
An advantage of this is that it can be used to make seals which can be flowed at low temperatures, using different constituents to those used in prior compositions. This helps reduce the risk of damage to temperature sensitive materials near the seals, for example polymer coatings of optical fibers. Also, this composition can achieve such low flow temperatures without excessive degradation of other useful properties such as low viscosity, low TCE, good adhesion to glass and metals, low permeability of air, good long term hydrolytic stability, and so on. It can be mixed with a filler such as a ceramic powder, to enable the TCE to be matched accurately to the materials being sealed.
It can be used to fix silica fiber into electro-optic devices to achieve hermetic joints and to give high mechanical stability fixing of the fiber and other optical train related components for example. It can be heated to flow to form a seal using a Nd/YAG, CO
2
or diode laser, hot plate, hot air and induction heating. Of these the preferred heat sources are induction heating and the Nd/YAG laser. It can give substantial cost reduction, performance improvement and new design options whilst being quick, clean, repeatable and stable. It has many possible applications. The process and materials are much more environmentally friendly than prior processes and materials. Material delivery can be in various forms including powder, preform and paste (allowing screen printing options).
As a preferred feature for a dependent claim, the temperature coefficient of expansion is between 4 and 12 ppm/
−
C. This is another key property to ensure long term reliability of the seal in realistic conditions of temperature changes. This TCE is the value before matching by adding filler. It is useful to keep this value low so th

Affiliated with

Also associated with

Rating

Sealing glass composition does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Sealing glass composition, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Sealing glass composition will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3317306