Stock material or miscellaneous articles – All metal or with adjacent metals – Microscopic interfacial wave or roughness
Reexamination Certificate
2000-06-15
2002-04-09
Jones, Deborah (Department: 1775)
Stock material or miscellaneous articles
All metal or with adjacent metals
Microscopic interfacial wave or roughness
C428S652000, C428S655000, C428S680000, C428S687000, C428S937000, C427S456000
Reexamination Certificate
active
06368727
ABSTRACT:
BACKGROUND OF THE INVENTION
The invention relates to bond coats. In particular, the invention relates to roughened bond coats for thermal barrier coating systems.
Thermal barrier coating systems are used in hot-section components in turbine and turbine components, for example components of jet engines and gas turbines. The thermal barrier coating system insulates the turbines from high temperatures during thermal cycling. Thermal barrier coating systems include a thermal barrier coating (TBC) disposed on a bond coat, which in turn is disposed on a substrate. The thermal barrier coating normally comprises zirconia, for example such as one of a stabilized zirconia and a partially-stabilized zirconia (PSZ). The bond coat typically comprises an oxidation-resistant metallic layer disposed between the TBC and substrate (turbine component). The TBC is adhered to the bond coat typically by mechanical interlocking, so the bond coat provides oxidation resistant to the substrate and a relatively rough surface. The bond coat surface generally has Ra (Arithmetic Average Roughness (Ra) as determined from ANSI/ASME Standard B461-1985) values over about 350 mainly by mechanical interlocking. So the function of the bond coat is to provide oxidation resistant to the substrate and a relatively rough surface, preferably with Ra values over about 350 microinches, for the TBC to adhere to the substrate. Thus, the TBC is disposed over the turbine component can provide thermal insulation.
FIG. 1
is a schematic representation of a known thermal barrier coating system
1
. A substrate
10
comprises an underlying part of a component, for example a turbine component. A bond coat
12
is disposed on the substrate
10
. The bond coat is disposed on the substrate
10
by any appropriate method, for example, but not limited to, thermal spray processes, such as vacuum plasma spray (VPS), air plasma spray (APS) and hyper-velocity oxy-fuel (HVOF) spray processes.
The structure and roughness of bond coat surface
13
are dependent on the spray process. Bond coats deposited by a VPS process are typically dense and free of oxides. Therefore, VPS-applied bond coats provide protection at high temperatures against oxidation. The VPS application process disposes fine powders, and thus, VPS-applied bond coats are typically dense, for example having a density greater than about 90% of its theoretical density, but have relatively smooth surfaces. Consequently, a TBC does not adhere well to a VPS bond coat.
An air plasma spray (APS) process produces rough bond coats because of large powders used in APS. The large powders possess a relatively high heat capacity; however, the APS-applied bond coats contain high amounts of oxides. Also, APS-applied bond coats possess a relatively low porosity due to the oxidation environment and low momentum of the powders. Although APS-applied bond coats provide better TBC adhesion due to their roughness, they are more prone to oxidation because of their relatively high oxide levels and relatively low porosity.
Bond coats deposited by HVOF are sensitive to particle size distributions. Dense and oxide-free bond coats can be deposited by HVOF using very lean conditions (low oxygen amounts) and finer particles, for example particles with a size about −325+10 &mgr;m. The surface roughness of HVOF-applied bond coats is relatively smooth. Rough bond coats can be deposited by HVOF using coarser powders, for example particles with a size about −230+325, however a low HVOF flame temperature is needed. The low flame temperatures results in the bond coat comprising un-melted powders, therefore the coating is porous and less dense.
A TBC
14
is disposed on the bond coat
12
and forms a surface
15
against the surface
13
. The TBC
14
is disposed on the bond coat
12
by any appropriate process to adhere (bond) to the bond coat. The TBC surface
15
and bond coat surface
13
define an interfacial area
16
at their adjoining surfaces.
Effectiveness of a thermal barrier coating system during thermal cycling is compromised by de-bonding of the TBC and bond coat, for example at the TBC and bond coat interfacial area. De-bonding can be caused by a poor TBC and bond coat adhesion or lack of accommodation of thermal expansion mismatch between the TBC and bond coat. The lack of adhesion is characteristic of smooth adjoining surfaces where total surface areas are minimal. The thermal expansion mismatch between the TBC and bond coat results from different coefficients of thermal expansion of the materials used for these features. If the different coefficients of thermal expansion of the adhered elements are large, one element expands much more than the other, and separation and de-bonding occur at the interfacial areas. De-bonding of the TBC and bond coat is undesirable as the insulation effect of the thermal barrier coating system will be lost at TBC separation.
Therefore, it is desirable to use a very dense and rough bond coat that provides oxidation resistance and promotes enhanced adhesion between the TBC and the bond coat. The oxidation resistance and enhanced adhesion assist in preventing de-bonding. The adhesion between the TBC and bond coat can be increased by increasing an area at an interfacial area mating surface of adhered elements. Increasing a roughness of the bond coat provides an increased area and enhanced mechanical interlocking between the bond coat and TBC. Increasing a bond coat's roughness also provides an increased interfacial surface area for accommodation of any thermal mismatch, with respect to non-roughened bond coats.
SUMMARY OF THE INVENTION
The invention overcomes the above noted deficiencies of known thermal barrier coating systems. The invention sets forth a method of forming a dense bond coat. The method comprises providing a metal powder mixture and disposing the metal powder mixture onto a substrate. The disposing is conducted by a thermal spray process such as high velocity oxygen fuel spraying, to form a dense bond coat possessing an uneven, undulated, and irregular surface.
A dense (for example at least about 95% its theoretical density), bond coat is also provided by the invention, where the bond coat comprises a roughened layer possessing an uneven, undulated, and irregular surface. The layer is formed of a metal powder mixture disposed on a substrate by high velocity oxygen fuel spraying. The metal powder mixture comprises a first powder having a first melting point and a second powder having a second melting point that is higher than the first melting point.
Another embodiment of the invention provides a method of forming a thermal barrier coating system. The thermal barrier coating system comprises a thermal barrier system and a dense (for example at least about 95% its theoretical density), roughened bond coat disposed on a substrate, where the roughened bond coat possesses an uneven, undulated, and irregular surface. The method comprises disposing a bond coat on a substrate and disposing a thermal barrier coating on the bond coat. The bond coat is disposed by providing a metal powder mixture and disposing the metal powder mixture onto the substrate by high velocity oxygen fuel spraying.
Yet another embodiment of the invention provides a thermal barrier coating system. A thermal barrier coating system comprises a dense (for example at least about 95% its theoretical density), roughened bond coat disposed on a substrate and a thermal barrier coating disposed on the roughened bond coat. The dense roughened bond coat comprises a layer possessing an uneven, undulated, and irregular surface. The layer is formed of a metal powder mixture disposed on a substrate by high velocity oxygen fuel spraying. The metal powder mixture comprises a first powder having a first melting point and a second powder having a second melting point that is higher than the first melting point. The TBC is then applied by a spraying process, such as air plasma spray (APS).
These and other aspects, advantages and salient features of the invention will become apparen
Jackson Melvin Robert
Lau Yuk-Chiu
Ritter Ann Melinda
General Electric Company
Johnson Noreen C.
Jones Deborah
Santandrea Robert P.
Savage Jason
LandOfFree
Roughened bond coat for a thermal barrier coating system and... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Roughened bond coat for a thermal barrier coating system and..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Roughened bond coat for a thermal barrier coating system and... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2924166