Metal treatment – Stock – Carburized or nitrided
Reexamination Certificate
1997-07-28
2001-01-09
Sheehan, John (Department: 1742)
Metal treatment
Stock
Carburized or nitrided
C148S318000, C148S906000, C384S492000, C384S912000
Reexamination Certificate
active
06171411
ABSTRACT:
FIELD OF THE INVENTION
This invention relates to a rolling bearing used in automobiles, agricultural machinery, and constructional machinery. More particularly, it relates to a rolling bearing which has a long bearing life even under contaminated lubrication as demanded for use in driving systems, such as a transmission and an engine.
BACKGROUND OF THE INVENTION
Rolling bearings are generally made of bearing steel or case hardening steel which is to be carburized. Since rolling bearings are to be used with a shearing stress repeatedly imposed thereon under a high contact pressure, bearing steel is subjected to hardening and tempering, and case hardening steel is subjected to carburizing followed by hardening and tempering in order to secure a rolling fatigue life withstanding the shearing stress.
Compared with case hardening steel requiring carburizing, bearing steel is largely advantageous in terms of cost of heat treatment, reducing the total cost of production. However, bearing steel is disadvantageous from the standpoint of workability of the raw material and has an insufficient rolling life under a severe running condition. In order to overcome these disadvantages of bearing steel, techniques for improving the raw material workability to further reduce the production cost and for extending the rolling life have been proposed as disclosed, e.g., in JP-A-8-3689 and JP-A-8-53735 (the term “JP-A” as used herein means an “unexamined published Japanese patent application”).
On the other hand, case hardening steel is, while economically disadvantageous, advantageous for its longer rolling life. In recent years, however, the working environment of bearings has been getting stricter. In particular, there has been a demand for extension of a life under contaminated lubrication as well as reduction of cost. Under these circumstances, the state-of-the-art case hardening steel cannot sufficiently meet the demands of life and cost.
The applicant previously proposed in JP-A-2-125841 a long-life rolling bearing made of an economical raw material which has a reduced Cr content (Cr is ready to precipitate into a carbide harmful to the life) and has added thereto as much Mn as the reduction of Cr to secure hardenability and which has an increased carbon content to improve productivity in heat treatment.
JP-A-8-4774 proposes increasing the carbon content of a raw material thereby to cut the cost of heat treatment, adding Si to the raw material, and subjecting the raw material to carburizing thereby to improve the life under contaminated lubrication.
According to the conventional techniques as taught by JP-A-8-3689 and JP-A-8-53735, somewhat extended durability of bearing steel has been attained, but no considerations has been given to the life under contaminated lubrication to cope with the recent environment of use of bearings.
The technique of JP-A-2-125841 aims at obtaining a rolling bearing having a long life under contaminated lubrication by retaining austenite in the surface layer in a proportion of 25 to 45% by volume. This can be achieved by setting the dissolved carbon content of at least the surface layer at 0.8% by weight or more so as to keep the retained austenite content within the above range. However, considering the case in which the carbonitrided surface is ground, the machinability (grindability) greatly varies depending on the surface nitrogen content, and the surface nitrogen content is decided by the alloying elements of the raw material and the conditions of heat treatment. From this viewpoint the technique of JP-A-2-125841 still has room for further improvement for reducing the total production cost, while paying due attention to efficiency of carburizing and grindability after carbonitriding as well.
Attention is not paid to the grindability after heat treatment in JP-A-8-4774, either. That is, considerations for not only grindability but materials, heat treatment, etc. are insufficient in making a reduction of production cost.
In other words, although the above-mentioned techniques have achieved an extended bearing life through improvement on bearing steel raw material that is economically advantageous, the life reached is still not equal to that of bearings made of carburized or carbonitrided case hardening steel. On the other hand, attempts to reduce the cost of case hardening steel that is to be carburized or carbonitrided have not succeeded in providing bearings competitive in price with normally hardened articles made of bearing steel.
SUMMARY OF THE INVENTION
Attention being paid to these problems of conventional techniques, an object of the present invention is to provide a rolling bearing which has a long life under contaminated lubrication and yet is less expensive than conventional bearings made of bearing steel.
The present invention provides a rolling bearing comprising an inner race, an outer race, and a plurality of rolling elements, wherein at least one of the inner race, outer race, and rolling elements is formed of an alloy steel comprising 0.7 to 0.9% by weight of C, 0.1 to 0.5% by weight of Si, 0.5 to 1.1% by weight of Mn, 0.1 to 0.6% by weight of Cr, and the balance of Fe and unavoidable impurity elements, and has a surface layer containing at least one of, carbon and nitrogen atoms, with the proviso that the carbon content is 0.8 to 1.4% by weight and the nitrogen content is 0.01 to 0.3% by weight. It is particularly preferred that at least one of the inner race and outer race satisfies such requirements.
In order to accomplish the above object, the inventors of the present invention have thoroughly studied all the steps involved in a process for producing a rolling bearing which comprises forging (cold forging, warm forging, hot forging, etc.), rolling and turning if necessary, heat treatment, and grinding and various possible combinations of raw materials applicable to bearings and methods of heat treatment. As a result, they have developed a novel rolling bearing having excellent rolling fatigue life under contaminated lubrication which is obtained from a raw material suitable to every working step for completing a bearing and containing minimum alloying elements and thus reached the present invention.
REFERENCES:
patent: 4642219 (1987-02-01), Takata et al.
patent: 4871268 (1989-10-01), Furumura et al.
patent: 5352303 (1994-10-01), Murakami et al.
patent: 5413643 (1995-05-01), Murakami et al.
patent: 5705124 (1998-01-01), Ochi et al.
patent: 0626468 (1994-11-01), None
patent: 1354828 (1974-05-01), None
patent: 2294058 (1996-04-01), None
patent: 2294270 (1996-04-01), None
patent: 2306506 (1997-05-01), None
Okita Shigeru
Tanaka Susumu
NSK Ltd.
Sheehan John
Sughrue Mion Zinn Macpeak & Seas, PLLC
LandOfFree
Rolling bearing does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Rolling bearing, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Rolling bearing will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2495065