Roll of winding equipment in rolling factory

Roll or roller – Concentric layered annulus – Specific composition

Patent

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

492 58, B23P 1500

Patent

active

059446447

DESCRIPTION:

BRIEF SUMMARY
TECHNICAL FIELD

The present invention relates to a roll of a down coiler (hereinafter simply referred to as "each roll" or "roll"), provided within a winding equipment in a rolling factory as an iron manufacturing arrangement, wherein said roll has a hardened buildup substrate on a surface of its body and a carbide-particle-dispersed type autogenous-alloy-sprayed layer upon said substrate.


BACKGROUND ART

Generally, each roll of a winding equipment in a rolling factory suffers abrasion due to: corrosive environment caused by contact with cooling water and high temperature passing plate material (900.degree. C. or less); sliding on the passing plate material; and impact at the time of inrushing of the passing plate material.
Performance required for, each roll includes, mainly, gripping force on passing plate material (a friction coefficient), plate flaw (slip flaw and flaw by seizure) resistance, and the like.
As for an arrangement of rolls, as shown in FIG. 2, an equipment for winding and coiling high temperature plate material 10 of 400-900.degree. C., which has been rolled to standard size, comprises, for each coiler, upper and lower pinch rolls 11, 1, and wrapper rolls (unit rolls) 6-9 located around each coiler mandrel, and sometimes, comprises pinch rolls 11, 1 located independently in front of a group of coilers. The pinch rolls and wrapper rolls perform tension adjustment, conveyance, and a change of direction, between apparatuses after and before them, i.e., between a finishing mill and a coiler, contributing to smooth winding in the coiler and to putting a winding shape in good order.
Surfaces of the pinch rolls 1 shown in FIG. 2 suffer abrasion due to contact with and slide on the high temperature passing plate material 10 accompanying pressing force of the upper pinch rolls 11, and due to corrosion by cooling water. Further, the wrapper rolls (unit rolls) are used in the similar severe conditions.
If a shape of a roll body is changed by the above-described abrasion, it accompanies changes in the pinch force and pressing force on the passing plate material, and becomes cause of deformation of the winding shape and generation of plate flaws. Therefore, usually, each roll is exchanged in a short life period of about one month, producing a great loss respecting an operating ratio of the equipment and repair cost.
For pinching and conveying the passing plate material, it is necessary to ensure a suitable friction coefficient of the roll surface. When the value of the friction coefficient is small, there arises severe slips or seizure, inviting a loss such as flaws in the passing plate material, exchange of rolls, or the like.
As a roll in the winding equipment, one of the steel group such as a hardened buildup product, a tinned product, or a forged steel product is mainly used. Those products, however, have reached their limit of performance for attaining both the abrasion resistance and plate flaw resistance, and attaining stable operation and stable operational cost property. These products do not have sufficient abrasion resistance, conveyance resistance, and plate flaw resistance at the same time.
Japanese Laid-Open Unexamined Patent Publication No. 55-149710 suggests a roll having spalling resistance and abrasion resistance, which is obtained by hardened buildup welding with given conditions, on a surface of a roll body of the iron group, and further building up an autogenous-alloy-sprayed layer on the welded surface. The object of that invention, however, is very wide one, "rolls relating to iron manufacturing".
As for the lower pinch roll, importance lies in its performance in applying a pinch force on the passing plate material and maintaining suitable conveyance property, so as to prevent plate flaws and to put a winding shape in good order.
According to the specifications of the surface film of the roll according to Japanese Laid-Open Unexamined Patent Publication No. 55-149710, the friction coefficient is in an extremely low level, which becomes cause of plate flaws and unstableness of

REFERENCES:
patent: 4771524 (1988-09-01), Barbezat et al.
patent: 4796342 (1989-01-01), Miihkinen
patent: 5161306 (1992-11-01), Nakahara et al.
patent: 5445589 (1995-08-01), Shimizu

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Roll of winding equipment in rolling factory does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Roll of winding equipment in rolling factory, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Roll of winding equipment in rolling factory will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2424842

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.