Metal founding – Process – Shaping liquid metal against a forming surface
Patent
1993-01-08
1994-09-27
Bradley, P. Austin
Metal founding
Process
Shaping liquid metal against a forming surface
164 80, 164102, 264 44, 428614, B22D 1914
Patent
active
053500040
DESCRIPTION:
BRIEF SUMMARY
DESCRIPTION
1. Technical Field
The present invention relates to a novel process for forming metal matrix composite bodies. Particularly, in a preferred embodiment of the present invention directed to forming metal matrix composites by a spontaneous infiltration technique an infiltration enhancer and/or an infiltration enhancer precursor and/or an infiltrating atmosphere are in communication with a rigidized filler material or a rigidized preform, at least at some point during the process, which permits molten matrix metal to spontaneously infiltrate the rigidized filler material or rigidized preform. Such spontaneous infiltration occurs without the requirement for the application of any pressure or vacuum.
2. Background Art
Composite products comprising a metal matrix and a strengthening or reinforcing phase such as ceramic particulates, whiskers, fibers or the like, show great promise for a variety of applications because they combine some of the stiffness and wear resistance of the reinforcing phase with the ductility and toughness of the metal matrix. Generally, a metal matrix composite will show an improvement in such properties as strength, stiffness, contact wear resistance, coefficient of thermal expansion (C.T.E.), density, thermal conductivity and elevated temperature strength retention relative to the matrix metal in monolithic form, but the degree to which any given property may be improved depends largely on the specific constituents, their volume or weight fraction, and how they are processed in forming the composite. In some instances, the composite also may be lighter in weight than the matrix metal per se. Aluminum matrix composites reinforced with ceramics such as silicon carbide in particulate, platelet, or whisker form, for example, are of interest because of their higher specific stiffness (e.g., elastic modulus over density), wear resistance, thermal conductivity, low coefficient of thermal expansion (C.T.E.) and high temperature strength and/or specific strength (e.g., strength over density) relative to aluminum.
Various metallurgical processes have been described for the fabrication of aluminum matrix composites, including methods based on powder metallurgy techniques and liquid-metal infiltration techniques which make use of pressure casting, vacuum casting, stirring, and wetting agents. With powder metallurgy techniques, the metal in the form of a powder and the reinforcing material in the form of a powder, whiskers, chopped fibers, etc., are admixed and then either cold-pressed and sintered, or hot-pressed. The maximum ceramic volume fraction in silicon carbide reinforced aluminum matrix composites produced by this method has been reported to be about 25 volume percent in the case of whiskers, and about 40 volume percent in the case of particulates.
The production of metal matrix composites by powder metallurgy techniques utilizing conventional processes imposes certain limitations with respect to the characteristics of the products attainable. The volume fraction of the ceramic phase in the composite is limited typically, in the case of particulates, to about 40 percent. Also, the pressing operation poses a limit on the practical size attainable. Only relatively simple product shapes are possible without subsequent processing (e.g., forming or machining) or without resorting to complex presses. Also, nonuniform shrinkage during sintering can occur, as well as nonuniformity of microstructure due to segregation in the compacts and grain growth.
U.S. Pat. No. 3,970,136, granted Jul. 20, 1976, to J. C. Cannell et al., describes a process for forming a metal matrix composite incorporating a fibrous reinforcement, e.g. silicon carbide or alumina whiskers, having a predetermined pattern of fiber orientation. The composite is made by placing parallel mats or felts of coplanar fibers in a mold with a reservoir of molten matrix metal, e.g., aluminum, between at least some of the mats, and applying pressure to force molten metal to penetrate the mats and surround the oriented fibers. Molte
REFERENCES:
patent: 3031340 (1962-04-01), Girardot
patent: 3149409 (1964-09-01), Maruhn
patent: 3364976 (1968-01-01), Reding et al.
patent: 3396777 (1968-08-01), Reding, Jr.
patent: 3547180 (1970-12-01), Cochran et al.
patent: 3608170 (1971-09-01), Larson et al.
patent: 3718441 (1973-02-01), Landingham
patent: 3864154 (1975-02-01), Gazza et al.
patent: 3868267 (1975-02-01), Gazza et al.
patent: 3915699 (1975-10-01), Umehara et al.
patent: 3969553 (1976-07-01), Kondo et al.
patent: 3970136 (1976-07-01), Cannell et al.
patent: 4076888 (1978-02-01), Perugin et al.
patent: 4082864 (1978-04-01), Kendall et al.
patent: 4148894 (1979-04-01), Hillig et al.
patent: 4232091 (1980-11-01), Grimshaw et al.
patent: 4376803 (1983-03-01), Katzman
patent: 4376804 (1983-03-01), Katzman
patent: 4450207 (1984-05-01), Donomoto et al.
patent: 4455135 (1984-09-01), Pinkhasov
patent: 4473103 (1984-09-01), Kenney et al.
patent: 4548253 (1985-10-01), Funatani et al.
patent: 4548774 (1985-10-01), Akiyama
patent: 4559246 (1985-12-01), Jones
patent: 4570316 (1986-02-01), Sakamaki et al.
patent: 4630665 (1986-12-01), Novak et al.
patent: 4657065 (1987-04-01), Wada et al.
patent: 4659593 (1987-04-01), Rocher et al.
patent: 4662429 (1987-05-01), Wada et al.
patent: 4673435 (1987-06-01), Yamaguchi et al.
patent: 4713111 (1987-12-01), Cameron et al.
patent: 4753690 (1988-06-01), Wada et al.
patent: 4777097 (1988-10-01), Kubo et al.
patent: 4802524 (1989-02-01), Donomoto
patent: 4828008 (1989-05-01), White
patent: 4871008 (1989-10-01), Dwivedi et al.
patent: 4885263 (1989-12-01), Brockmeyer
patent: 4932099 (1990-06-01), Corwin
patent: 4995444 (1991-02-01), Jolly
patent: 5000248 (1991-03-01), Newkirk
patent: 5141683 (1992-08-01), Hyndman
F. Delannay, L. Froyen, and A. Deruyttere, "Review: The Wetting of Solids by Molten Metals and Its Relation to the Preparation of Metal-Matrix Composites", Journal of Materials Science, vol. 22, No. 1, pp. 1-16, Jan. 1987.
G. R. Edwards and D. L. Olson, "The Infiltration Kinetics of Aluminum in Silicon Carbide Compacts", Annual Report from Center for Welding Research, Colorado School of Mines, under ONR Contract No. M00014-85-K-0451, DTIC Report AD-A184 682, Jul. 1987.
A. Mortensen, M. N. Gungor, J. A. Cornie, and M. C. Flemings "Alloy Microstructures in Cast Metals Matrix Composites", Journal of Metals, vol. 38, No. 3, pp. 30-35, Mar. 1986.
International Search Report for International Patent Application Ser. No. PCT/US91/03233.
A. Mortensen, J. A. Cornie, and M. C. Flemings, "Solidification Processing of Metal-Matrix Composites", Journal of Metals, vol. 40, No. 2, pp. 12-19, Feb. 1988.
B. D. Sparks and F. W. Meadus, "The Development of an Infiltrated Lead/Iron Composite Material For Use as a Non-toxic Bird Shot", Composites, pp. 37-39, Jan. 1978.
Aghajanian Michael K.
Becker Kurt J.
Rocazella Michael A.
Antolin Stanislav
Bradley P. Austin
Lanxide Technology Company, LP
Mortenson Mark C.
Pelto Rex E.
LandOfFree
Rigidized filler materials for metal matrix composites and precu does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Rigidized filler materials for metal matrix composites and precu, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Rigidized filler materials for metal matrix composites and precu will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1260361