Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Mixing of two or more solid polymers; mixing of solid...
Reexamination Certificate
1999-08-20
2002-03-12
Mullis, Jeffrey (Department: 1711)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Mixing of two or more solid polymers; mixing of solid...
C527S300000, C527S311000, C527S313000, C527S314000, C106S031250, C106S031680
Reexamination Certificate
active
06355734
ABSTRACT:
CROSS-REFERENCE TO RELATED APPLICATIONS
STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT
BACKGROUND OF THE INVENTION
In general, the present invention relates to resin-fortified emulsion polymer compositions comprising a sugar-based vinyl monomer.
Emulsion Polymers
High molecular weight emulsion polymers are useful in the coatings and inks industry. However, high molecular weight emulsion polymer technology has some drawbacks. Problems associated with high molecular weight emulsion polymer systems include wetting and adherency problems, mechanical instability, freeze/thaw instability and inability to biodegrade or be repulped.
U.S. Pat. No. 4,151,143, issued to Blank, et al., discloses a surfactant-free polymer emulsion coating composition and a method for preparing the same. U.S. Pat. No. 4,179,417, issued to Sunada, et al., discloses a composition for water based paints containing a water soluble resin and a water dispersible polymer which are employed as water based paints and can optionally contain a cross linking agent. Canadian Pat. No. 814,528, issued Jun. 3, 1969, discloses low molecular weight alkali soluble resin, resin cuts and method of their preparation and purification. U.S. Pat. No. 4,820,762 discloses resin-fortified emulsion polymers that are created by addition of a low molecular weight support resin during the emulsion polymerization process.
Sugar-based Vinyl Monomers
U.S. Pat. No. 5,827,199 discloses copolymers prepared from alkyl polyglycoside maleic acid esters (sugar monomer) and vinyl monomers. These water borne copolymers contain sugar units in their polymeric structure introduced by way of the bifunctional sugar monomer. Acrylic copolymers containing around 10% sugar monomer have been found to be noninterfering in paper recycling, while copolymers containing at least 40% sugar monomer are biodegradable under composting conditions as per ASTM D5338 (see Adhesives Age 41(2):24, 1998).
BRIEF SUMMARY OF INVENTION
The resin-fortified emulsion polymers of the present invention provide suitable mechanical, physical and performance properties when compared to conventional emulsion polymers and represent an advance in emulsion polymerization technology. It is an object of the present invention to provide novel copolymers that are useful in biodegradable, repulpable inks, primers coatings, overprint coatings and related products used on paper and paperboard, synthetic and natural polymer films, metallized films and metal foils and sheets, as well as combinations thereof. These printed or decorated substrates could be used in packaging, publication, commercial printing, wallpaper, specialty and other related applications.
Briefly, in accordance with the present invention, a resin-fortified emulsion polymer is prepared by exposing a resin to an emulsion polymerization reaction mixture comprising a sugar-based vinyl monomer and other vinyl comonomers. The resin is a low molecular weight polymer and is soluble or dispersible in water or alkali solutions. The emulsion polymerization reaction mixture contains any monomers employed in emulsion polymerization reactions and additionally comprises a sugar-based vinyl monomer. The resulting resin-fortified emulsion polymers have enhanced performance for coatings, ink and graphic art applications and are recycling friendly.
DETAILED DESCRIPTION OF THE INVENTION
The present invention is both a method of obtaining a resin-fortified emulsion polymer comprising a sugar-based vinyl monomer and the polymer itself. When used herein the term “emulsion polymer” refers to any polymer prepared by emulsion polymerization. Such polymers are formed by the polymerization of one or more monomers capable of undergoing free radical emulsion polymerization. When used herein the term “resin” encompasses all low molecular weight resins of from about 500 to about 20,000, and preferably about 500 to 10,000, number average molecular weight which are soluble or dispirsible in water or alkali.
In practicing the present invention, a solution polymer support resin is exposed to an emulsion polymerization reaction mixture during the emulsion polymerization reaction.
Typically, the solution polymer support resin is first added to a reactor under an inert atmosphere. Water, surfactant and buffer are then added with agitation and brought to reaction temperature. A pre-emulsion is prepared separately by mixing together water, surfactant and the monomers including the sugar-based vinyl monomer. The pre-emulsion step is preferred because the sugar-based vinyl monomer may not be soluble in the monomers and may not form a single homogenous phase. A surfactant is required to cosolubilize the monomers and allow a homogenous feed to be fed to the reactor during the starve-fed polymerization process to ensure a random incorporation of the monomers. The charge initiator, preferably a water-soluble initiator, is added to the reactor followed immediately by the start of the pre-emulsion feed, which is fed to the reactor over an extended period of time, typically 1-2 hours. This is what is termed a “starve-fed” emulsion process. Base (typically ammonium hydroxide, 30 wt % in water) is added simultaneously with the pre-emulsion to keep the emulsion slightly basic. A second initiator feed is added to the emulsion at the finish of the pre-emulsion feed. A final initiator feed is added one hour later as a chaser to scavenge any unreacted monomer. The emulsion is allowed to react an additional hour before it is cooled to room temperature.
In conducting the present emulsion polymerization reaction, standard emulsion polymerization techniques are employed with the addition of a pre-emulsion prepared by separately mixing together water, surfactant and the monomers and the addition of base along with the pre-emulsion to keep the emulsion slightly basic.
Standard nonionic and anionic surfactants are employed in the reaction. Advantageously, the reaction is conducted at an elevated temperature ranging from about 60° to about 100° C., at ambient pressure and under an inert atmosphere such as nitrogen. The reaction mixture is maintained under agitation employing standard mixing techniques.
Before the resin is mixed with the emulsion polymerization reaction mixture there must be a polymeric (or steric) stabilizer present in the reaction mixture to prevent coagulation of the emulsion particles. The stabilizer can be any of the conventional nonionic surfactants such as ethoxylated alkylphenols including ethoxylated nonylphenol having at least 20 ethylene oxide units, ethoxylated octylphenol having at least 20 ethylene oxide units or, alternatively, functional monomers such as acrylic acid, methacrylic acid or polyethylene glycol monomethacrylate. The stabilizer is added to the reaction mixture prior to resin addition and usually in amounts ranging from about 1 to about 8 percent by weight of the reaction mixture and preferably from about 2 to about 4 weight percent.
Suitable low molecular weight support resins employed in the practice of the present invention include any solution or bulk polymerized polymers prepared from ethylenically unsaturated monomers such as olefins, mono vinylidene aromatics, alpha, beta-ethylenically unsaturated carboxylic acids and esters thereof, and ethylenically unsaturated dicarboxylic anhydrides. They are known materials and are prepared employing standard solution polymerization techniques. Preferably, the support resins are prepared in accordance with the teachings of U.S. Pat. No. 4,414,370, U.S. Pat. No. 4,529,787 and U.S. Pat. No. 4,456,160 all of which are incorporated herein by reference.
Other suitable commercially available resins include water dispersed or water dispersible aliphatic polyurethanes such as Spensol L52 an aliphatic polyurethane commercially available from Reichhold Chemical, Inc., and water dispersible silicone ethylene oxide copolymers such as FF400, a water dispersible silicone-ethylene oxide copolymer commercially available from Dow Corning. These and other similar resins can be used especially where the des
Bloembergen Steven
Cassar Scott E.
Fishman David H.
McLennan Ian J.
Ecosynthetix Inc.
Mullis Jeffrey
Quarles & Brady LLP
LandOfFree
Resin-fortified sugar-based vinyl emulsion copolymers and... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Resin-fortified sugar-based vinyl emulsion copolymers and..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Resin-fortified sugar-based vinyl emulsion copolymers and... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2828424