Reinforced polyamide resin composition and process for producing

Details Reinforced polyamide resin composition and process for producing Reinforced polyamide resin composition and process for producing

1993-12-28

1995-05-09

Yoon, Tae H.

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

At least one aryl ring which is part of a fused or bridged...

524449, 524606, 524791, 524879, 523216, C08K 334

Patent

active

054140420

ABSTRACT:
A reinforced polyamide resin composition which involves 100 parts by weight of a polyamide and from 0.01 to 100 parts by weight of fluoromica-based mineral with swelling characteristics.
A process for producing the reinforced polyamide resin composition involving polymerizing a monomer in a state where from 0.01 to 100 parts by weight of fluoromica-based mineral with swelling characteristics is present per the monomer in an amount of forming 100 parts by weight of a polyamide.
The reinforced polyamide resin composition is excellent in mechanical strength, toughness, heat resistance and dimensional stability.

REFERENCES:
patent: 3883469 (1975-05-01), Brassat
patent: 4555439 (1985-11-01), Ueada et al.
patent: 4623586 (1986-11-01), Umeya et al.
patent: 4739007 (1988-04-01), Okada et al.
patent: 5204078 (1993-04-01), Tateyama et al.
"Synthesis of Expandable Fluorine Mica from Talc", Tateyama et al. Clays and Clay Minerals, vol. 40, No. 2, pp. 180-185, 1992.
"Summary of Recommendations of AIPEA Nomenclature Committee", S. W. Bailey, Clay Science 5, pp. 209-220, 1979.

Affiliated with

Also associated with

Rating

Reinforced polyamide resin composition and process for producing does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Reinforced polyamide resin composition and process for producing, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Reinforced polyamide resin composition and process for producing will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-1705831