ABSTRACT:

The present invention concerns improvements in refining, more especially it concerns an improved process useful in the refining of precious metals.
In this specification, we intend “precious metal” to include one or more of gold and the platinum group metals (“PGMs”, namely Pt, Rh, Pd, Ru, Ir, Os). Silver is not to be regarded as precious metal.
After the mining of precious metal ores, or as a by-product of mining other minerals, for example, nickel, or in the recovery of precious metal values from recycled materials, it is common to produce a concentrate containing precious metal components, silver compounds and base metal compounds (which means compounds of any other metal or amphoteric). The number and quantities of individual base metal compounds may vary substantially according to the origin of the concentrate. Preferred concentrates for use in the present invention are mine concentrates containing about 60 wt % or more of precious metal, but other concentrates may be used instead. It is envisaged, therefore, that suitable feedstocks for the present invention are concentrates containing more than 50 wt %, preferably about 60 wt %, of precious metal, in admixture with base metals, including particularly arnphoteric elements. It has been found that certain elements such as copper, nickel, iron, cobalt, sulphur, silver, selenium, lead, tellurium, zinc, bismuth, arsenic, antimony and tin, are generally deleterious and disadvantageous in refining the precious metals and even some of the precious metals have such low value and create complications in further refining that it would be helpful to separate at least a proportion thereof; osmium is such a precious metal.
A number of processes involving chlorination of precious metal feedstocks have previously been disclosed. For example, GB 1,502,765 (Matthey Rustenberg Refiners) discloses a process by which a solid concentrate is treated with a halogen-containing gas to remove base metals and silver by volatilisation of the corresponding halides. A preferred subsequent step is to dissolve the precious metal-containing residue in hydrochloric acid containing an oxidising agent. Another proposed process is disclosed in CA 2,181,369 (Prior Engineering), and this comprises three steps of oxidising feedstock at a first temperature, reducing the residue at a second temperature and chlorinating in a third step. The first oxidising step is a roasting step using oxygen or an oxygen-containing gas, and removes sulphur and amphoterics such as selenium as their dioxides, and it is possible that some osmium is volatilised as its tetroxide. A proportion of the metals remaining are oxidised, and therefore a reduction step follows, using a reducing gas such as hydrogen or a hydrogen-containing gas. The final step of chlorination preferably uses chlorine, and converts the majority of the base metals present to chlorides, which are generally volatile at the temperatures employed. (800 to 1300° C.), and are removed in the gas stream. Whilst this can certainly be regarded as beneficial, we have carried out tests which indicate that a number of volatile precious metal chlorides are also formed, causing significant losses of gold, palladium and ruthenium. This chloride formation, therefore, must remove this process from serious consideration in refining such precious metal concentrates. There remains, therefore, a need for a practicable refining process which converts a precious metal concentrate to a refined product amenable to further processing and with minimal losses of the valuable precious metals.
The present invention provides a method for the refining of a solid precious metal-containing concentrate comprising the following steps:
1. a high temperature treatment of the concentrate with hydrogen chloride gas to yield a first residue;
2. an optional treatment of the first residue with chlorine gas to yield a second residue.
3. a high temperature treatment of the first or second residue with oxygen to yield a third residue, and
4. a high temperature treatment of the third residue with hydrogen to yield a final residue.
It is to be understood that the HCI gas, Cl
2
, O
2
and H
2
gas may be in admixture with an inert gas or any other gas that does not interfere with the primary reactions taking place. The gas may possibly be substituted by a precursor(s) for the gas, if appropriate for example, hydrogen and chlorine react to form HCl. It is preferred to flush each residue with an inert or other non-interfering gas between each process step, if there is any risk of forming an explosive mixture. Our experimental work has found that a flush with nitrogen for 15 minutes is sufficient for this purpose.
We have found that the steps 1,3, and 4 of the method of the invention can be carried out at the same high temperature, suitably in the range 750° C. to 1100° C., preferably 850° C. to 1050° C., especially about 950° C. The chlorination step 2, however, is preferably carried out at a lower temperature, e.g. 200 to 400° C., preferably about 300° C. Details of preferred operating temperatures are given below.
Initial tests have shown that, operating under the preferred conditions, total losses of Pt, Pd, Rh and Ir are less than 1% while achieving >98% removal of Se, >80% removal of Te and >98% removal of As. There are losses of Os of the order of 50-60% but this is not regarded as a serious penalty, and losses of Ru of from 2 to 4% but the majority of this can be recovered using known procedures which form no part of the present invention.
The feedstock may be any solid concentrate from mining the platinum group metals, or a concentrate from refining processes applied to primary (that is, from mine production) or secondary (that is, from recycled precious metals) or mixtures thereof. The method of the invention is believed to be sufficiently robust to cater for a wide variety of feedstocks. These may be comminuted or in agglomerated (e.g. briquette or pellets or similar) form. We have found that there can be a physical loss of precious metal fines in the gas stream if conventional processes such as fluidised beds or upward gas flow are used. Accordingly, it is preferred to operate each of the steps in a downflow gas mode in a reactor vessel such as a vertical tube. A gas-permeable base is preferably used in the reactor vessel. The gases removed from each step may be treated in conventional scrubbers and metal values collected by essentially conventional processing. It is preferred to avoid condensation of volatile products prior to the scrubbers, and heating of pipework and tubes may be necessary to avoid build-up of condensates and possible blockages.
In a first embodiment, the method is directed to minimising the losses of desired precious metals, whilst removing as much deleterious material as possible. In a second embodiment which includes the optional chlorination step, the method is directed to removing as much of the deleterious elements as possible, with less emphasis on precious metal losses. The embodiment chosen will depend largely on individual feedstocks and the downstream refining and metal separation technology that is available. In brief, one example of carrying out the first embodiment is as follows:
During the first step of the method, the solid feedstock is subject to a chlorinating environment in the form of hydrogen chloride gas. The temperature range should be maintained between 750° C. and 1100° C., preferably 850° C.-1050° C., especially about 950° C. This environment is conducive to removing the majority of the base metal elements by forming stable base metal chlorides that are volatilised. To a lesser degree, the amphoteric elements are also removed.
Prior to the oxidative treatment, the furnace is flushed with an inert gas, usually nitrogen. In the presence of oxygen, the problematic amphoteric elements such as selenium, tellurium and arsenic are removed as their metal oxides.
The temperature range for this operation should be within 750° C. and 1100° C., preferably 850° C. to 1050° C., especially about 950° C.
Once agai

Affiliated with

Also associated with

Rating

Refining does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Refining, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Refining will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2934010