Recording material for the ink jet printing method

Details Recording material for the ink jet printing method Recording material for the ink jet printing method

2000-11-14

2003-07-29

Hess, Bruce H. (Department: 1774)

Stock material or miscellaneous articles

Ink jet stock for printing

Physical properties of support specified

Reexamination Certificate

active

06599592

ABSTRACT:

BACKGROUND OF THE INVENTION
The invention relates to an ink jet recording material with a base paper which is new for this purpose.
In the ink jet recording method tiny ink droplets are applied onto a recording material with the aid of different techniques, which have been already described several times, and received by the recording material.
Different requirements are placed on the recording material such as high color density of the printed dots, a fast ink reception and a sufficient wiping fastness connected therewith, a dye diffusion in the transverse direction of the printed dots which does not surpass the required degree as well as minimal mottle and a high water fastness.
Ink jet recording materials are comprised of a carrier material, an ink receiving layer applied thereto, and optionally further auxiliary layers.
Ink jet printers for producing photo-like prints use ink with a high proportion of water as a solvent. When using conventional ink jet papers, a wavy appearance in the transverse direction (cockle) occurs due to the high water content which penetrates through the ink receiving layer into the paper support. This wavy appearance results in a contact of the recording material with the print head and has the consequence of a deterioration of the printed image. Moreover, the head contact can result in damage of the receiving material. It is therefore required to employ for producing photo-like ink jet prints a recording material in which the base paper has a high dimensional stability and is thus able to receive a large water quantity without exhibiting the aforementioned wavy appearance.
From JP 06-262845 A a receiving material is known whose paper carrier contains hardwood pulp and has a sizing of starch and alkyl ketene dimer. The claimed paper is said to have a good absorption capability and uniform appearance of the printed dots. However, a disadvantage of this receiving material is the insufficient dimensional stability (wavy appearance) at high water uptake.
The same problem of insufficient dimensional stability at high water uptake is also observed in a recording paper described in JP 08-258399 A which contains a calcium carbonate with spindle-shaped particles and neutral sizing agents.
The cockle problem is to be solved according to JP 11-099737 by an ink jet paper which, in addition to an ink receiving layer, has at least one further so-called carrier layer which is comprised of a water-insoluble resin such as polyethylene or polypropylene. A disadvantage is the long drying time of the printed recording paper.
SUMMARY OF THE INVENTION
It is an object of the invention to provide a recording material for the ink jet printing method which exhibits a good dimensional stability and high water uptake capability and, moreover, in addition to a high color density, exhibits excellent wiping fastness and good water fastness.
This object is solved by a base paper which is free of a beater sizing agent, contains 5 to 55% by weight of a filler, and is impregnated with an impregnation resin, wherein the resin uptake is adjusted such that the base paper at the backside has a liquid uptake of at most 20 g/m
2
, preferably 3 to 6 g/m
2
. The backside of the base paper is the side opposite the image-carrying side.
The subject matter of the invention is moreover an ink jet recording material with the aforedescribed base paper as a support and at least one ink receiving layer arranged on the front side. Between the support and the ink receiving layer, and on the ink receiving layer, further layers can be arranged.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
The filler contained in the raw paper can be titanium dioxide, zinc sulfide, calcium carbonate, kaolin, talc, clay, or mixtures of these fillers. In a preferred embodiment, a mixture of titanium dioxide and kaolin in a mixing ratio (weight) of 1:10 to 10:1 is used. Especially good results are obtained for a mixing ratio of 1:1. The filler proportion is 5 to 55% by weight, preferably 20 or 25 to 50% by weight based on the weight of the raw paper.
For producing the base paper according to the invention, softwood pulp (long fiber pulp) or hardwood pulp (short fiber pulp) can be used. Preferred is a pulp or pulp mixture with a specific volume of 1.4 to 2.0 cm
3
/g, in particular, 1.4 to 1.6 cm
3
/g (for a freeness value of 20 to 35° SR). The fiber length after beating should be preferably 0.6 to 1.2 mm. According to a preferred embodiment of the invention, a eucalyptus pulp or a mixture of eucalyptus and softwood pulp is used.
Wet strength agents such as polyamide/polyamine-epichlorohydrin resin, retention agents such as quaternary polyammonium salts, defoaming agents, penetration accelerators such as saccharides, and other additives can be added to the pulp suspension. In comparison to conventional base papers for ink jet recording materials, the raw papers according to the invention have no sizing agents which are conventionally used in beater sizing.
According to one embodiment of the invention, the recording material contains a so-called one-sided smooth raw paper. The raw paper smooth on one side is preferably produced on a Yankee machine wherein the Fourdrinier wire side of the paper web is smoothed with the aid of a heated cylinder. Because of the long contact time of the paper with the cylinder, a closed surface can be generated whose smoothness should not fall below 1000 ml/sec, measured according to Bendtson.
In further embodiments of the invention, it is also possible to employ a raw paper open on both sides, i.e., not smoothed, which can then be smoothed in a calender after impregnation on one side or both sides.
The resin is an impregnation resin that is conventionally employed in the paper industry. It can be selected from the group of diallyl phthalates, epoxide resins, urea formaldehyde resins, urea-acrylic acid ester copolyesters, melamine formaldehyde resins, melamine phenol formaldehyde resins, phenol formaldehyde resins, poly(meth)acrylates or unsaturated polyester resins. In a special embodiment of the invention, the coating mass contains a mixture of an acrylic acid ester and urea formaldehyde resin. Especially good results can be obtained with a mixing ratio (weight) of acrylic acid ester/urea formaldehyde resin of 1:10 to 10:1.
The impregnation with the resin can be performed in-line in the paper machine in a sizing box or off-line external to the paper machine in a size press or in an impregnation device. The raw paper can be impregnated from the front side or from the backside or from both sides, wherein the resin penetrates into the interior of the raw paper. The resin uptake of the paper is adjusted such that the impregnated raw paper has at the backside a liquid uptake of at most 20 g/m
2
, preferably 3 to 6 g/m
2
. The amount of resin (coating mass) can be 2 to 25 g/m
2
, preferably 5 to 8 g/m
2
.
Basically any desired ink receiving layer can be applied onto the base paper according to the invention. These are usually hydrophilic coatings which contain water-soluble or water-dispersible polymers, for example, polyvinyl alcohol, cationic polyvinyl alcohol, polyvinyl pyrrolidone, polyvinyl acetate, starch, gelatin, casein, or carboxymethyl cellulose. The ink receiving layer can contain additionally pigments and cationic substances for fixation of the ink dyes.
In a particularly preferred embodiment of the invention, the ink receiving layer comprises a polyvinyl alcohol or a mixture of polyvinyl alcohol and an acrylic acid ester homopolymer and/or copolymer. In another embodiment of the invention the ink receiving layer may contain a cationic dye fixing agent and a pigment. The application weight of the ink receiving layer is 2 to 20 g/m
2
, in particular 6 to 15 g/m
2
. The ink receiving layer can be applied with conventional application methods such as roller coating, gravure coating, or nip methods and air brush or roll doctor metering.
In a special embodiment of the invention the recording paper may comprise an additional polymer layer arranged on the receiving layer. The polymer conta

Affiliated with

Also associated with

Rating

Recording material for the ink jet printing method does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Recording material for the ink jet printing method, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Recording material for the ink jet printing method will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3068305