ABSTRACT:
BACKGROUND OF THE INVENTION
1) Field of the Invention
The present invention relates to a rare earth permanent magnet having rare earth elements R, transition metal elements T and boron B as a main composition, which provides excellent magnetic properties.
2) Description of Related Art
Among rare earth permanent magnets, demand for Nd—Fe—B system magnets has increased annually because of its excellent magnetic properties and because it is relatively inexpensive due to the abundant resources of Nd. Research and development to enhance the magnetic properties of Nd—Fe—B system magnet is being made vigorously. In recent years, a mixing method, wherein various kinds of metal powder and alloy powder of different compositions are mixed and then sintered, has become the main stream in the manufacturing of high performance Nd—Fe—B system magnets.
However, since Curie temperature of the Nd—Fe—B system magnets is low, its coercive force declines as temperature rises. Various attempts have been made to solve this problem. For example, it has been proposed that adding heavy rare earth elements such as Dy and Tb to the Nd—Fe—B system magnets is effective to enhance the coercive force (hereinafter, refer to as “conventional art A”).
Also, it has been proposed that appropriately changing the mixing ratio of R-T system alloy powder against R-T-B system alloy powder is effective in enhancing the magnetic properties in a method for manufacturing R-T-B system rare earth permanent magnet that employs a mixing method using a main phase with R
2
T
14
B-system intermetallic compound (R is one or more selected from the group of rare earth elements and Y, and T is at least one transition metal element) being a main composition and the R-rich phase being a main composing phase (hereinafter, refer to as “conventional art B”).
Also, it is proposed to add one or more of Ti, Ni, Bi, V, Nb, Ta, Cr, Mo, W, Mn, Al, Sb, Ge, Sn, Zr, Hf, Cu, Si and P (herein after referred to “Ti, etc.”) in order to enhance the magnetic properties of rare earth permanent magnet (hereinafter, refer to as “conventional art C”).
However, in the conventional art A, the addition of heavy rare earth elements such as Dy and Tb would enhance the coercive force but lower its residual magnetic flux density. Also, heavy rare earth elements are costly compared with other elements. Therefore, the key to the manufacturing cost reduction of rare earth permanent magnets is to decrease the volume of heavy rare earth element additives.
Moreover, rare earth permanent magnets manufactured in the conventional art B had a problem in that while they show a high residual magnetic flux density, the coercive force was low.
Moreover, it has been proposed in the conventional art C that Ti, etc. should be used as additives. However, no element has been specified for realizing both excellent coercive force and residual magnetic flux density.
SUMMARY OF THE INVENTION
In view of the above, the present invention provides a rare earth permanent magnet that excels in both coercive force and residual magnetic flux density.
Various studies were made by the present inventors to obtain high magnetic properties. As a result, it was discovered that Bi was effective in enhancing the magnetic properties of rare earth permanent magnets. In particular, when the Bi content is 0.01 to 0.2 wt % in the sintered magnet, it is possible to obtain a rare earth permanent magnet with excellent coercive force and residual magnetic flux density. Therefore, the present invention provides to a rare earth permanent magnet that essentially consists of 20-40 wt % of rare earth element R, 0.5-4.5 wt % of boron B, 0.03-0.5 wt % of M (at least one of Al, Cu, Sn and Ga), 0.01-0.2 wt % of Bi and the balance being at least one transition metal element T.
The rare earth permanent magnet according to the present invention may preferably contain 31-32.5 wt % of Nd+Dy, 0.5-1.5 wt % of boron B, 0.15 wt % or less (but not 0 wt %) of Cu, 0.15-0.3 wt % of Al, 2 wt % or less of Co (but not 0 wt %), 0.01-0.2 wt % of Bi, and Fe as the balance. Also, the Bi content may preferably be 0.02-0.1 wt %. Moreover, the Dy content may preferably be between 2 wt % and 15 wt %.
The rare earth permanent magnet according to the present invention produces excellent magnetic properties of 1.25 T or greater in residual magnetic flux density and coercive force of 1,650 kA/m or greater. In the present invention, it is desirable that Bi is dispersed in the grain boundary phase.
In the present invention described above, the content for M (at least one of Al, Cu, Sn and Ga) may be 0.03-0.5 wt %, and the Bi content be 0.01-0.2 wt %. However, only Bi, whose content be 0.01-0.2 wt %, is also effective without containing M.
Therefore, the present invention also provides to a rare earth permanent magnet may include 20-40 wt % of R, 0.5-4.5 wt % of boron B, 0.01-0.2 wt % of Bi and the balance being at least one transition metal element T.
The rare earth permanent magnet in accordance with the present invention presents excellent magnetic properties of 2,100 or greater (T×kA/m) in terms of the product (Br×Hcj) of residual magnetic flux density Br and coercive force Hcj. Also, the value obtained by dividing the coercive force Hcj by the weight percentage of the heavy rare earth element (Hcj/weight percentage of heavy rare earth element) is 230 or greater (kA/m×1/wt %). Therefore, according to the present invention, a rare earth permanent magnet with excellent magnetic properties can be obtained while reducing the amount of costly heavy rare earth element to be added. Here, as for heavy rare earth element, at least one element is selected from the group of Gd, Tb, Dy, Ho, Er, Yb and Lu.
Moreover, the salient point of the present invention is the effect of enhancing coercive force Hcj by adding a small amount of Bi. The value obtained by dividing the coercive force Hcj by the weight percentage of Bi (Hcj/weight percentage of Bi) is 8,000 or greater (kA/m×1/wt %).
Also, the present invention provides a rare earth permanent magnet comprising of a R
2
T
14
B magnetic phase and a non-magnetic grain boundary phase wherein Bi is dispersed, with a value obtained by dividing the coercive force Hcj by the weight percentage of Bi (Hcj/weight percentage of Bi) being 8,000 or greater (kA/m×1/wt %).
Rare earth permanent magnets of the present invention described above are suitably applicable to sintered magnets.
Other objects, features and advantages of the invention will become apparent from the following detailed description taken in conjunction with the accompanying drawings.
REFERENCES:
patent: 4765848 (1988-08-01), Mohri et al.
patent: 5545266 (1996-08-01), Hirosawa et al.
patent: 6511552 (2003-01-01), Makita et al.
patent: 4 135 403 (1993-04-01), None
patent: 19 945 943 (2001-04-01), None
patent: 0 106 948 (1984-05-01), None
patent: 59-089401 (1984-05-01), None
patent: 59-132104 (1984-07-01), None
patent: 60-032306 (1985-02-01), None
patent: 62-116756 (1987-05-01), None
patent: 62-244105 (1987-10-01), None
patent: 06-283318 (1994-10-01), None
patent: 07-050205 (1995-02-01), None
Fukuno Akira
Ishizaka Chikara
Kato Eiji
Nakane Makoto
Hogan & Hartson LLP
Sheehan John P.
TDK Corporation
LandOfFree
Rare earth permanent magnet does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Rare earth permanent magnet, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Rare earth permanent magnet will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3307107