Production of patterned coated abrasive surfaces

Details Production of patterned coated abrasive surfaces Production of patterned coated abrasive surfaces

2001-04-02

2003-01-28

Parker, Fred J. (Department: 1762)

Coating processes

Direct application of electrical, magnetic, wave, or...

Electrostatic charge, field, or force utilized

C427S469000, C427S475000, C051S295000

Reexamination Certificate

active

06511713

ABSTRACT:

BACKGROUND
This invention relates to coated abrasives and specifically to a method or making coated abrasives with a patterned surface.
It is well known that there are significant advantages to be obtained from the selective deposition of abrasive materials on a substrate. These may range from the avoidance of wasted grain by non-deposition on the parts of a substrate that do not see active abrasion during conventional use, to the creation of islands of abrasive material that ensure efficient use of the abrasive grain and room for swarf to be carried away during grinding. The present invention provides a very efficient and versatile way of producing patterned coated abrasive surfaces that can be adapted to all manner of coated abrasive applications.
In the production of a conventional coated abrasive, a backing is provided with a maker coat, the primary function of which is to bind abrasive grain deposited thereon to the backing. The grain is therefore applied before the maker coat is fully cured so that it still allows the grain to stick to its surface. A size coat is then applied over the grain adhered to the maker coat and primary function of this coat is to anchor the grain to the backing. It will be clear therefore that, if a maker coat is applied in a pattern rather than as a uniform coating over the backing material, the grain deposited thereon will only adhere to the pattern in which the maker coat has been deposited. This provides a known avenue for the production of patterned surfaces. It does however mean that non-adhered abrasive grain has to be collected and separated from the backing while the manufacturing process is continuing. This can lead to problems and is generally inefficient. In addition the selective printing of specific areas with maker coat is not simple since it means that, instead of using a simple roll-coater with a doctor knife to secure uniformity or a slit die deposition mechanism, several deposition orifices must be kept free-flowing to secure a uniform patterned coated abrasive surface.
An alternative process involves the use of a masking layer which allows deposition of maker coat and/or abrasive grain only in places corresponding to holes in the masking layer. This can be quite effective but the removal of the masking layer can lead to problems if there has been penetration behind the layer that could cause the layer to be difficult to remove, or if there has been some overlap such that removal of the layer causes some of the abrasive also to become dislodged. In addition the masking layer may not be reusable unless carefully cleaned and this represents an unnecessary inconvenience and expense.
Grain deposition is generally practised by gravity feed or by electrostatic deposition. In a gravity feed process the grain is deposited from a deposition hopper in a uniform manner, though this depends on ensuring that the grain remains free-flowing. The tendency is however to over-deposit such that, when the substrate surface passes over a roll to reverse the direction of travel, the coated surface faces downwards and excess grain not adhered by the maker coat drops off. It has been proposed to deposit grain selectively on the substrate using a series of directed shrouds so as to obtain a desired pattern. In such a process the backing is generally uniformly coated with the maker coat such that the production of a patterned surface is a function of the physical control of deposition of grain on to the maker coat. While such processes are quite efficient, the use becomes more problematical as the abrasive grain size becomes smaller since the smaller grains are more susceptible to flow problems that could lead to pattern disruption. In addition there is the possible problem of over-application and lack of definition of the pattern unless the shroud positioning and the line speed are adequately controlled.
In an electrostatic deposition process, often referred to as an UP (upward projection) process, a tray containing abrasive grain is located between two electrodes with the upper electrode being grounded and the lower adapted to carry a charge. A backing that has been given a maker coat is passed between the electrodes and above the tray of abrasive grain. To initiate grain deposition the lower electrode is charged and abrasive grain is projected upwardly in the direction of the ground electrode and becomes adhered to the maker coat on the substrate. This gives a very uniform, controllable coating and is widely practised for that reason. It is not readily adapted to producing patterns however unless through the use of patterned maker coat depositions, which suffer from the drawbacks outlined above.
The present invention provides an extremely versatile and efficient process for the production of patterned surfaces on a coated abrasive using an efficient UP deposition technique.
GENERAL DESCRIPTION OF THE INVENTION
The present invention provides a process for the production of a coated abrasive having a patterned surface which comprises depositing abrasive grain on a substrate by an electrostatic projection technique wherein the field by which the grain is projected is controlled to provide that the grain is preferentially deposited in the desired pattern.
In essence the pattern is created by the generation of a non-homogenous electrostatic deposition field corresponding to the pattern. The “pattern” can be a simple peripheral ring around an abrasive disc or of lines along the edges of an abrasive sheet. Alternatively it can be a pattern of dots, with each dot having any desired configuration and the pattern elements having any desired spacing. The definition of each element of the pattern is not necessarily crisp because electrostatic fields between electrodes are not defined by clear lines of demarcation. There is however a clearly higher level of deposition corresponding to the areas of greatest electrostatic field intensity and this is the basis of the “pattern” as the term is used herein.
In the context of the present invention the term “non-homogeneous” is intended to convey intentional imposed variations in the intensity of the electrostatic field by which abrasive grain is projected towards the backing. It does not relate to edge effects that are often observed in the areas around the edges of the electrodes, where there may be some attenuation of the strength of the field.
The variations can be brought about in a number of ways, each of which can provide significant advantages for different applications. The field can for example be essentially uniform between conventional electrodes but be locally intensified by the passage of a treated deposition substrate between the electrodes. Thus for example a backing having first and second major surfaces with a maker coat applied to the first major surface and a pattern printed on the second major surface in a conductive ink will, as it passes between the electrodes, locally intensify the field and therefore the deposition on the first major surface opposite the printed areas. If the field strength is adjusted such that, in the absence of the local intensification, it is insufficient to bring about significant deposition of the grain on the substrate, grain will be deposited in a pattern that corresponds to the pattern printed on the reverse side of the film. This pattern can be as simple as a series of dots or stripes or perhaps more complex patterns as desired. Sometimes it may be desirable to print stripes along the lateral edges of a sheet to ensure enhanced deposition in an area that is often inadequately provided with abrasive grain when using conventional UP processes. The printing is most frequently applied to the back side of the substrate, that is the side opposite to that on which the abrasive grain is to be deposited. This however is not essential and printing on the side to receive the grain can often have advantages.
This embodiment of the process is particularly effective when the backing is a plastic film or paper rather than a fabric material which may produce a less intense local vari

Affiliated with

Also associated with

Rating

Production of patterned coated abrasive surfaces does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Production of patterned coated abrasive surfaces, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Production of patterned coated abrasive surfaces will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3058154