Metal treatment – Process of modifying or maintaining internal physical... – With casting or solidifying from melt
Reexamination Certificate
2001-02-13
2003-12-16
Wyszomierski, George (Department: 1742)
Metal treatment
Process of modifying or maintaining internal physical...
With casting or solidifying from melt
C148S692000, C148S696000, C164S463000
Reexamination Certificate
active
06663729
ABSTRACT:
BACKGROUND OF THE INVENTION
This invention relates to the production of aluminum alloy foil products. Specifically, it relates to a process for manufacturing an aluminum alloy foil using a continuous strip casting process in which the material has excellent rollability in the final rolling step and good strength of final foil product.
Thin gauge foils are generally prepared by casting an ingot of an aluminum alloy such as AA8021 in a process known as DC or direct chill casting. The ingots are generally heated to a high temperature, hot rolled to a re-roll gauge thickness of between 1 and 10 mm, then cold rolled to a “foil-stock” gauge typically 0.2 to 0.4 mm thick. The strip is often subjected to an interanneal step during the cold rolling process. The “foil-stock” is then subject to further cold rolling operations, often using double rolling techniques to produce a final foil thickness of about 5 to 150 microns.
There is a cost advantage to using continuous strip casting as the starting point in manufacture of such foils since homogenization prior to hot rolling is not required, and the amount of hot reduction to form re-roll gauges is greatly reduced. Where high volume continuous casting is required, twin belt casting is the preferred method of continuous casting. However, continuous strip casting processes apply different cooling conditions during solidification from those in DC casting, and there is an absence of a high temperature homogenization step prior to hot rolling. Consequently when continuous strip casting processes are used with alloys normally prepared by DC casting and homogenization, this results in the formation of different intermetallic species in the cast product which cause surface defects, known as “fir tree effect”, in the final foil stock product. In continuous strip casting, the cooling rate of the strip during casting is generally higher (in some cases much higher) than the cooling rate in large DC ingots. Thus, such alloys processed in a continuous strip casting process also result in foil stock which has a higher supersaturation of solute elements, and therefore has undesirable hardening and softening properties, resulting in difficulties in rolling the foil stock to the final gauge thickness.
There is a particular interest in being able to produce aluminum foils from AA8021-type alloys by continuous strip casting. An AA8021-type alloy has the nominal composition of less than 0.2% by weight silicon and 1.2 to 1.7% by weight iron, with the balance aluminum and incidental impurities. This alloy is widely used, e.g. in Japan, in the production of foil, where it is normally cast by direct chill casting. When the same AA8021 alloy is cast on a continuous strip caster, the resulting strip does not have the same microstructure as that obtained by direct chill casting. For instance, belt casting creates cooling rates during solidification much higher than in DC casting and this generates a wide variety of intermetallic sizes and concentrations that negatively affect microstructure control. Therefore, the final anneal cannot produce the desired structure for a foil.
It is known to produce high strength aluminum foil by continuous strip casting an AA1200-type alloy strengthened by the addition of other strengthening alloying elements, such as Mn, Cu and Si. Such an alloy is easily castable on a continuous strip caster and the final product has excellent strength. However, because of the added strengthening solute elements, there is a high work hardening rate of the material during cold rolling. Thus, it is difficult to roll this material to final thin gauge.
A twin roll casting process for producing high strength aluminum foil is described in Furukawa Alum, Japanese Patent JPO1-034548. That process used an aluminum alloy containing, in percentages by weight, 0.8 to 2% Fe, 0.1 to 1% Si, 0.01 to 0.5% Cu, 0.01 to 0.5% Mg and 0.01 to 1% Mn. Ti and B were also included at grain refining levels. The alloy was twin roll cast to a thickness of 0.5 to 3 mm and rolled to foil. A heat treatment at 200 to 450° C. was also included.
Ward et al. U.S. Pat. No. 5,725,695 utilized an AA8111 alloy (containing 0.30 to 1.0% by weight Si and 0.40 to 1.0% by weight Fe) which was processed via twin roll casting, cold rolling with interanneal to a maximum of 441° C. and final anneal. The alloy used contained silicon in an amount equal to or higher than the amount of iron.
A further continuous strip casting technique using Al—Fe—Si type aluminum alloy is described in Katano et al. WO 99/23269. The continuous cast material was interannealed in a two step process using two different temperature ranges.
Another procedure for producing high strength foil material based on Al—Fe—Si alloy is described in Furukawa JPO6-101004. In this procedure the alloy was strip cast to a preferred thickness of 5 to 10 mm followed by interanneal, cold rolling and final anneal.
It is an object of the present invention to produce, using continuous strip casting, an aluminum foil having a low work hardening rate and hence good rollability, while providing high strength in the final foil product.
It is a further object of the present invention to produce an aluminum foil having a low work hardening rate and hence good rollability, and high strength in the final foil product by using a high productivity casting method.
SUMMARY OF THE INVENTION
In accordance with the present invention, the problem of producing a quality aluminum alloy foil using a continuous strip caster has been solved by way of a new alloy composition and a new processing route. Thus, the alloy that is used is one containing 1.2 to 1.7 wt % Fe and 0.35 to 0.8 wt % Si, with the balance aluminum and incidental impurities. The above alloy is then cast in a continuous strip caster to a strip thickness of less than about 25 mm, preferably about 5 to 25 mm, followed by cold rolling to interanneal gauge. The interannealing is carried out at a temperature of at least 400° C., followed by cold rolling to final gauge and final anneal.
The interanneal is preferably carried out at a temperature of about 400 to 520° C. for about 1 to 8 hours. The final anneal is preferably at a temperature of about 250 to 400° C. for about 1 to 12 hours and the continuous strip casting is preferably conducted on a belt caster.
In the above procedure, the continuously cast strip is optionally hot rolled to a re-roll gauge (typically 1 to 5 mm) before cold rolling to the interanneal gauge. The cold rolling reduction prior to interanneal is typically at least 40%. For best results both the heating and cooling rates in the interanneal stage are maintained within the range of about 20 to 60° C./h.
The use of the above alloy composition has substantially eliminated the “fir tree effect”. The absence of this fir tree effect means that the surface quality of the final foil is improved and the pin hole frequency in the final foil is reduced.
It has also surprisingly been found that with the above combination of alloy composition and processing route, the work hardening behaviour of the alloy is similar to that of fully homogenized direct chill cast AA8021. It is believed that this surprising effect is a result of the accelerated decomposition of the supersaturated alloying elements in the matrix alloy during the interanneal process.
Thus, the invention provides the structure and properties of foil material that are essential for making a good quality, high strength foil, namely:
(a) a uniform intermetallic phase distribution in the as-cast state (no fir tree effect);
(b) low work hardening rate and hence good rollability (UTS after a cold reduction of 90% is below 190 MPa); and
(c) high strength in the final product (UTS at 0 temper—after final anneal—is greater than 90 MPa).
In the above alloy, the Fe is the primary strengthening element and forms Fe containing intermetallic particles during casting (which are broken into smaller particles during subsequent rolling stages). These particles contribute to strengthening by particle strengthening and by stimulating grain nucleation
Anami Toshiya
Gabryel Christopher
Gatenby Kevin
Jin Iljoon
Okamoto Ichiro
Alcan International Limited
Combs Morillo Janelle
Cooper & Dunham LLP
Wyszomierski George
LandOfFree
Production of aluminum alloy foils having high strength and... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Production of aluminum alloy foils having high strength and..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Production of aluminum alloy foils having high strength and... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3152445