ABSTRACT:
The present invention relates to a process for producing-ultrafine or “nano-sized” titanium dioxide, parts of the process, and the product of the process. In particular, the present invention relates to the processing of aqueous titanium solutions to ultrafine titanium dioxide. The process includes a novel combination of operational steps to economically produce a high quality-ultrafine titanium dioxide.
BACKGROUND OF THE INVENTION
Titanium dioxide (TiO
2
) for pigment use may be present in either of two predominant forms, anatase or rutile, and is used in paints, paper, plastics, ceramics, inks, etc. The titanium dioxide for pigment use generally has an average particle size of 150 to 250 nanometer and is considered the principal white pigment of commerce. It has an exceptionally high refractive index, negligible color, and is quite inert. Titanium dioxide having a smaller average particle size, for instance in the 10 to 100 nanometer median particle size range, is used commercially in cosmetics and personal care products, plastics, surface coatings, self-cleaning surfaces, and photovoltaic applications. This titanium dioxide is referred to as ultrafine or nano-sized titanium dioxide.
There are several processes for making ultrafine titanium dioxide, some in commercial use and some in development. Some use anhydrous titanium tetrachloride as a feedstock and burn it in an oxygen-hydrogen flame or in a plasma arc. Another process uses a titanyl sulfate solution as the feedstock. In this process, titanium dioxide is precipitated from the feedstock in a controlled manner, followed sequentially by calcination and intense steam micronization to break up agglomerates formed during the calcination step.
Both types of processes, however, suffer from a lack of control over the product particle size distribution, as well as the product mineralogy. In other words, although the average particle size of the titanium dioxide may be from 10 to 100 nanometer, the particle size distribution may vary greatly. Furthermore, the titanyl sulfate process produces an anatase form whereas the anhydrous chloride oxidation produces a rutile crystallographic modification. Therefore, there is a need for a process to economically make ultrafine titanium dioxide having a narrow particle size distribution and having a specific crystallographic modification made by an easily controlled, lower cost, environmentally sound route.
SUMMARY OF THE INVENTION
The present invention provides an economical hydrometallurgical process for producing ultrafine TiO
2
from aqueous titanium chloride solutions. The solutions may be derived from any of several sources, but are practically derived from processing mineral ores and, in particular, ilmenite ore or an ilmenite mineral concentrate. The processing to produce the solutions can be, for instance, a leaching or dissolution process, followed by any of several means for solution purification. The solution could also be produced by hydration of anhydrous titanium tetrachloride. The solution may also be derived from the process described in application No. 60/141,114 and from U.S. application Ser. No. 09/500,207, the entire contents of which are incorporated herein by reference.
The aqueous titanium chloride solution is generally comprised of water, hydrochloric acid, titanium oxychlorides and titanium chlorides. The solutions may vary widely in composition with respect to the hydrochloric acid content and the titanium content.
Minor quantities of any of several chemical control agents may be introduced into the solution. The solution is further converted to a titanium oxide solid in a process involving total, controlled evaporation of the solution and the formation of a thin film of titanium dioxide. This process is conducted above the boiling point of the solution and below the temperature where there is significant crystal growth. The water and hydrochloric acid are vaporized and the hydrochloric acid may be recovered.
The titanium oxide is next calcined at an elevated temperature to induce and control crystallization. The concentration and type of chemical control agent as well as the calcination conditions determine the desired crystalline form and crystal size of the ultrafine titanium dioxide.
Following calcination, the titanium dioxide is milled or dispersed to yield a final nano-sized or ultrafine titanium dioxide having a narrow particle size distribution.
The advantages of the process according to the present invention include a superior high quality ultrafine titanium dioxide due to the narrow particle size distribution and readily controlled physical and chemical characteristics, and low cost processing.
REFERENCES:
patent: 3903239 (1975-09-01), Berkovich
patent: 3935094 (1976-01-01), Bergeron et al.
patent: 3941583 (1976-03-01), Martin et al.
patent: 3961005 (1976-06-01), Sparks
patent: 3961940 (1976-06-01), Fukushima et al.
patent: 3966455 (1976-06-01), Taylor
patent: 3967954 (1976-07-01), Chen
patent: 3996332 (1976-12-01), Elger et al.
patent: 4012338 (1977-03-01), Urwin
patent: 4065544 (1977-12-01), Hamling et al.
patent: 4082832 (1978-04-01), Watanabe et al.
patent: 4085190 (1978-04-01), Shiah
patent: 4089675 (1978-05-01), Preston et al.
patent: 4097574 (1978-06-01), Auger et al.
patent: 4107264 (1978-08-01), Nagasubramanian et al.
patent: 4120694 (1978-10-01), Elger et al.
patent: 4152252 (1979-05-01), Tolley et al.
patent: 4158041 (1979-06-01), Tolley
patent: 4168297 (1979-09-01), Nagasubramanian et al.
patent: 4172878 (1979-10-01), Tolley
patent: 4174274 (1979-11-01), Tolley et al.
patent: 4174963 (1979-11-01), Tolley
patent: 4175110 (1979-11-01), Tolley
patent: 4175952 (1979-11-01), Tolley
patent: 4178176 (1979-12-01), Tolley
patent: 4183768 (1980-01-01), Knapp et al.
patent: 4199552 (1980-04-01), Rado
patent: 4206021 (1980-06-01), Rivory
patent: 4230542 (1980-10-01), Traini et al.
patent: 4269619 (1981-05-01), Keil et al.
patent: 4269809 (1981-05-01), Tolley et al.
patent: 4288417 (1981-09-01), Rahm et al.
patent: 4288418 (1981-09-01), Davis et al.
patent: 4304758 (1981-12-01), Rieck et al.
patent: 4313913 (1982-02-01), Panek et al.
patent: 4359449 (1982-11-01), Hard et al.
patent: 4384883 (1983-05-01), Fensom
patent: 4389391 (1983-06-01), Dunn, Jr.
patent: 4390365 (1983-06-01), Hard et al.
patent: 4401467 (1983-08-01), Jordan
patent: 4468248 (1984-08-01), Megy
patent: 4842832 (1989-06-01), Inoue et al.
patent: 4923682 (1990-05-01), Roberts et al.
patent: 4944936 (1990-07-01), Lawhorne
patent: 4986742 (1991-01-01), Denecker et al.
patent: 5061460 (1991-10-01), Watanabe et al.
patent: 5068056 (1991-11-01), Robb
patent: 5068093 (1991-11-01), Mauer
patent: 5104445 (1992-04-01), Dubrovsky et al.
patent: 5106489 (1992-04-01), Schmidt et al.
patent: 5135652 (1992-08-01), Boateng
patent: 5192443 (1993-03-01), Delloye et al.
patent: 5224986 (1993-07-01), Mostert et al.
patent: 5225178 (1993-07-01), O'Donnell et al.
patent: 5378438 (1995-01-01), Leary
patent: 5397375 (1995-03-01), O'Donnell et al.
patent: 5399751 (1995-03-01), Gentry et al.
patent: 5427749 (1995-06-01), Hollitt et al.
patent: 5441712 (1995-08-01), Duyvesteyn et al.
patent: 5482691 (1996-01-01), O'Donnell et al.
patent: 5490976 (1996-02-01), Rennie et al.
patent: 5562763 (1996-10-01), Bruckner et al.
patent: 5595347 (1997-01-01), Walpole
patent: 5601630 (1997-02-01), Hoecker
patent: 5679131 (1997-10-01), Obushenko
patent: 5698177 (1997-12-01), Pratsinis et al.
patent: 5698205 (1997-12-01), Brückner et al.
patent: 5714260 (1998-02-01), Okuda et al.
patent: 5730774 (1998-03-01), Hollitt et al.
patent: 5730795 (1998-03-01), Herkimer
patent: 5770310 (1998-06-01), Noguchi et al.
patent: 5826162 (1998-10-01), Aral et al.
patent: 5833892 (1998-11-01), Gurav et al.
patent: 5840111 (1998-11-01), Wiederhoft et al.
patent: 6001326 (1999-12-01), Kim et al.
patent: 6037289 (2000-03-01), Chopin
patent: 6099634 (2000-08-01), Uenishi et al.
patent: 197 25 616 (1998-11-01), None
patent: 0 016 583 (1980-10-01), None
patent: 0 186 370 (1986-02-01), None
patent: 0 356 132 (1990-02-01), None
pa
Duyvesteyn Willem P. C.
Prochazka Jan
Sabacky Bruce James
Spitler Timothy Malcome
Altair Nanomaterials Inc.
Brinks Hofer Gilson & Lione
Griffin Steven P.
Nguyen Cam N.
Nichols G. Peter
LandOfFree
Processing aqueous titanium chloride solutions to ultrafine... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Processing aqueous titanium chloride solutions to ultrafine..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Processing aqueous titanium chloride solutions to ultrafine... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2974483