Coating processes – Spray coating utilizing flame or plasma heat – Nonuniform or patterned coating
Reexamination Certificate
2002-07-11
2003-12-23
Bareford, Katherine A. (Department: 1762)
Coating processes
Spray coating utilizing flame or plasma heat
Nonuniform or patterned coating
C427S453000, C427S256000, C427S287000, C427S421100, C029S889721
Reexamination Certificate
active
06667076
ABSTRACT:
TECHNICAL FIELD
The invention relates to a process and a device for coating a temperature-stable component with a thermal protection layer, in which the temperature-stable component has a surface which is to be coated with the thermal protection layer and at which there is at least one cooling-passage opening which is connected to a cooling passage running inside the component. The invention also describes a temperature-stable component which can be produced using the above process.
PRIOR ART
Temperature-stable components are designed for use in hot environmental conditions and are substantially characterized by the choice of materials of which they consist. In the discussions which follow, the temperature-stable components considered will be those components of a gas turbine installation which are directly or indirectly exposed to the hot gas flow, such as for example the combustion chamber walls and components which divert the hot gas flow, such as rotor blades and guide vanes within the respective gas turbine stages. Of course, in this context consideration can also be given to other temperature-stable components which are used in other technical fields in which the components are also exposed to high thermal loads.
Temperature-stable components of this type are completely or partially coated, in a manner known per se, with an additional thermal protection layer (TBC=Thermal Barrier Coating), in order to further improve their ability to withstand heat. The use of thermal protection layers has long been known and in conjunction with gas turbine components can be found, inter alia, in the following documents: U.S. Pat. No. 5,960,249, U.S. Pat. No. 5,512,382 and U.S. Pat. No. 6,077,036.
The thermal protection layer is applied, in a manner which is known per se, during a spraying operation, to the surface of the heat-resistant components. The spraying operation is carried out under ambient conditions in standard coating chambers. In this context, thermal flame spraying processes, in which coating material in powder form is heated and melted, are particularly suitable. The drops which are formed are then directed by means of a gaseous carrier jet onto the component surface which is to be coated, where the drops cool and solidify as a layer structure.
If the heat-resistant components to be coated are components which have internal cooling systems which, via cooling-passage openings, open out at the surface of the component in order to further cool their component surface, the coating operation encounters the difficulty that the cooling-passage openings which are present at the component surface which is to be coated should not be closed up. For this reason, the cooling passages which open out at the component surface have hitherto only been introduced into the component after the coating operation, but this entails additional production costs. Alternatively, the cooling-passage openings which are already present in the component surface are covered over in order to protect them from being closed up by the material which is to form the coating, but in particular if there are a large number of cooling-passage openings of this type this has not proven to be a suitable measure.
Highly modern air-cooled guide vanes and rotor blades of a gas turbine have, by way of example, more than 800 cooling-passage openings at their surface, each with a diameter of less than 1 mm. All coating techniques which have been known hitherto and which either make do with subsequent punching through the coating layer or, by suitable measures, make use of covering of the individual cooling-passage openings before the coating, have not proven practical on an industrial scale. The possibility of making the cooling-passage openings larger, in order in this way to prevent the opening from being completely closed up during the coating, have proven to have little prospect of success, since the relatively large cooling-passage openings which have been at least partially blocked as a result of the coating operation, on account of the additional removal of material around the cooling-passage opening, acquire undefined opening structures, which is of considerable detriment to the cooling effect which it is desired to produce by means of the cooling-passage openings.
SUMMARY OF THE INVENTION
The invention is based on the object of further developing a process and a device for coating a temperature-stable component, preferably a gas turbine component, such as for example a guide vane or a rotor blade, with a thermal protection layer, the temperature-stable component having a surface which is to be coated with the thermal protection layer and at which there is at least one cooling-passage opening which is connected to a cooling passage which runs inside the component, in such a manner that, despite the coating operation, the cooling-passage opening is retained with the minimum possible technical and design outlay. The intention is that the surface which is to be coated should be covered with a thermal protection layer of the same quality as that achieved in the prior art. In particular, it is important that the surface-cooling action of the cooling air which emerges from the cooling openings should not be adversely affected and should even be improved.
Furthermore, it is an object of the invention to describe an arrangement with which the process can be carried out with the minimum possible cost and design outlay. The arrangement is in particular to allow temperature-stable components for use on a large industrial scale to be coated.
The process according to the invention for coating a temperature-stable component with a thermal protection layer, in which the temperature-stable component has a surface which is to be coated with the thermal protection layer and at which there is at least one cooling-passage opening which is connected to a cooling passage running inside the component, is developed in such a manner that, during the coating, a mass flow passes through the cooling-passage opening. This mass flow prevents the cooling-passage opening from being closed up during the coating operation as a result of the material which is to be deposited on the surface being effectively blown away at least within the area of the cooling-passage opening. Furthermore, the process according to the invention provides for the deliberate use of an anisotropic coating technique as a result of a targeted coating mass flow, i.e. a coating mass flow which has a preferred propagation direction, being directed onto the surface which is to be coated. Thermal flame spraying processes which are known per se are particularly suitable for this purpose, allowing the production of protection layers consisting of MCrAlY or TBC materials. Finally, in the process according to the invention the coating is to be carried out in such a manner that the mass flow which emerges through the cooling-passage opening and the coating mass flow include an angle &agr;≠0°.
The invention makes use of the idea of supplying air through the cooling-passage system in the interior of the temperature-stable component during the coating operation, which substantially involves depositing material on the surface which is provided with the cooling-passage openings, so that the air which flows out through the cooling-passage openings prevents the coating material which is being deposited on the surface from blocking the cooling-passage openings. In this way, components, preferably gas turbine blades or vanes, which have already been produced with a fully-formed cooling system with cooling-passage opening, to be subjected to a coating process which is able to coat the entire component surface which is provided with cooling-passage openings in a single coating step. There is no need for preparatory measures aimed at keeping the holes open beforehand at the surface of the component which is to be coated, and nor is there any need for remachining steps to open the holes up again after the coating operation.
However, the inventive idea goes still further, since the method
Fried Reinhard
Neuhoff Heinz
Alstom (Switzerland) Ltd.
Bareford Katherine A.
Cermak Adam J.
LandOfFree
Processes for coating a temperature-stable component with a... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Processes for coating a temperature-stable component with a..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Processes for coating a temperature-stable component with a... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3131635