Process for the treatment of austenitic stainless steel...

Metal treatment – Process of modifying or maintaining internal physical... – Carburizing or nitriding using externally supplied carbon or...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C148S225000

Reexamination Certificate

active

06238490

ABSTRACT:

This invention relates to a process for the treatment of austenitic stainless steel articles and is more particularly concerned with a process for the treatment of austenitic stainless steel articles so as to produce a hardened surface layer thereon.
BACKGROUND OF THE INVENTION
Austenitic stainless steels have good corrosion resistance in many environmental conditions, but they have low hardness and poor friction and wear properties. Attempts have thus been made to develop surface treatment methods for improving these properties. However, surface modification of austenitic stainless steels usually has to overcome two major problems. One problem is the formation of an oxide scale (Cr
2
O
3
) on the steel surface due to the strong affinity of chromium, which is the principal alloying element in austenitic stainless steels, with oxygen in air. This oxide scale frequently results in poor adhesion between a coating and the steel surface. Therefore, such surface modification techniques as PVD coatings, electroplating and electroless plating have limitations for stainless steels, as compared with coating and plating of most other ferrous alloys.
Another problem associated with surface treatment of austenitic stainless steels lies in the fact that in many cases the improvement in surface hardness and wear resistance of the steels by surface treatments is accompanied by a loss in the corrosion resistance. For example, plasma nitriding, which is carried out in a glow discharge in a nitrogen gas-containing mixture at a pressure of 100 to 1000 Pa (1 to 10 mbar), is one of the most widely used methods to treat stainless steel surfaces, resulting in a nitrogen diffusion layer having high hardness and excellent wear resistance. However, nitriding hardening is induced by the precipitation of chromium nitrides in the nitrided layer. This leads to a depletion of chromium in the austenite matrix and thus a significant reduction in corrosion resistance [see E. Rolinski, “Effect of Plasma Nitriding Temperature on Surface Properties of Austenitic Stainless Steel”,
Surface Engineering,
Vol. 3, No. 1. 1987, pages 35-40].
Therefore, attempts have been made to develop surface treatment methods for improving the wear resistance of austenitic stainless steels without losing their corrosion resistance. A low temperature plasma nitriding technique has been developed, in which a conventional dc or pulsed plasma nitriding apparatus is used. The process is carried out at temperatures below 500° C. for a time up to 60 hours in a nitrogen-containing gas of pressure 100 to 1000 Pa(1 to 10 mbar) [see P. A. Deamley, A. Namvar, G. G. A Hibberd and T. Bell, “Some Observations on Plasma Nitriding Austenitic Stainless Steel”,
Proceedings of the First International Conference on Plasma Surface Engineering,
Garmisch-Partenkirchen, Germany, 1989, pages 219-226.] Low temperature nitriding can produce a nitrided layer having high hardness and good corrosion resistance. However, the hardened layer is very thin and brittle, and it is difficult to achieve uniform layer thickness.
A low pressure plasma carbon diffusion treatment has recently been proposed for stainless steels, in which a triode ion plating apparatus is used and the treatment is carried out at temperatures between 320° C. and 350° C. and in a gas mixture of argon, hydrogen and methane [see P. Stevenson, A. Leyland. M. Parkin and A. Matthews, “Effect of Process Parameters on the Plasma Carbon Diffusion Treatment of Stainless Steels at Low Pressure”,
Surface and Coatings Technology,
Vol. 63, 1994, pages 135-143.] A working pressure of 1 to 2 Pa (0.01 to 0.02 mbar) is used for the treatment, which requires the use of a diffusion pump throughout the treatment lasting up to 30 hours. An additional sputter cleaning stage of several hours is required to effect carbon mass transfer and diffusion. A typical process comprises 4 hours sputter cleaning in argon or argon and hydrogen mixture, followed by 20 hours treatment at 320-350° C., producing a carburised layer of 11 &mgr;m thick with a maximum hardness about 7000 MN/mm
2
(700 HV
0.01
). No corrosion test results are reported for this treatment The low pressure plasma carbon diffusion treatment uses an expensive and complicated triode ion plating system, and requires operation of the diffusion pump throughout the process and an additional sputter cleaning step. In addition, the growth rate and hardening response of the layer are low. Similar comments apply also to the procedures described in GB-A-2261227.
K. T. Rie et al (Haerterie-Technische Mitteilungen, vol 42, No. 6, Nov. 1, 1987, pages 338-343) disclose plasma nitriding and plasma nitrocarburising procedures conducted so as to produce a compound layer on sintered mild steel, which has a body-centred cubic structure. In contrast to this, the present invention is concerned with austenitic stainless steels which have a face-centred cubic structure.
Th. Lampe et al (Haerterie-Technische Mitteilungen vol 46, No. 5, September 1991, pages 308-316) disclose plasma nitriding and plasma nitrocarburising procedures conducted so as to form a compound layer on iron-based material such as sintered mild steel, ledeburitic cast iron and pearlitic cast iron which, like the mild steel of K. T. Rie et al (supra), has a body-centred cubic structure.
G. V. Shcherbedinskii et al (Metal Science and Heat Treatment, 34 (1992) May/June, Nos. 5/6, pages 375-378) also disclose a procedure for the plasma nitrocarburising of high speed steels using dicyanogen formed in situ by decomposition of ferrocyanides.
SUMMARY OF THE INVENTION
It is an object of the present invention to provide an improved method of treatment of austenitic stainless steel articles which can enable the above-mentioned disadvantages to be obviated or mitigated. In particular, it is an object of the present invention to provide a treatment process which is relatively cost-effective and which is capable of forming, at a relatively low temperature, a corrosion-resistant hardened surface layer with high ductility and uniform thickness on austenitic stainless steel articles, so as to provide such articles with enhanced wear resistance without adversely affecting the corrosion resistance to an undue extent.
According to the present- invention, there-is-provided a process for the treatment of an austenitic stainless steel article, comprising the step of plasma heat-treating the article at a temperature in the range of 300 to 600° C. for 0.1 to 100 hours and at a pressure in the range of 100 to 1500 Pa in a carbon-containing treatment atmosphere so as to introduce carbon interstitially into the austenite phase in a surface layer on the article.
The resultant hardened layer comprises expanded austenite supersaturated with carbon.
The heat-treatment temperature is preferably in the range of 350 to 540° C., and is typically about 450 to 500° C.
The heat treatment is typically carried out at a pressure of about 500 Pa (about 5 mbar). The time for treatment depends upon the temperature, the carbon-activity of the atmosphere, the pressure and the required depth for the hardened surface layer (which may be in the range of 5 to 50 &mgr;m), and varies from 0.1 to 100 hours. For reasons of economy and efficiency, a treatment time of 3 to 40 hours is preferred.
The treatment atmosphere may be a gas mixture comprising at least one carbon-containing gas such as methane, carbon dioxide, carbon monoxide or other C—H organic gases or vapours with at least one relatively inert gas such as hydrogen, argon or rare gas such as helium.
It is also within the scope of the present invention for nitrogen to be introduced into the surface layer, provided that carbon is dominant in interstitial solid solution. Where nitrogen is also to be in into the surface layer, this may be provided by nitrogen gas or ammonia in the gas mixture.
A gas mixture of hydrogen with methane or hydrogen and argon with methane, with the composition of methane in the range of 0.5 to 20% by volume is preferred for carbon diffusion, and the abov

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Process for the treatment of austenitic stainless steel... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Process for the treatment of austenitic stainless steel..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for the treatment of austenitic stainless steel... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2446720

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.