Plastic and nonmetallic article shaping or treating: processes – Outside of mold sintering or vitrifying of shaped inorganic... – Shaping or treating of multilayered – impregnated – or...
Reexamination Certificate
1994-02-18
2002-02-05
Fiorilla, Christopher A. (Department: 1731)
Plastic and nonmetallic article shaping or treating: processes
Outside of mold sintering or vitrifying of shaped inorganic...
Shaping or treating of multilayered, impregnated, or...
C264S638000, C264S656000, C264S669000, C264S674000, C264S108000, C264S171100, C419S002000, C419S004000, C505S430000
Reexamination Certificate
active
06344167
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates generally to superconductor containing filaments and processes for preparing them. More particularly, the present invention relates to superconductor containing filaments prepared from multicomponent filaments and processes for preparation of the same.
BACKGROUND OF THE INVENTION
As used herein, the term “green” refers to material that has not been through a heat treatment during which organic polymeric materials are combusted.
The terms “filament” or “filaments” refer to fibers of long or indefinite length.
The term “multicomponent filament” refers to filaments having two or more longitudinally continuous distinct domains of constituents.
The terms “ceramic” or “ceramics” refer to inorganic, nonmetallic solids that are subjected to high temperature, generally greater than 600° C., during manufacture or use or both.
The terms “superconductor” or “superconductors” refer to materials that will conduct electricity with no loss of energy due to resistance below a certain critical transition temperature (Tc), below a certain critical current (Jc) and in a magnetic field below a critical strength (Hc). These materials show the Meissner effect (the repulsion of magnetic fields independent of field polarity) below the critical transition temperature (Tc) and critical magnetic field strength (Hc). The critical field strength (Hc) is a function of the temperature. Field strength values are higher at lower temperatures. “High temperature superconductors” are those which have a superconducting transition temperature (Tc) above 77K (boiling point of nitrogen under atmospheric pressure).
The term “viscose” refers to a viscous solution containing dissolved cellulose xanthate such as is used for spinning into rayon.
The term “rayon” refers to a semisynthetic fibrous material spun from viscose and composed of regenerated cellulose.
The terms “precursor” or “precursors” refer to starting or intermediate materials in the fabrication of the superconducting materials that have not yet been processed into a crystalline or semi-crystalline solid capable of superconduction. Metal oxide superconductor precursors are stoichiometric mixtures of nonsuperconducting oxides, nitrates, acetates, carbonates, or other chemical derivatives of potentially superconducting materials that are to be fired or sintered into the superconducting alloy. During firing or sintering, the undesired elements are driven off leaving a superconducting residue.
The discovery of high temperature superconductors opened the pathway for several applications (e.g., supermagnets, generators, electrical energy storage). There are, however, many issues that need to be resolved prior to commercial use of the high temperature superconductors. For example, it is believed that, unlike malleable metals, high temperature superconducting materials cannot be processed by first melting and then forming them to the desired shape, for example, wires. One important field of investigation is, therefore, how to produce superconducting wires having sufficient current density and which are sufficiently insensitive to magnetic fields.
Early work along these lines involved mixing a slurry of a superconducting material into a fiber forming material, and spinning the mixture to form fibers. Fibers made by this process generally lack good fiber properties since high loading of superconducting material into the fiber forming material deteriorates spinning performance. As a result, insufficient superconductor loading resulted in poor superconducting performance, e.g., insufficient consolidation of the superconducting particles. R. B. Cass, “Fabrication of Continuous Ceramic Fiber by the Viscous Suspension Spinning Process”,
Ceramic Bulletin, Vol.
70, No. 3, 1991 describes the loading of viscose with superconducting material which is then spun.
Oxide ceramic superconducting fibers are described in Japanese Kokai Tokkyo Koho Nos. 01,122,511; 01,122,512; and 01,122,521. The fibers may be made by dispersing the superconductor or its source material in an aqueous solution of a water soluble polymer like polyvinyl alcohol; wet spinning the aqueous solution into a solution which precipitates the polymer; and heating the fibers.
Superconducting fibers based on oxide superconductors and products resulting therefrom may be prepared by extruding the superconductor in a binder. Brazilian Patent Application No. 87 03,412 discloses ceramic oxide powder in a polymer binder. The polymer is removed by heating at 100° C. and the superconductor is sintered. Japanese Kokai Tokkyo Koho No. 01,176,606 describes a process for making oxide superconducting fiber precursors by dispersing or dissolving an oxide superconductor source material in a solution containing a polymer. The polymer is then spun to form a precursor fiber which is heated. The polymer may be polyvinyl alcohol.
Ceramic superconducting fibers have been spun using nitrate and acetate superconducting precursors in polyacrylic acid gels. Catania, Hovnanian, Cot, “Superconducting YBa
2
Cu
3
O
7−x
Fibers From Aqueous Acetate/PAA and Nitrate/PAA Gels”,
Mat. Res. Bull
., Vol. 25, 1990, pp. 1477-1485, describe a lengthwise orientation of the fiber particles. The resulting fibers are described as having poor mechanical properties.
Goto, Sugishita and Kojima, “A New Fabrication Process of Y
1
Ba
2
Cu
4
O
8
Superconducting Filament by Solution Spinning Method Under Ambient Pressure”,
Physica
, C 171, 1990, pp. 441-443 describe the preparation of ceramic superconducting fibers by dry spinning superconducting precursors (yttrium, barium and copper acetates) in a polyvinyl alcohol carrier under one atmosphere oxygen pressure. The resulting fiber was considerably porous.
Goto, “Nonaqueous Suspension Spinning of High-T
c
Ba—Y—Cu—O Superconductor”,
Japanese Journal of Applied Physics
, Vol. 27, No. 4, April, 1988, pp. L680-L682 discusses the nonaqueous suspension spinning of a superconducting ceramic oxide filament by suspending a fine powder of the oxide precursors in polyvinyl alcohol dimethyl sulfoxide solution containing a dispersant. The suspension is extruded into a precipitating medium of methyl alcohol and coiled on a winding drum. The wound filament is dried and subjected to heat treatment to generate the superconductor.
European Patent Application Publication No. 0 248 432 discloses a process for making a ceramic green body (which may be a fiber) including contacting a superconductor precursor material slurry with a solidifying liquid. The slurry contains a ceramic powder raw material, a binder and a solvent. The binder may be nitrocellulose or cellulose acetate.
It is known to make ceramic fibers from ceramic precursor sheath/core fibers. U.S. Pat. No. 4,863,799 to Mininni et al. describes a preceramic fiber made by melt or solution spinning a sheath/core fiber in which the preceramic material forms the core. Organosilicone preceramic polymers are spun as a core and certain film forming polymers are used for spinning a sheath layer. Cellulose esters of carboxylic acids, such as cellulose acetate, cellulose propionate, cellulose acetate propionate, and the like, may be used as the sheath.
U.S. Pat. No. 4,559,191 to Arons describes another process for preparing a green ceramic fiber using a sheath/core spinning technique. A green ceramic powder is formed into a dispersion or slurry and placed in the core. Suitable sheath forming polymers include cellulosic esters, among others. When the fiber is wet spun, it is extruded into a coagulation bath. The coagulation bath is any nonsolvent for the sheath forming polymer including water, methanol, propanol, ethylene glycol and the like.
It is also known to make bicomponent cellulosic fibers. Viscose rayon bicomponent fibers are described in U.S. Pat. No.2,428,046 to Sisson et al.
There remains a need for a green filament which has superconducting particles at a density and aligned properly to give a usefully high current density and yet still remains manageable, e.g., non-friable.
Also, precursors to superconducting m
Hoyt Matthew B.
Mitchell David F.
Morgan Carol W.
Roberts Clyde Gordon
Tuominen Olli P.
BASF Corporation
Fiorilla Christopher A.
LandOfFree
Process for the production of superconductor containing... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for the production of superconductor containing..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for the production of superconductor containing... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2959287