ABSTRACT:
The invention relates to the production of a fiber-reinforced composite material in which a multiplicity of continuous filaments are wetted by a melt of a thermoplastic polymer which during processing has a melt viscosity of >100 Ns/m
2
and at most 2500 Pa·s.
The process of European Patent 56703 (ICI) produces a fiber-reinforced, thermoformable composite material comprising a thermoplastic polymer and at least 30% by volume of parallel aligned reinforcing filaments by a pultrusion process. The process is said to make it possible to use conventional thermoplastic materials of high molecular weight for the impregnation of fiber strands. However, the process ceases to be suitable for polymers which exhibit a high viscosity (above 100 Ns/m
2
) at the processing temperature, because fiber strands can no longer be wetted by such melts in the pultrusion process (see loc cit. p. 3, line 10). For this reason, polymers having very low starting molecular weights are used, so that their use in recycled form does not seem very promising.
Other processes describe impregnation in open systems which are not sealed air-tight, at elevated temperatures causing extensive thermal-oxidative damage to the polymer or enabling only very low production rates. This produces very cost-intensive materials.
Accordingly, the object is to indicate a process which enables thermoformable semi-finished articles to be produced from thermoplastics of medium to fairly high viscosity. Examples of such thermoplastics are poly-propylene, polyamides, polyoxymethylene, polyethylene, polyurethane, polyphenylene sulfide, polyesters, polycarbonate, polyaryl ether ketones and mixtures thereof having the appropriate molecular weight. The process must ensure good wetting of the reinforcing fibers, such as glass, carbon, aramid, steel and ceramic fibers and/or other sufficiently temperature resistant polymer fibers. High viscosity of the melt is a characteristic feature of products having high molecular weight. High molecular weight improves recycling behavior because repeated melting results in a melt which, despite its oxidative and thermal degradation, is still in the high-molecular-weight region.
The present invention achieves this object.
There is accordingly provided a process for the production of a fiber-reinforced composite material in which, in order to form a band, a multiplicity of continuous filaments having single-filament diameters of 7 to 30 micrometers are arranged in parallel and tensioned, the filament band is wetted with a thermoplastic polymer melt in a melt pultrusion process, the filament band being pulled over at least two heated spreader surfaces and the continuous-filament volume content of the solidifying filament band being set at 5 to 70% by volume. In this process, the viscosity of the melt, measured at low shearing rates, is 105 to 2500 Ns/m
2
(=Pa·s), the tension upon entering the first spreader surface is 5 N to 50 N per 4000 single filaments and the speed of the filament band is at least 3 m/min. The viscosity of the melt is preferably in the range from 130-2000 Pa·s, in particular 130-500 Pa·s. The single-filament diameter of the continuous filaments is preferably in the range from 7 to 24 &mgr;m. The continuous-filament volume content is preferably 15 to 50% by volume.
It has been found that, as the viscosity of the melt increases, the filament pretension required has to be increased too. At a viscosity of 105 Pa·s, it has to be at least 5 N. It increases too with the filament surface area of the filament strand. The tension on the impregnated filament band at take-off from the last spreader surface is higher than the tension upon entering the first spreader surface and is preferably at least 50 N per 4000 single filaments.
Example 29 of European Patent 56703 already discloses that the tension at which the impregnated fiber band is hauled from a melt of 20 Ns/m
2
(and hence from the spreader surface) should be about 3.8 kg (for a strand or roving of 6000 filaments). According to the invention, this take-off tension, i.e. the tension upon entering the first spreader surface, is substantially higher. Take-off tensions ranging from 20 to 80% of the tear strength of the unwetted filament band are preferred.
An advantage of the process according to the invention is that it allows very high impregnation speeds. Impregnation speeds of 3-40 m/min, preferably in the range 10-30 m/min, in particular 10-20 m/min, are preferred for reasons of economy.
Yet the process according to the invention does ensure excellent wetting of the fiber material. X-ray diffraction shows that the proportion of free fiber, i.e. of unwetted fiber surface, is below 25% in the process according to the invention. Determination of the density of the semi-finished article and of the flexural modulus also indicates a high degree of wetting.
In contrast, the impregnation speeds of 0.2-0.6 m/min used in the examples of EP 056703 are substantially lower, although the viscosity of the impregnating melt is much lower, for example 10 Pa·s, which should facilitate wetting of the fiber material.
It is surprising that such a good wetting of the fiber material, which was not believed to be possible, can be achieved at all using melts of high viscosity. It is particularly surprising that this effect is achieved at impregnation speeds which are substantially higher than those of EP 056703 for material of low viscosity.
The principle underlying the invention is still unclear. Perhaps, as a result of the increased tension, the drag flow accompanying the filaments leads to the formation, in the vicinity of the curvatures of the spreader surfaces, of hydrodynamic wedges which generate a forced flow through the filament bundle. This is because it is favorable for the geometry of the spreader surfaces to be such that the nips defined by the spreader surfaces and the incoming band to be filled with melt and for the fiber bundles not to be brought into direct contact with the feed opening for the melt. The melt can be fed in at any desired point of the impregnating device of preferably undulatory design, provided the fibers do not come into contact with this point. The drag flow and superimposed pressure flow produced in the impregnating device result in general in a pressure of at least 1.5 bar between the last spreader surface and the outlet opening of the impregnating device, which constantly ensures complete filling of the impregnating device.
The process according to the invention is surprising in that it could not be expected that such high tensions on the fibers and the absence of contact between the fibers and the feed opening for the melt would permit the use of such highly viscous polymers and hence the achievement of such a high impregnation quality. What is particularly surprising is that the impregnation speeds achieved by this method are very much higher.
The fiber volume content of the semi-finished article can be controlled by adjusting the feed rate of the polymer melt, relative to the filament speed. Furthermore, superfluous amounts of polymer melt can be scraped off by means of perforated plates.
The undirectionally parallel aligned multifilament reinforcing fibers which are required for the process according to the invention are unwound from bobbins as rovings with a controlled take-off force. The control can be effected mechanically, mechano-physically, electrically or electronically. This directly applied take-off pretension is usually in the range from 10 N to about 25 N, depending on the type of roving used and the thickness of the fiber.
It has been found that the take-off tension, once established, should advantageously be kept constant.
A device which, inter alia, is suitable for keeping the take-off tension constant mechanically forms the subject of German Utility Model 9 107 510.6 (Bolenz & Schäfer Maschinenfabrik GmbH).
If required, the pretension can be further increased by inserting one or more further pairs of tension rods between bobbin and impregnating device. This ensures the time- and also roving-d
Heckel Horst
Heydweiller Joachim
Skaletz Detlef
Wagner Bruno
Aftergut Jeff H.
Lawrence William F.
Ryan Matthew K.
LandOfFree
Process for the production of fiber-reinforced semi-finished... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for the production of fiber-reinforced semi-finished..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for the production of fiber-reinforced semi-finished... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3144712