Process for the preparation of aluminum fluoride

Details Process for the preparation of aluminum fluoride Process for the preparation of aluminum fluoride

1998-05-20

2001-02-13

Nguyen, Ngoc-Yen (Department: 1754)

Chemistry of inorganic compounds

Halogen or compound thereof

Binary fluorine containing compound

C423S495000, C502S231000

Reexamination Certificate

active

06187280

ABSTRACT:

The present invention relates to a process for preparing aluminum fluoride and the so obtained aluminum fluoride.
In particular the invention relates to an improved process for preparing aluminum fluoride starting from the corresponding oxide.
The aluminum fluoride (AlF
3
) is an inorganic solid well known in the art of the preparation of heterogeneous catalysts. It is used both as such and as support for metal salts and shows catalytic activity due to its strong acidity according to Lewis and/or its thermal and chemical inertia. It is widely used, for instance, in the fluorination of chlorinated organic compounds to obtain the corresponding fluorinated compounds; in this case it is used also as a support of chromium, cobalt, nickel salts, etc. See for instance U.S. Pat No. 4,967,023 and U.S. Pat. No. 5,008,475.
The preparation, in industrial scale, of aluminum fluoride is carried out by fluorination of the aluminum oxide (alumina) with anhydrous hydrofluoric acid (HF). Other methods are also known which however have substantially a laboratory application, such as the pyrolysis of hexafluoroaluminates; the treatment of alumina with chlorofluorinated organic compounds; the F/X exchange on an aluminum halide wherein X is equal to Cl, Br, et.
In the case of alumina fluorination the amount of fluorine content depends on the reaction conditions and can be also much lower than the stoichiometric.
The alumina fluorination with anhydrous HF to obtain AlF
3
is well known in the art and is described for instance in FR 1,383,927, wherein the so obtained AlF
3
is then used as such to catalyse the HF sum on acetylene.
As it is well known to the skilled in the catalyst preparation, it is desirable that a solid which must be used as heterogeneous catalyst, both as such, and as a support for a catalytically active phase, has a surface area (SA) and a pore volume (Vp) as high as possible. Typical examples of solid used to this purpose are the various kinds of alumina having surface areas of 200-300 m
2
/g and pore volumes around 0.5 cc/g.
However the alumina fluorination to obtain AlF
3
drastically reduces said parameter values: the obtained AlF
3
shows indeed low SA and low Vp. To try to increase these values it is well known to limit the fluorination well below the stoichiometric.
This process of course cannot be applied to the fluorination catalysts, since the HF used as reactant would lead to completion the fluorination of the alumina, with consequent loss of surface area and of catalytic activity.
In order to overcome this drawback, it has been suggested, see GB 1,000,485, to regenerate the alumina when it overfluorinated by steam treatment at high temperature. Such process is of course not very practical in industrial scale, especially for the great aggressiveness of the gaseous mixture of HF and water at high temperature which is thus produced. A further drawback is in that these kinds of catalyst require frequent regenerations and therefore the interruption of the production processes where they are used.
SUMMARY OF THE INVENTION
It has been now surprisingly and unexpectedly found by the Applicant that it is possible to obtain AlF
3
with high surface area and high pore volume, by fluorination of alumina with anhydrous HF by using the process described hereinafter.
It is therefore an object of the present invention a process for preparing aluminum fluoride having an high surface area and high pore volume comprising the fluorination with gaseous HF of alumina having surface area of at least 150 m
2
/g and pore volume not lower than 0.3 cc/g, said alumina comprising from about 0.5 up to about 15% by weight of silicon oxide, preferably from 1 to 10% by weight, more preferably from 1.5 to 6% by weight.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
As aluminum fluoride, according to the present invention, it is meant the alumina fluorination product, having a fluorine content not lower than 90%, preferably not lower than 95%, of the stoichiometric.
The AlF
3
obtained with the process of the invention maintains its characteristics of high surface area and of high pore volume also during its use in fluorination and therefore it does not require frequent regeneration processes.
The AlF
3
obtainable with the process of the invention has been found to maintain a fraction of the surface area of the starting alumina which is also the double of that obtainable starting from alumina not containing silica. Likewise the maintained fraction of the pore volume results higher when alumina containing silica according to the present invention is used.
The AlF
3
obtainable with the process of the invention has generally a surface area not lower than 25 m
2
/g, preferably not lower than 30 m
2
/g and a pore volume not lower than 0.20 cc/g, preferably 0.25 cc/g.
The fluorination conditions of alumina containing silica are not particularly critical. One generally operates at a temperature comprised between about 250° C. and about 450° C., preferably higher than 300°-400° C. Indeed if one operates at temperatures lower than those indicated, the fluorination is too slow.
The total pressure has no relevant effects and one generally operates at atmospheric pressure or slightly higher, generally of some atmospheres.
It is advantageous that the partial pressure of HF is low, especially at the beginning of the fluorination, to moderate the heat development which could locally increase the temperature over the above limits: indeed two highly exothermic phenomena contemporaneously occur: the reaction between HF and alumina with formation of AlF
3
and water and the hydration of the unreacted HF from the latter.
To moderate these exothermic effects it is sufficient to use HF diluted with a gas inert in the fluorination conditions, for instance, air or nitrogen; the partial pressure of HF is generally comprised between 0.1 and 0.50.
A better control of the temperature is possible also by carrying out the reaction in fluidized bed and this is the preferred way to carry out the fluorination. In this case the aluminas to be fluorinated have a granulometry compatible with the use of fluidized beds.
In general the alumina which is used according to the present invention contains less than 0.1% by weight (each) of undesirable contaminants in the final product AlF
3
such as: iron, sulphates, sodium.
If aluminas are in hydrated form, it is preferable to subject the aluminas to a calcination phase in air or nitrogen, at a temperature comprised between 300° C. and 400° C., before the fluorination step. This limits the development of water during the reaction, which is undesirable especially because it favours the equipment corrosion.
The aluminas containing silica are prepared with known methods in the art, for instance by spray-drying of suitable precursors.
The aluminas containing silica which are preferably used according to the present invention are for instance commercial products of Condea Chemie (Germany).
Aluminas, aluminas containing silica and aluminum fluorides are characterized by techniques well known to the skilled in the art of the solid characterization: the surface area (SA) is measured by nitrogen adsorption according to the BET method; the pore volume is measured by mercury injection at high pressure; the crystalline phases by X ray diffraction; the constituent analyses are carried out by wet way according to known methods, or by X ray fluorescence by comparison with standards prepared on the same matrix by calibrated additions.
AlF
3
obtained according to the process of the present invention generally is mainly formed by gamma phase as described in FR 1,383,927.
Some examples are reported for illustrative purposes, the variations which can be introduced without deviating from the scope of the invention are easily accessible to the skilled in the art.


REFERENCES:
patent: 3473887 (1969-10-01), Chu et al.
patent: 3836635 (1974-09-01), Reh et al.
patent: 3855401 (1974-12-01), Aiso et al.
patent: 4275046 (1981-06-01), McVicker et al.
patent: 4745236 (1988-05-01), Azerad et al.
patent: 4967023 (1990-10-01), Ca

Affiliated with

Also associated with

Rating

Process for the preparation of aluminum fluoride does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Process for the preparation of aluminum fluoride, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for the preparation of aluminum fluoride will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2566985