Chemistry of hydrocarbon compounds – Adding hydrogen to unsaturated bond of hydrocarbon – i.e.,... – Hydrocarbon is contaminant in desired hydrocarbon
Reexamination Certificate
2000-10-06
2004-06-08
Griffin, Walter D. (Department: 1764)
Chemistry of hydrocarbon compounds
Adding hydrogen to unsaturated bond of hydrocarbon, i.e.,...
Hydrocarbon is contaminant in desired hydrocarbon
C585S258000, C585S260000, C585S261000, C585S262000, C585S276000
Reexamination Certificate
active
06747181
ABSTRACT:
The invention relates to a process for the hydrogenation of phenyl acetylene in a styrene-containing medium with the aid of a catalyst and in the presence of hydrogen gas.
Styrene is often polymerized to polystyrene. In the styrene-containing medium which is used for this purpose, the phenyl acetylene causes undesirable side reactions during the polymerization, such as cross-linking of the polymer chains. It is therefore of importance to keep the phenyl acetylene content of the styrene-containing medium as low as possible.
The above-mentioned process for the hydrogenation of phenyl acetylene is known from JP-A-55,35368.
Said patent publication describes a process for the hydrogenation of phenyl acetylene in a mixture of styrene, phenyl acetylene and o-xylene with the aid of a palladium or nickel catalyst. In the specific Example hydrogenation is effected with the aid of a palladium catalyst on an alumina carrier.
A drawback of the use of a palladium catalyst is that a palladium catalyst, when used for the hydrogenation of phenyl acetylene in a styrene-containing medium with minor amounts of impurities, rapidly loses its activity and thus has a short service life. This is a major drawback because it entails high catalyst regeneration costs. Further, regeneration of the catalyst means loss of production or the need to have a second reactor which is put on stream while the catalyst is being regenerated in the first reactor.
The aim of the invention is to provide a catalyst which does not present said drawback or only to a lesser extent.
The invention is characterized in that the catalyst is a supported nickel catalyst with a nickel content of 10-25 wt. %. Surprisingly it has appeared now that in a same styrene-containing medium a nickel catalyst is much less sensitive to impurities and thus has a much longer service life. This is all the more surprising in that a person skilled in the art, relying on his knowledge of catalysts, would not be likely to opt for a nickel catalyst instead of a palladium catalyst, since a nickel,catalyst normally has a lower activity and selectivity than a palladium catalyst in the conversion of acetylenes to alkenes (see for instance J. A. Moulijn, P. W. N. M. van Leeuwen and R. A. van Santen, Catalysis, Elsevier, 1993, pp. 180-181).
Further advantages of application of a nickel catalyst are that the price of a nickel catalyst is lower than that of a palladium catalyst and that nickel catalysts are commercially available with a larger catalytically active surface area.
The nickel catalyst applied according to the invention is a supported nickel catalyst. Examples of suitable carrier materials are: silica, &agr;-, &thgr;- and &ggr;-alumina, zeolites, carbon and oxidic carriers, such as for instance magnesium oxide, titanium oxide and zirconium oxide.
Mixtures of different carrier materials can also be used. By preference, &thgr;- and &ggr;-alumina, silica or carbon are used as carrier material. Particular preference is given to &thgr;- or &ggr;-alumina as carrier material, because this is an inert carrier material with a large total surface area and a good poor volume distribution.
The nickel catalyst is synthesized for instance in the following way. The nickel is applied onto the carrier material by impregnating it with a solution of nickel salts. Water is commonly used as solvent. Then the impregnated carrier material is dried and subsequently calcinated at elevated temperature. The nickel oxide thus obtained is then activated on the carrier material through a treatment with hydrogen at elevated temperature. A high degree of dispersion of the nickel on the carrier results in a catalyst with a large catalytically active surface area. The higher the catalytically active surface area in the catalyst, the better the phenyl acetylene is hydrogenated.
For economical and technical reasons the nickel content of the nickel catalyst is kept as low as possible. A nickel catalyst with a higher nickel content is more expensive and when the nickel content becomes higher, the dispersion of the nickel in the catalyst is worse.
The nickel content of the catalyst is normally 10-25 wt. %. Supported nickel catalysts are commercially available with for instance 10, 15 or 20 wt. % of nickel. The nickel content of the nickel catalyst preferably is 11 to 25 wt. %.
Most preferably the nickel content of the catalyst is more than 11 and less or equal to 20 wt. %.
Besides the nickel the catalyst can also contain minor amounts of other compounds which enhance the activity and selectivity of the catalyst. Examples of such compounds are: chromium, gold, rhodium and ruthenium. The catalyst can also be modified with sulphur-containing compounds.
When its activity in the hydrogenation of phenyl acetylene has declined strongly, the nickel catalyst can be regenerated. Regeneration is effected for instance by treating the contaminated catalyst with steam and air at a high temperature, for instance 300 to 350° C., followed by reduction with hydrogen at the same temperature. If the catalyst is lightly contaminated it can also be regenerated by merely treating it with hydrogen at an elevated temperature of 100-300° C.
When naphtha, gas condensates and LPG are cracked, cracked petrol is formed. This cracked petrol mainly contains aliphatic and aromatic compounds with 6-9 carbon atoms, including 1-50 wt. % of styrene. Fractionation of this cracked petrol yields a C8 fraction which contains 30-70 wt. % of styrene. When this C8 fraction is extracted with a solvent and then distilled, a styrene-rich fraction is obtained which may contain more than 95 wt. % of styrene. The cracked petrol, the C8 fraction as well as the styrene-rich fraction can be used as styrene-containing medium.
A styrene-containing medium can also be obtained by means of chemical synthesis. Alkylation of benzene with ethene gives ethyl benzene, which through dehydrogenation can be converted into a styrene-containing medium which besides styrene can also contain ethyl benzene and phenyl acetylene.
The invention is not restricted, however, to the hydrogenation of phenyl acetylene in the above-mentioned styrene-containing media. Styrene-containing media which have been obtained in another way can also be employed.
The styrene-containing media can comprise up to 99.99 wt. % of styrene.
The styrene-containing medium preferably comprises more than 30 wt. % of styrene. By particular preference, the styrene-containing medium is a C8 hydrocarbon fraction which comprises more than 30 wt. % of styrene.
In the hydrogenation of phenyl acetylene in the styrene-containing medium it is preferred for all phenyl acetylene in the styrene-containing medium to be converted to styrene or ethyl benzene, with a limited amount of phenyl acetylene or styrene being hydrogenated to ethyl benzene.
The phenyl acetylene content of a styrene-containing medium is normally between 0.01 and 5 wt. % relative to the styrene present in the styrene-containing medium. During the hydrogenation process according to the invention this content is reduced. Said content is preferably reduced to less than 100 ppm, by particular preference to less than 10 ppm in the styrene-containing medium.
The process for the hydrogenation of phenyl acetylene in a styrene-containing medium is carried out in a reactor. The catalyst on a support is present in the reactor. The reactor is fed with the styrene-containing medium and hydrogen gas. The hydrogen gas can optionally have been diluted with another, inert gas such as for instance nitrogen gas. The styrene-containing medium and the hydrogen gas can be mixed before being fed to the reactor.
The reactor can be operated as a two-phase or as a three-phase reactor.
If the reactor is operated as a two-phase reactor, then the hydrogen gas that is required for the At hydrogenation of the phenyl acetylene is fully dissolved in the styrene-containing medium that is supplied to the reactor.
If the reactor is operated as a three-phase reactor the styrene-containing medium and the hydrogen gas are fed in at the bottom of the reactor and the pro
Bosman Hubertus J. M.
Grootendorst Edwin J.
Postma Leonardus H.
Smeets Theodorus M.
DSM N.V.
Griffin Walter D.
Pillsbury & Winthrop LLP
LandOfFree
Process for the hydrogenation of phenyl acetylene in a... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for the hydrogenation of phenyl acetylene in a..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for the hydrogenation of phenyl acetylene in a... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3357137