Hazardous or toxic waste destruction or containment – Containment – Solidification – vitrification – or cementation
Reexamination Certificate
1998-10-07
2003-01-21
Silverman, Stanley S. (Department: 1754)
Hazardous or toxic waste destruction or containment
Containment
Solidification, vitrification, or cementation
C588S253000, C588S253000, C423S24000R, C423S24000R
Reexamination Certificate
active
06509511
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to process for the decomposition of fluorine-containing compounds, in particular perfluoroalkanes, a catalyst for use in such a process for preparing the catalyst.
BACKGROUND OF THE INVENTION
Fluorine-containing compounds represent a group of compounds which can display a high level of stability, making them difficult to convert or decompose. As a result, these compounds can be difficult to remove from effluent and waste gas streams before such streams are released into the atmosphere. A particularly troublesome group of compounds to decompose or convert are the perfluoroalkanes.
Perfluoroalkanes are a specific group of halogen-containing compounds that consist of carbon and fluorine atoms. Perfluoroalkanes are saturated, that is they do not possess double or triple carbon-carbon bonds. Perfluoroalkanes differ from chlorofluorocarbons (CFC's), hydrochlorofluorocarbons (HCF's) and hydrofluorocarbons (HFC's) in that perfluoroalkanes contain neither hydrogen nor chlorine. Examples of operations which emit perfluoroalkanes to the environment include, but are not limited to, electrolytic aluminum smelting, manufacture of fluoroplastics, dry chemical etching, chamber cleaning process and semiconductor manufacturing process. Examples of perfluoroalkanes include carbon tetrafluoride (CF
4
) hexafluoroethane (C
2
F
6
, octafluoropropane (C
3
F
8
), octafluorocyclobutane (C
4
H
8
) and decafluorobutane (C
4
H
10
). Perfluoroalkanes are some of the most stable compounds known (Kiplinger et al.
Chem. Rev
., p.373 (1994). As a result, these compounds are efficient as so-called “green house” gases, with global warming potentials estimated to be many times that of CO
2
(Langen et al., 1996). The stability of perfluoroalkanes makes these compounds difficult to decompose or convert to useful products, such as for example by conversion of perfluoroalkanes to perfluoroalkenes.
A number of catalysts and catalytic processes have been reported for the decomposition of halogen-containing organic compounds. A review of the literature reveals that the majority of these catalysts and catalytic process focus on the decomposition of chlorine-containing compounds, or organic compounds containing both chlorine and fluorine. Only limited results have been reported on the decomposition of organic compounds containing only fluorine. Bond and Sadeghi, in an article entitled “Catalyzed Destruction of Chlorinated Hydrocarbons,”
J. Appl. Chem. Biotechnol
., p.241 (1975), report the decomposition of chlorinated hydrocarbons over a platinum catalyst supported on high surface area alumina. In particular, experiments are reported on the conversion of a range of chlorinated hydrocarbons over a platinum/gamma-alumina catalyst on which a hydrocarbon fuel is being oxidized. The ability of this catalyst to decompose perfluoroalkanes was not reported.
Kamaker and Green, in an article entitled “An investigation of carbon difluoridedichloride (CF
2
Cl
2
) decomposition on TiO
2
Catalyst,”
J. Catal
, p394 (1995), report the use of a TiO
2
catalyst to decompose CFCl
2
at reaction temperatures between 200 and 400° C. in streams of humid air. Again, there is no discussion of the decomposition or conversion of perfluoroalkanes.
Bickel et al., in an article entitled “Catalytic Destruction of Chlorofluorocarbons and Toxic Chlorinated Hydrocarbons,”
Appl. Catal., B:Env
. p.141 (1994), report the use of a platinum supported on phosphate-doped zirconium oxide for the decomposition of CFC113 (Cl
2
FCCC1F
2
) in air streams. The catalyst was able to achieve in excess of 95% decomposition of CFC113 at reaction of 500° C. for approximately 300 hours of continuous operation. After this time, the catalyst rapidly deactivated. The ability of this catalyst to decompose perfluoroalkanes was not reported.
Fan and Yates, in an article entitled “Infrared Study of the Oxidation of Hexafluoropropene in TiO
2
,” J. Phys. Chem
, p. 10621 (1994), report the decomposition of a perfluoroalkene over TiO
2
. Perfluoroalkanes differ from perfluoroalkanes in that they contain a carbon-carbon double bond, that is are unsaturated. Although the catalyst was able to readily decompose hexafluoropropylene (C
3
F
6
), the loss of titanium, as TiF
4
, was evident. The formation of TiF
4
would undoubtedly lead to deactivation of the catalyst. The ability of this catalyst to decompose perfluoroalkanes was not reported.
Faris et a., in an article entitled “Deactivation of a Pt/Al
2
O
3
Catalyst During the Oxidation of Hexafluoropropylene,”
Catal. Today
, p. 501 (1992), report the decomposition of hexafluoropropylene over a catalyst comprising platinum supported on a high surface area alumina. Although the catalyst could readily decompose hexaflurorpropylene at reaction temperatures between 300 and 400° C., over the course of the experiment (less than 100 hours), the aluminum oxide was converted to aluminum triflouride, which resulted in a severe loss of catalytic activity. The ability of this catalyst to convert perfluoroalkanes was not reported. However, transformation of the aluminum oxide to aluminum triflouride suggests that aluminum oxides will not be stable in fluorine-containing environments.
Campbell and Rossin, in a paper entitled “Catalytic Oxidation of Perfluorocyclobutene over a Pt/TiO
2
Catalyst,” presented at the 14th N. Am. Catal. Soc. Meeting (1995), report the use of a platinum/TiO
2
catalyst to decompose perfluorocyclobutene (C
4
F
6
) at reaction temperatures between 320 and 410° C. The authors note that even at a reaction temperature of 550° C., no conversion of perfluorocyclobutane (c-C
4
F8), a perfluoroalkane, could be achieved using the Pt/TiO
2
catalyst. Results presented in this study demonstrate that perfluoroalkane are significantly more difficult to decompose or convert than the corresponding perfluoroalkane.
Nagata et al, in a paper entitled “Catalytic Oxidative Decomposition of Chlorofluorocarbons (CFC'ss) in the Presence of Hydrocarbons,”
Appl. Catal. B:Env
., p. 23 (1994), report the decomposition of 1,1,2-trichloro-1,2,2-trifluoroethane (CFC113), 1,2-dichloro-1,1,2,2-tetrafluoroethane (CFC114) and chloropentafluoroethane (CFC115) in the presence of hydrocarbons using catalyst prepared by impregnating a range of support materials, in particular gamma-alumina, silica-alumina, zeolites, mordenite, ferrierite, with vanadium, molybdenum, tungsten and platinum. Silica was also employed as a catalyst. Tungsten (VI) oxide and vanadium (V) oxide catalyst exhibited the highest activity. The decomposition of the CFC's became more difficult as the number of carbon atoms in the CFC molecule decreased. The ability of the catalyst to decompose or convert perfluoroalkanes was not reported. However, results suggest that the parent molecule becomes more difficult to destroy upon replacement of chlorine with fluorine. No information regarding the stability of the catalyst was reported.
Burdeniuc and Crabtree, in an article entitled “Mineralization of Chlorofluorocarbons and Aromatization of Saturated Fluorocarbons by a Convenient Thermal Process,”
Science
, p. 340 (1996), report the transformation of cyclic perfluoroalkanes to perfluoroarenes by means of contact with sodium oxalate to yield sodium fluoride as a reaction product. Both reactions, however, are slow and non-catalytic, since sodium oxalate is stoichiometrically consumed by being converted into sodium fluoride during the course of the reaction. This process would not be able to decompose or convert perfluoroalkanes present in streams of air, since the oxygen and/or moisture in the air would readily convert the sodium oxalate to sodium oxide.
Accordingly, it can be seen that there exists a need for a process for the conversion of perfluoroalkanes present in effluent gaseous streams, in particular streams containing perfluoroalkanesin a mixture with air. Pending U.S. patent application Ser. No. 08/662129 concerns a process for the decomposition of perfluoroalkanes in which the perfluoroalkanes are con
Guild Associates, Inc.
Nave Eileen E.
Silverman Stanley S.
LandOfFree
Process for the conversion of perfluoroalkanes, a catalyst... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for the conversion of perfluoroalkanes, a catalyst..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for the conversion of perfluoroalkanes, a catalyst... will most certainly appreciate the feedback.