ABSTRACT:
BACKGROUND OF THE INVENTION
Industrial reactions between reactant gases and liquids such as those involving the hydrogenation of unsaturated organic compounds and those having functional groups capable of condensation with hydrogen are often performed by using finely divided powdered slurry catalysts in stirred-tank reactors. These slurry phase reaction systems are inherently problematic in chemical process safety, operability and productivity. The finely divided, powdered catalysts are often pyrophoric and require extensive operator handling during reactor charging and filtration. By the nature of their heat cycles for start-up and shut-down, slurry systems promote co-product formation which can shorten catalyst life and lower yield to the desired product.
An option to the use of finely divided powder catalysts in stirred reactors has been the use of pelleted catalysts in fixed bed reactors. While this reactor technology does eliminate much of the handling and waste problems, a number of engineering challenges have not permitted the application of fixed bed reactor technology to the reaction of gases with liquid organic compounds. Controlling the overall temperature rise and temperature gradients in the reaction process has been one problem. A second problem is that in fixed bed packed reactors there is a significant pressure drop due to the high flow rates required for hydrogenation. A third problem is that liquid-gas distribution is problematic thus often leading to poor conversion and localized concentration gradients.
Monolith catalytic reactors are an alternative to fixed bed reactors and have a number of advantages over conventional fixed bed reactors. These reactors have low pressure drop which allow them to be operated at higher gas and liquid velocities. These higher velocities of gas and liquids promote high mass transfer and mixing and the parallel channel design of a monolith inhibits the coalescence of the gas in the liquid phase.
The use of monolith catalytic reactors has also led to problems in catalytic metal regeneration. Liquid phase hydrogenation of organic compounds can be quite different from gas phase hydrogenation in the types of byproducts, e.g., tars, formed. Penetration of the catalytic surfaces by liquid reactants and solvents may cause these byproducts to become embedded or deposited within the catalytic metal and support. Slurry phase hydrogenation reactions often use solvents to remove deposits followed by reduction of the catalyst to an activated state. However, such treatment may not be not suited for the regeneration of monolith catalytic reactors.
The following patents and articles are illustrative of the prior art as they relate to hydrogenation of aromatic compounds in monolith catalytic reactor.
U.S. Pat. No. 6,005,143 relates to an improvement in a process for hydrogenating a nitroaromatic composition, namely dinitrotoluene, by contacting the dinitrotoluene with hydrogen in a monolith catalytic reactor under liquid phase conditions. Broadly the improvement resides in the continuous, essentially solventless, adiabatic hydrogenation of dinitrotoluene to toluenediamine in a monolith catalytic reactor operating in plug flow.
WO 99/19292 discloses a continuous process for producing aromatic diamines by the fixed bed catalytic hydrogenation of aromatic dinitro and polynitro compounds with hydrogen in the presence of hydrogenated product. Nickel carried on a support, Raney nickel, and palladium on carbon are suggested as catalysts. Regeneration of the catalyst is effected by terminating the feed aromatic dinitro or polynitro compounds while continuing flow of hydrogenation product and hydrogen through the reactor.
U.S. Pat. No. 6,043,394 discloses the fixed bed, gas phase hydrogenation of nitroaromatic amines. Catalytic metals suited for the hydrogenation include palladium carried on a support. Deactivated beds are regenerated with N
2
/O
2
mixtures at temperatures of from 200 and 400° C., preferably between 250 and 350° C. Preferably, regeneration is begun at N
2
contents of between 90 and 99% and O2 contents of from 1-9% with the O
2
content being raised in stages to pure air. At the end of regeneration, tenacious carbon residues may optionally be burned off with pure oxygen. Inert carrier gases other than nitrogen, such as for example argon, helium or steam, may also be added to oxygen or air.
BRIEF SUMMARY OF THE INVENTION
The invention relates to an improvement in a process for regenerating monolith catalytic reactors employed in liquid phase hydrogenation reactions, particularly those kinds of reactions involving nitroaromatic compounds. Over time, the catalytic metals in the monolith catalytic reactor become deactivated, because of the deposition of carbonaceous and deactivating byproducts, and the catalytic metals must be regenerated in order to extend the catalyst service life and reduce costs. The regeneration process involves two steps. The first step involves oxidation of the carbonaceous and deactivating byproducts at moderate temperatures and the second step involves reduction of the active catalytic metal species to its activated state.
Significant advantages can be achieved by the practice of this invention and these include:
an ability to extend the service life of a monolith catalytic reactor used in liquid phase hydrogenation reactions;
an ability to minimize downtime of the monolith catalytic reactor caused by catalytic metal deactivation because of simple and efficient regeneration procedures; and,
an ability to substantially activate the catalytic metal employed in the monolith catalytic reactor to original activity levels.
DETAILED DESCRIPTION OF THE INVENTION
In the hydrogenation of liquid organic compounds such as unsaturated organic compounds and those having functional groups capable of condensation with hydrogen, particularly nitroaromatic compounds, catalyst activity degrades over time. This decay of activity can be attributed to a number of factors, which include the deposition of non-volatile carbonaceous products, such as, tars and deactivating byproducts, such as cresols, on the catalytic metal surface. In the hydrogenation of dinitrotoluene, for example, tar-like byproducts can be formed by several reactions, including: (a) linking of two or more product toluenediamine molecules, and (b) reactions between a toluenediamine product molecule and dinitrotoluene, or an intermediate product, amino-nitrotoluene.
Essentially two steps are involved in the regeneration process. The first step requires oxidation of contaminant species, e.g., carbonaceous and deactivating byproducts at moderate temperature and the second step requires reduction of active catalytic metal, such as, nickel and palladium.
In the first step, oxidation of the byproducts contaminating the catalytic metals is effected under gas phase conditions by passing an oxidizing gas at an elevated temperature through the monolith catalytic reactor for a time sufficient to effect substantial removal of the carbonaceous products, tars and deactivating byproducts. The oxidizing gas typically is a blend of oxygen in combination with an inert gas. Often, a blend of an oxidizing gas comprised of 1 to 50%, preferably 2 to 15%, oxygen by volume, with a balance of an inert gas is passed into the monolith catalytic reactor. Representative inert gas species include nitrogen, helium, or argon.
Under oxidation conditions, the effluent containing unreacted oxidizing agent, water, contaminants, and CO
2
evolved during oxidation of the catalyst are removed. To achieve oxidizing conditions temperatures of from 250-450° C. are used. Higher temperatures may reduce the cycle time required for complete oxidation, but such temperatures also may lead to sintering of the active metal species thereby destroying the catalyst activity.
Flow rates of the oxidizing gas depend on the total open cross-sectional area of the catalyst bed. This is defined as the open cross-sectional area of each monolith cell times the total number of cells available to flow. Flow rates are set to achiev
Cartolano Anthony Rocco
Mazzafro William Joseph
Welp Keith Allen
Wilhelm Frederick Carl
Air Products and Chemicals Inc.
Barts Samuel
Bongiorno Mary E.
LandOfFree
Process for regenerating a monolith hydrogenation catalytic... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for regenerating a monolith hydrogenation catalytic..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for regenerating a monolith hydrogenation catalytic... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3134381