ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to deposition processes and materials. More particularly, this invention relates to a process for reclaiming and recycling donor materials used to deposit aluminide coatings by vapor phase deposition.
BACKGROUND OF THE INVENTION
The operating environment within a gas turbine engine is both thermally and chemically hostile. While significant advances in high temperature alloys have been achieved through the formulation of iron, nickel and cobalt-base superalloys, improvements in the environmental properties of such alloys are often achieved at the expense of mechanical properties, and vice versa. Accordingly, components formed from superalloys whose chemistries are formulated to have optimum mechanical properties at high temperatures are often susceptible to environmental attack, especially if used in certain sections of a gas turbine engine, such as the turbine, combustor and augmentor. A common solution is to provide such components with a protective environmental coating that inhibits oxidation and hot corrosion.
Coating materials that have found wide use for this purpose include diffusion aluminide coatings, which are generally single-layer oxidation-resistant layers formed by diffusion processes, such as pack cementation or vapor phase deposition. Diffusion aluminiding processes generally entail reacting the surface of a component with an aluminum-containing gas composition to form two distinct zones, the outermost of which is an additive layer containing an environmentally-resistant intermetallic represented by MA1, where M is iron, nickel or cobalt, depending on the superalloy substrate material. Beneath the additive layer is a diffusion zone comprising various intermetallic and metastable phases that form during the coating reaction as a result of diffusional gradients and changes in elemental solubility in the local region of the substrate. During high temperature exposure in air, the MAl intermetallic forms a protective aluminum oxide (alumina) scale or layer that inhibits oxidation of the diffusion coating and the underlying substrate.
Vapor phase deposition processes used to form diffusion aluminide coatings (known as vapor phase aluminiding, or VPA) generally involve the use of an aluminum-rich source (donor) material composed of aluminum or an aluminum alloy that is mixed or bonded with a metal having a higher melting temperature. Primary examples for the higher melting constituent include chromium, cobalt and iron. The donor material is typically in particulate form, with particle sizes typically on the order of about five to twenty millimeters in diameter. The donor particles and a suitable halide salt activator, such as NH
4
F, NaF, KF, NH
4
Cl or AlF
3
, are then heated to a temperature that will vaporize the activator, which reacts with the donor material, thereby forming a volatile aluminum halide that reacts at the surface of the component to form the diffusion aluminide coating. The chromium, cobalt or iron constituent of the donor does not deposit on the component, but instead merely serves as an inert carrier or binder for the aluminum.
At the end of the coating process, an aluminum-depleted layer is present on the surfaces of the donor particles. Over multiple coating operations, this layer becomes an encapsulating shell composed predominantly of the high-temperature constituent of the donor, and inhibits further removal of aluminum from the donor particles. In the past, used donor material has been processed through a sieve sizing operation to remove the particle shells and undersized particles, permitting reuse of the donor material. However, shell removal is incomplete, with the result that the donor material does not perform as well as when new. As an example, the time required to deposit an aluminide coating of desired thickness is often significantly longer than would otherwise be expected. Accordingly, though a potential cost advantage exists, there are significant process limits to the use of aluminum alloy donor material reclaimed from vapor phase aluminiding processes.
From the above, it can be appreciated that it would be desirable if a process were available to improve the quality of aluminum alloy donor material reclaimed from vapor phase aluminiding processes, so that the consistency and uniformity of diffusion aluminide coating produced by the reclaimed donor material might also be improved.
BRIEF SUMMARY OF THE INVENTION
The present invention provides a process for reclaiming aluminum alloy donor from a vapor phase deposition process used to form a diffusion aluminide coating on a component, such as the high-temperature superalloy components of gas turbine engines. The process of this invention generally entails recycling a particulate aluminum alloy donor material, the particles of which have an aluminum alloy core encased in an aluminum-depleted shell as a result of the donor material having been used to deposit a diffusion aluminide coating on an article by vapor phase deposition. The process generally entails tumbling the donor material in a manner that removes the aluminum-depleted shell, followed by sieving the donor material to remove shell fragments and particles that are smaller than what is required for the vapor phase process.
According to the invention, the combination of tumbling and sieving the particulate donor material more fully removes the aluminum-depleted shell surrounding the donor particles, such that the particles are more nearly equivalent to the original condition of the particles. In a preferred embodiment, the donor material is tumbled with an abrasive media in order to scour the surfaces of the particles. The tumbling operation, its duration, the amount of abrasive media used, and the timing of when the abrasive media is added have together been shown to produce a recycled donor material that is functionally equivalent to its original condition. As a result, recycled donor material can now be reliably used to produce diffusion aluminide coatings of controlled and predictable thickness.
Other objects and advantages of this invention will be better appreciated from the following detailed description.
REFERENCES:
patent: 3486927 (1969-12-01), Gauge
patent: 3598638 (1971-08-01), Levine
patent: 3951642 (1976-04-01), Chang et al.
patent: 3961910 (1976-06-01), Baladjanian et al.
patent: 3993454 (1976-11-01), Giggins, Jr. et al.
patent: 5704823 (1998-01-01), Wittebrood
patent: 5817371 (1998-10-01), Gupta et al.
patent: 5897966 (1999-04-01), Grossklaus, Jr. et al.
patent: 6020075 (2000-02-01), Gupta et al.
patent: 6146696 (2000-11-01), Das et al.
patent: 6168874 (2001-01-01), Gupta et al.
patent: 6174448 (2001-01-01), Das et al.
Betscher Keith H.
Das Nripendra N.
Heidorn Raymond W.
King Jackie L.
Mantkowski Thomas E.
General Electric Company
Gressel Gerry S.
Hess Andrew C.
Pianalto Bernard
LandOfFree
Process for recycling vapor phase aluminiding donor alloy does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for recycling vapor phase aluminiding donor alloy, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for recycling vapor phase aluminiding donor alloy will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2578231