ABSTRACT:

The present invention relates to a process for purifying pentafluoroethane HFC-125 from chloropentafluoroethane CFC 115.
CFC 115 is an impurity of HFC-125 which forms in the processes for the production of pentafluoroethane. Besides, it is an impurity very difficult to be separated from HFC-125 by distillation.
It is possible to directly obtain by synthesis, according to the processes of the prior art, HFC 125 having high purity but with yield damage and therefore decreasing the profitability of these processes.
HFC 125 is industrially produced by direct fluorination of perchloroethylene or of a halogenated compound of general formula C
2
HX
5
, wherein X is any combination of halogens of which at least one different from fluorine, or by dismutation of HCFC 124 (tetrafluorochloroethane C
2
HF
4
Cl) to HFC 125 and HCFC-123.
The former route is more direct than the latter, but it has a lower selectivity. When the reaction conditions are forced towards the production of HFC 125, significant amounts of CFC 115 are formed, or, when the reaction is carried out so as to favour the selectivity, the amounts of pentafluoroethane obtained from the reaction are insufficient to make the process industrially profitable. Besides in the fluorination process it is necessary to use HCFC 124 having an high purity, free from CFC 114 which in the fluorination reaction would lead to the formation of CFC 115, as reported in WO 95/16,654. Therefore the purification of HCFC 124 in the fluorination process is an additional cost of said process.
Also in the process for obtaining pentafluoroethane by dismutation of HCFC 124, obtained by fluorinating the above mentioned halogenated compounds followed by purification to remove CFC 114, it is not possible to obtain high conversions, since CFC 115 forms together with other by-products, although in lower amounts with respect to the direct fluorination process. See U.S. Pat. No. 5,841,006 in the name of the Applicant.
In conclusion the obtainment of very pure HFC 125 by direct synthesis according to the prior art processes has the drawback to decrease the process yields and/or increase the production costs due to the purification step of the intermediate compounds.
Alternatively, it is possible to use processes allowing the purification of HFC 125 from CFC 115. In EP 687,660 a process is described for purifying HFC 125 by reacting with hydrogen a mixture formed by at least 85% by volume of pentafluoroethane and of chloropentafluoroethane in % by volume not higher than 15%, in the presence of a group VIII metal catalyst, at temperatures in the range 170° C.-400° C. As known the reactions wherein gaseous hydrogen is used require a specific plant, since this gas is flammable and explosive and besides it is incompatible with various metal materials. In EP 508,631 a reduction process of CFC 115 by its absorption in an organic solution of a complex metal hydride is described. The use of these reactants implies high costs. Besides, hydrides in the presence of traces of moisture develop hydrogen, wherefore also in this case it is valid what said for the process of EP 687,660. In U.S. Pat. No. 5,346,595 a multistage distillation process is described to remove CFC 115 from HFC 125. The process requires a separate distillation section and at least two distinct distillation steps, working at different pressures, with optional recycle in the second step. The maximum obtainable purity of HFC 125 is 99.8% with 0.2% of residual content of CFC 115, therefore still very high.
The need was therefore felt of a simplified process for purifying HFC 125 from CFC 115, economically cheaper than those of the prior art, in particular such as not to require a specific plant HF or hydrogen resistant.
The present invention is related to the solution of this technical problem.
It is an object of the present invention a gaseous process for substantially reducing the amount of chloropentafluoroethane (CFC 115) impurity present in pentafluoroethane (HFC 125) characterized in that pentafluoroethane is allowed to flow on a fluorination catalyst in solid phase, optionally supported, at temperatures in the range 200° C.-400° C., preferably 280° C.-350° C., obtaining the reaction of chloropentafluoroethane with pentafluoroethane with formation of hexafluoroethane (FC 116) and tetrafluorochloroethane (HCFC 124).
Both FC 116 and HCFC 124 are easily separable from HFC 125; besides HCFC 124 can be recycled in the synthesis process of HFC 125. FC 116 is an industrially useful product. The process according to the present invention does not require the addition of reactants converting CFC 115 into an easily separable product from HFC 125.
The trivalent chromium salt catalyst can for example be that used for obtaining HFC 125 with the processes of the prior art, for example by fluorinating with HF perchloroethylene (WO 95/16654) or by dismutation of HCFC 124 (U.S. Pat. No. 5,345,014).
It is possible to directly carry out the process according to the present invention in the same reactor used for obtaining HCFC 124, with evident economic advantage.
The contact time with the catalyst, measured as the ratio between the catalyst volume and that of the gas flow at the working temperature and pressure, is in the range 1-30 seconds, preferably 5-20 seconds.
The working pressure is not critical, but preferably one operates in the range 1-10 bar.
The reaction is carried out by flowing the CFC 115/HFC 125 mixture, optionally diluted with an inert gas, through the catalyst in a fixed or fluidized bed. When the catalyst is in a fluidized bed the catalyst particles have sizes suitable for this process.
The fluorination catalyst is preferably a chromium salt.
Preferably the catalyst support is aluminum fluoride AlF
3
obtainable by alumina fluorination and having a fluorine content not lower than 90%, preferably not lower than 95%, with respect to the stoichiometric.
Generally the used aluminum fluoride is mainly constituted by gamma phase, as described in FR 1,383,927, and has a surface area generally in the range 25-35 m
2
/g. When the catalyst is used in a fluided bed, the support must have the granulometry suitable for this kind of reactor, as it is well known to the skilled in the prior art.
The chromium amount in the supported catalyst is in the range 5-15% by weight, preferably 10-15%, determined as metal amount with respect to the weight of the finished supported catalyst.
The supported catalyst is preferably prepared by impregnation of the support with an aqueous solution of a soluble chromium salt.
The impregnation of the support can be carried out by any method known in the prior art, for example by the method known as “dry impregnation”.
According to this method, the impregnation is carried out by pouring on the support, in sequence, aliquots of an impregnating solution, such that the total volume is not higher than the volume of the aluminum fluoride pores. The solution for the impregnation is prepared by dissolving in water the required amounts of the corresponding salts, preferably chlorides, of the trivalent chromium. The solution is poured in aliquots on the support, drying at 110° C. for some hours after each addition, to evaporate water from the support pores.
The unsupported catalyst is prepared by methods known in the art, for example by precipitation of a soluble trivalent chromium salt as described in U.S. Pat. No. 5,345,014.
Before use the catalyst is activated by calcining for 4-8 hours in a current of inert gas, at the temperature of about 400° C., and then treating it at 360° C. with anhydrous HF for a time comprised between 12 and 24 hours. The operation can be carried out in the reactor used for the purification of HFC 125.
With the process of the invention the purification of HFC 125 can be carried out until the desired extent of the residual amount of CFC 115 combining the reaction temperature, the contact time and optionally the recycle of the product, since in the reaction according to the invention the HFC 125 degradation is negligible, practically the HFC 125 recovery obtained with t

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Process for purifying pentafluoroethane from... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Process for purifying pentafluoroethane from..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for purifying pentafluoroethane from... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3014749

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.