ABSTRACT:
BACKGROUND OF THE INVENTION AND RELATED ART STATEMENT
The present invention relates to a process for producing a cordierite-base ceramic honeycomb structure by extruding.
Cordierite-based ceramic honeycomb structures are in use as a carrier for exhaust gas purification catalyst for use in automobiles and various industries, a filter, a heat exchanger, etc.
In recent years, with the progress of technologies, it has been strongly desired to improve the ceramic honeycomb carrier for catalyst used particularly in the exhaust gas system of automobiles. Desired improvements were in (1) volume (smaller volume), so as to obtain better catalytic performance and better light-off performance, in (2) pressure loss (lower pressure loss) for improved fuel consumption and higher engine output, in (3) strength for reduced cost of canning into casing, and in (4) thermal shock resistance and strength for mounting close to engine and resultant higher catalytic activity.
In this connection, investigations have been made to develop a honeycomb structure with thinner ribs and higher cell density, for improved catalytic performance and to produce a honeycomb structure with thinner ribs, having a required cell density, for lower pressure loss. Use of thinner ribs in porous cordierite-based ceramic honeycomb structures produced problems of (a) reduced strength and (b) a substantially increased thermal expansion coefficient caused by the use of die of smaller slit width in extruding and consequent necessity to use finer materials (particularly, magnesia source material).
It was difficult to allow a cordierite-based ceramic honeycomb structure to have a high density.
Particularly, when raw materials were used for cordierite formation having a low thermal expansion coefficient of 2.0×10
−6
/°C. or less in a temperature range from room temperature to 800° C. was used, it was necessary to minimize amounts of impurities (which become a flux) such as calcia, alkali or sodium. Consequently, the cordierite-based ceramic honeycomb structure obtained had a very small amount of a vitreous phase and it was porous.
In order to alleviate this problem, attempts were tried using raw materials of low impurity content, for example, severely selected talc, kaolin, alumina, etc. The honeycomb structure obtained, however, had a porosity of as low as 20 to 45%.
It was necessary that a cordierite-based ceramic honeycomb structure, when used as a carrier for an automobile exhaust gas purification catalyst, had a thermal expansion coefficient of 1.5×10
−6
/°C. or less.
In the case of a honeycomb structure having a porosity of 30% or less, use of an increased amount of an impurity and fine raw materials were necessary and consequently it was impossible to obtain a honeycomb structure having a thermal expansion coefficient of 1.0×10
−6
/°C. or less in a temperature range from room temperature to 800° C.
A cordierite-based ceramic honeycomb structure of relatively low porosity shows a large shrinkage in drying and firing steps and easily generates cracks. Therefore, it was difficult to produce such a honeycomb structure in a high yield and in a large size.
In order to alleviate these problems, JP-B-4-70053 disclosed a method for obtaining a cordierite ceramic having a higher strength by controlling its porosity at 30% or less, i.e. making it more dense.
Thereby, it was possible to prevent, in a honeycomb structure, the reduction in isostatic strength (which is a compressional load applied from the outer wall and circumference of the honeycomb structure), caused by the deformation of honeycomb cells arising during extruding.
In the above method, however, since the cordierite-based ceramic honeycomb structure has a porosity of 30% or less, the honeycomb structure did not have high catalyst coatability; the formability during extruding was not good; and the honeycomb structure had neither sufficiently thin wall thickness nor sufficiently high cell density.
SUMMARY OF THE INVENTION
In view of the above-mentioned problems of the prior art, the present invention has an object of providing a process for producing a cordierite-based ceramic honeycomb structure, wherein the formability during extruding, particularly the lubricity and the shape stability, is improved and which can produce a cordierite-based ceramic honeycomb structure having a thin partition wall and a high cell density and possessing an improved mechanical strength (isostatic fracture strength) and an improved catalyst coatability.
According to the present invention, there is provided a process for producing a cordierite-based ceramic honeycomb structure, which comprises: kneading raw materials for cordierite formation with a forming aid to obtain a raw material batch, subjecting the raw material batch to extruding to obtain a honeycomb structure, and subjecting the formed honeycomb structure to drying and firing in this order to obtain the cordierite-based ceramic honeycomb structure whose crystal phase is composed mainly of cordierite, wherein the raw material batch contains 65% by weight or more of raw materials for cordierite formation comprising talc, kaolin and aluminum hydroxide and having crystal water, and where the kaolin has an average particle diameter of 5 &mgr;m or more and a BET specific surface area of 10 m
2
/g or less and is contained in the raw material batch in an amount of 10% by weight or more.
In the present process, the kaolin preferably has a value of (average particle diameter)/(BET specific surface area), of 1 or more.
Further in the present process, the raw materials for cordierite formation preferably have, by sifting, a particle size of less than the slit width of the extrusion die used.
Furthermore in the present process, the cordierite-based ceramic honeycomb structure has a thermal expansion coefficient of 0.8×10
−6
/°C. or less between 40° C. and 800° C., in the passage direction, a porosity of 24 to 38%, and an isostatic strength of 10 kgf/cm
2
or more.
REFERENCES:
patent: 4772580 (1988-09-01), Hamanaka et al.
patent: 4877670 (1989-10-01), Hamanaka
patent: 5030398 (1991-07-01), Hamanaka et al.
patent: 5258150 (1993-11-01), Merkel et al.
patent: 5262102 (1993-11-01), Wada
patent: 5409870 (1995-04-01), Locker et al.
patent: 5916511 (1999-06-01), Kotani et al
patent: 5938992 (1999-08-01), Hamanaka et al.
patent: 6004501 (1999-12-01), Cornelius et al.
patent: 6048490 (2000-04-01), Cornelius et al.
patent: 4-70053 (1987-10-01), None
patent: 11-79831 (1999-03-01), None
Kotani Wataru
Makino Kyoko
Noguchi Yasushi
Group Karl
NGK Insulators Ltd.
Parkhurst & Wendel L.L.P.
LandOfFree
Process for production of cordierite-based ceramic honeycomb... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for production of cordierite-based ceramic honeycomb..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for production of cordierite-based ceramic honeycomb... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2458069