Process for producing composite material combining a magnesium a

Coating processes – Immersion or partial immersion – Molten metal or fused salt bath

Patent

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

4274442, 428608, 428614, B05D 118

Patent

active

057052298

ABSTRACT:
The invention relates to a composite material combining a magnesium alloy containing zirconium with a carbon reinforcement, as well as to its production process.
According to the invention, such a composite material is prepared by the infiltration of a reinforcement formed from graphite or carbon fibres by a liquid magnesium alloy containing 0.3 to 1% by weight zirconium at a temperature of 650.degree. to 850.degree. C.
Under these conditions, on said fibres is formed a zirconium carbide layer containing magnesium in solid solution and e.g. complying with the formula ZrC.sub.x Mg.sub.y with 0.3<x<1 and 0.02<y<0.12, which leads to the wetting of the fibres by the melted magnesium and to a good adhesion between the fibres and the matrix, without any deterioration to the mechanical characteristics of the fibres.

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Process for producing composite material combining a magnesium a does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Process for producing composite material combining a magnesium a, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for producing composite material combining a magnesium a will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2327250

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.