Process for producing anionic clays using magnesium acetate

Details Process for producing anionic clays using magnesium acetate Process for producing anionic clays using magnesium acetate

1999-02-10

2001-12-25

Griffin, Steven P. (Department: 1754)

Catalyst, solid sorbent, or support therefor: product or process

Zeolite or clay, including gallium analogs

Clay

C502S081000, C502S084000, C501S125000

Reexamination Certificate

active

06333290

ABSTRACT:

BACKGROUND OF THE INVENTION
This invention involves the preparation of anionic clays, more in particular, anionic clays with acetate as a charge balancing anion and the preparation of Mg—Al solid solutions by heat-treatment of the anionic clay. Anionic clays have a crystal structure which consists of postively charged layers built up of species combinations of metal hydroxides been which there are anions and water molecules. Hydrotalcite is an example of a naturally occurring anionic clay.
In hydrotalcite-like anionic clays the brucite-like main layers are built up of octahedra alternating with interlayers in which water molecules and anions, more particularly carbonate ions, are distributed. The interlayers contain anions such as NO
3
−
, OH, Cl
−
, Br, I
−
, SO
4
2−
, SiO
3
2−
, CrO
4
2−
BO
3
2−
, MnO
4
−
, HGaOs
3
2−
, HVO
4
2−
, ClO
4
−
, BO
3
2−
monocarboxylates such as acetate, dicarboxylates such as oxalate, and alkyl sulphonates such as laurylsulphonate.
It should be noted that a variety of terms are used to describe the material which is referred to herein as an anionic clay. Hydrotalcite-like and layered double hydroxide are interchangeably used by those skilled in the art. Herein we refer to the materials as anionic clays, comprising within that term hydrotalcite-like and layered double hydroxide materials.
The preparation of anionic clays has bean described in many prior art publications.
Recently, two major reviews of anionic clay chemistry were published in which the synthesis methods available for anionic clay synthesis have been summarized, F. Cavani et al, “Hydratalcitetype anionic clays: Preparation, Properties and Applications,”
Catasis Today”,
11 (1991) Elsevier Science Publishers B. V. Amsterdam.
J P Besse and others, “
Anionic clay: trends in pillaring chemistry its synthesis and micropgrous solids
” (1992)2,108 M. I. Ocelli and H. E. Robson, Van Nostrand Reinhold, N.Y.
In these reviews the authors state that a characterstic of anionic clays is that mild calcination at 500° C. results in the formation of a disordered MagO-like product. The disordered MgO-like product is distinguishable from spinel (which results upon severe calcineation) and from anionic clays. Furthermore, these Mg—Al solid solutions contain a well-known memory effect whereby the exposure to water of such calcined materials results in the reformation of the anionic clay structure.
For work on anionic clays, reference is given to the following articles:
HElv. Chim. Acta, 25, 106-137 and 555-569 (1942)
J. Am. Ceram. Soc., 42, no. 3, 121 (1959)
Chemistry Letters (Japan), 843 (1973)
Clays and Clay Minerals, 23, 369 (1975)
Clays and Clay Minerals, 28, 50 (1980)
Clays and Clay Minerals, 34, 507 (1996)
Materials Chemistry and Physics, 14, 569 (1986).
In addition there is an extensive amount of patent literature on the use of anionic clays and processes for their preparation.
European Patent Application 0 536 979 describes a method for introducing pH-dependent anions into the clay. The clay is prepared by the addition of a solution of Al(NO
3
)
3
and Mg(NO
3
)
2
to a basic solution containing borate anions. The product is then filtered, washed repeatedly with water, and dried ovenight Addtionally mixtures of Zn/Mg are used.
In U.S. Pat. No. 3,796,792 by Miyata entitled “composite Metal Hydroxides” a range of materials is prepared into which an extensive range of M
+
cations is incorporated, including Sc, La, Th, In, etc. In the examples given solutions of the divalent and trivalent cations are prepared and mixed with a base to cause co-precipitation. The resulting products are dehydrated, washed with water, and dried at 80° C. Example 1 refers to Mg and Al and Example 2 to Mg, and Bi. Other examples are given, and in each case soluble salts are used to make solutions prior to precipitation of the anionic clay at high pH.
In U.S. Pat. No. 3,879,523 by Miyata entitled “Composite Metal Hydroxides” also a large number of preparation examples is outlined. The underlying chemistry, however, is again based on the co-precipitation of soluble salts followed by washing and drying. It is important to emphasize that washing is a necessary part of such preparations, because to create a basic environment for co-precipitation of the metal ions, a basic solution is needed and this is provided by NaOH/Na
2
CO
3
solutions. Residual sodium, for example, can have a significant deleterious effect on the subsequent performance of the product as a catalyst or oxide support.
In U.S. Pat. No. 3,879,525 (Miyata) very similar procedures are again described.
In U.S. Pat. No. 4,351,814 to Miyata et al. a method for making fibrous hydrotalcites is described. Such materials differ in structure from the normal plate-like morphology. The synthesis again involves soluble salts For example, an aqueous solution of a mixture of MgCl
2
and CaCl
2
is prepared and suitably aged. From this a needlelike product Mg
2
(OH)
3
Cl.4H
2
O precipitates. A separate solution of sodium aluminate is then reacted in an autoclave with the solid Mg
2
(OH)
3
Cl.4H
2
O and few product is again fifitered, washed with water, and dried.
In U.S. Pat. No. 4,458,026 to Reichle, in which heat-treated anionic clays are described as catalysts for aldol condensation reactions, again use is made of magnesium and aluminum nitrate salt solutions. Such solutions being added to a second solution of NaOH and Na
2
CO
3
. After precipitation the slurry is filtered and washed twice with distilled water before drying at 125° C.
In U.S. Pat. No. 4,656,156 to Misra the preparation of a novel absorbent based on mixing activated alumina and hydrotalcite is described. The hydrotalcito is made by reacting activated MgO (prepared by activating a magnesium compound such as magnesium carbonate or magnesium hydroxide) with aqueous solutions containing aluminate, carbonate and hydroxyl ions. As an example the solution is made from NaOH, Na
2
CO
3
and Al
2
O
3
. In particular, the synthesis involves the use of industrial Bayer liquor as the source of Al. The resulting products are washed and filtered before drying at 105° C.
In U.S. Pat. No. 4,904,457 to Misra a method is described for producing hydrotalcites in high yield by reacting activated magnesia with an aqueous solution containing aluminate, carbonate, and hydroxyl ions.
The methodology is repeated in U.S. Pat. No. 4,656,158.
In U.S. Pat. No. 5,507,980 to Kelkar et at al. a process is described for making novel catalysts, catalyst supports, and absorbers comprising synthetic hydrotalcilike binders. The synthesis of the typical sheet hydrotalcite involves reacting pseudo-boehmite to which acetic acid has been added to peptize the pseudo-boehmite. This is then mixed with magnesia. More importantly, the patent summary states clearly that the invention uses mono carboxylic organic acids such as formic, propionic and isobutyric acid. In this patent the conventional approaches to preparing hydrotalcites are presented.
In U.S. Pat. No. 5,439,881 a process is disclosed for preparing catalysts for synthesis gas production based on hydrotalcites. The method of preparation is again based, on the co-precipitation of soluble salts by mixing with a base, for example, by the addition of a solution of RhCl
3
, Mg(NO
3
)
2
and Al(NO
3
)
3
to a solution of Na
2
CO
3
and NaOH.
Also, in U.S. Pat. No. 5,399,537 to Bhattacharyya in the preparation of nickel-containing catalysts based on hydrotalcite use is made of the co-precipitation of soluble magnesium and aluminium salts.
In U.S. Pat. No. 5,591,418 to Bhattacharyya a catalyst for removing sulphur oxides or nitrogen oxides from a gaseous mixture is made by calcining an anionic clay, the anionic clay having been prepared by co-precipitation of a solution of Mg(NO
3
)
2
, Al(NO
3
)
3
and Ce(NO
3
)
3
. The product again is filtered and repeatedly washed with deionized water.
In U.S. Pat. No. 5,114,898 /WO 9110505 Pinnavaia et al. describe layered double hydroxide sorbents for the removal of sulphur oxide(s)

Affiliated with

Also associated with

Rating

Process for producing anionic clays using magnesium acetate does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Process for producing anionic clays using magnesium acetate, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for producing anionic clays using magnesium acetate will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2558061