Process for producing a lithium transition metal sulphide

Details Process for producing a lithium transition metal sulphide Process for producing a lithium transition metal sulphide

2001-12-05

2004-05-25

Bos, Steven (Department: 1754)

Chemistry of inorganic compounds

Sulfur or compound thereof

Reexamination Certificate

active

06740301

ABSTRACT:

The present invention relates to processes for the production of suiphides, in particular lithium transition metal sulphides useful in the production of batteries, and to the use of molten sulphur as a solvent in such processes.
In the 1980's, there was extensive research into lithium metal rechargeable batteries, particularly using sulphides, but also selenides, as cathode materials. Many lithium metal/molybdenum disulphide (Li/MoS
2
) batteries were produced but these were withdrawn following an incident in which a fire was attributed to the malfunction of such a battery. Other sulphides, such as iron disulphide FeS
2
, titanium disuiphide TiS
2
and selenides, such as niobium triselenide NbSe
3
have also been particularly investigated as alternative cathode materials
Although the use of lithium metal rechargeable batteries is now limited for reasons of safety, they are still used in the laboratory testing of materials. Lithium metal primary batteries using iron disulphide cathodes are manufactured.
Virtually all modern lithium rechargeable batteries are of the lithium-ion type, in which the negative electrode (anode) comprises lithium absorbed into a carbon support. These use a lithium containing cathode material, which is usually lithium cobalt oxide LiCoO
2
although lithium nickel oxide LiNiO
2
, lithium manganese oxide LiMn
2
O
4
and mixed oxides are also known to have been used.
Due to their high cost, the use of lithium rechargeable batteries at present is mainly limited to premium applications, such as portable computers or telephones. To gain access to wider markets, for example in applications such as the powering of electric vehicles, the cost must be reduced. Hence there is a strong demand for the high performance obtainable from lithium-ion batteries at much more economical prices.
On first inspection, the use of sulphides as cathode materials is not as attractive as the use of oxides. This is because the voltage achievable from sulphides is generally only about half of that achievable using corresponding oxides. However, the capacity of batteries incorporating sulphide based cathodes, measured In ampere hours per gram of material, is about 3 times greater than corresponding batteries incorporating oxide based cathodes. This leads to an overall advantage of about 1.5 times in terms of cathode energy density for batteries with sulphide based cathodes. A further advantage is that iron sulphides, In particular ferrous sulphide (FeS), are inexpensive materials which may be dug out of the ground as natural occurring minerals. By contrast, lithium cobalt oxide is an expensive material, due mainly to the high cost of cobalt metal.
Binary transition metal sulphides are however not suitable for direct use in lithium-ion cells as they do not contain lithium. Lithium transition metal ternary sulphides, such as lithium molybdenum sulphide, lithium titanium sulphide, lithium niobium sulphide and lithium iron sulphide have been suggested as electrode materials for batteries (see for example, Japanese Kokai No 10208782 and Solid State Ionics 117 (1999) 273-276). The conventional synthesis of lithium iron sulphide is via a solid state reaction in which lithium sulphide, Li
2
S, and ferrous sulphide, FeS, are Intimately mixed together and heated under an inert atmosphere at a temperature of ca. 800° C. The reaction is diffusion controlled and the kinetics are slow. Consequently, the reaction can take up to 1 month at temperature to reach completion. This is highly inconvenient and is costly in terms of energy input. The economics of this synthesis for battery production are clearly unfavourable.
On a laboratory scale, lithium iron sulphide can be made by an electrochemical synthesis route in which a lithium metal/iron disulphide cell is discharged, and the lithium metal is removed and replaced by a carbon anode. This process however, is not amenable to scaling up. A further laboratory synthesis of lithium iron sulphide is the solid state reaction of lithium nitride, Li
3
N, with iron disulphide, FeS
2
, but again, this method is unsuitable for large scale use because of the high cost and shock sensitivity of lithium nitride.
The applicants have developed an economical synthesis which can be operated on a large scale to produce sulphides, or mixtures of sulphides, which have useful electrochemical properties.
In accordance with the present invention a process for the production of a lithium transition metal sulphide comprises reaction a transition metal sulphide with lithium sulphide in a solvent comprising molten sulphur.
Suitably the transition metal sulphide used in the process is an iron, molybdenum, niobium or titanium sulphide and is preferably an iron sulphide. Ferrous sulphide, FeS is an inexpensive and readily available naturally occurring mineral.
Preferably the reaction is carried out at a temperature of between 95.5° C. and 444° C. This is sufficient to melt the sulphur in order to allow it to act as solvent.
The reaction proceeds more rapidly than previously known processes. On a laboratory scale, the reaction can be completed in a few hours, with the actual reaction time dependent largely on the heating time of the furnace.
Although lithium sulphide may be bought commercially, for large scale production it is more economical to produce lithium sulphide via the reduction of lithium sulphate. One convenient method is to heat lithium sulphate above its melting point of 860° C. in the presence of carbon. Other standard reduction methods may equally be used, as well known in the art.
The sulphur used as the solvent is inexpensive, but it is preferably recovered from the product and reused. This may be achieved by dissolving it out of the product using a solvent. A suitable solvent is carbon disulphide, which can also be recovered and recycled if desired. Alternatively, sulphur can be removed by vapourisation, for example by heating the product sulphur mixture above the boiling point of sulphur, which is 444° C. at atmospheric pressure. A temperature in the region of 500° C. is suitable.
Lithium transition metal sulphides obtained by the above described process form a further aspect of the invention. These may comprise a single lithium transition metal sulphide phase or a mixture of lithium transition metal sulphide phases and are useful in the production of electrodes for use in batteries. In particular, they are useful in the production of electrodes for rechargeable batteries. These electrodes form the cathode, and suitable anodes are lithium ion anodes as are known in the art. Suitable electrolytes are also well known and include mixtures of inorganic carbonates, for example ethylene carbonate, propylene carbonate, diethyl or dimethyl carbonates, ethyl methyl carbonate together with a lithium salt, usually lithium hexafluorophosphate, LiPF
6
, or lithium trifluoromethane sulphonate (“triflates”), LiCF
3
SO
3
or lithium tetrafluoroboate, LiBF
4
.
Molten sulphur is not a conventional solvent in a chemical reaction, and therefor this forms a further aspect of the invention. As described above, it is particularly suitable for use as a solvent in chemical reactions used in the production of sulphides, such as lithium transition metal sulphides.


REFERENCES:
patent: 3925098 (1975-12-01), Saunders et al.
patent: 4164069 (1979-08-01), Tomczuk
patent: 4172926 (1979-10-01), Shimotake et al.
patent: 4731307 (1988-03-01), Guidotti
patent: 4761487 (1988-08-01), Godshall
patent: 4917871 (1990-04-01), Dahn et al.
patent: 5677081 (1997-10-01), Iwamoto et al.
patent: 6207327 (2001-03-01), Takada et al.
patent: 6210836 (2001-04-01), Takada et al.
patent: 0 802 161 (1997-10-01), None
patent: 2420852 (1979-10-01), None
patent: 385895 (1932-07-01), None
patent: 453203 (1935-03-01), None
patent: 2017390 (1958-12-01), None
patent: 0805922 (1979-10-01), None
patent: 2 057 412 (1981-04-01), None

Affiliated with

Also associated with

Rating

Process for producing a lithium transition metal sulphide does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Process for producing a lithium transition metal sulphide, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for producing a lithium transition metal sulphide will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3234867