ABSTRACT:
A process for preparing silica-alumina compositions comprises mixing a first aqueous solution containing an aluminum salt (preferably KAl(SO.sub.4).sub.2) and an ammonium salt (preferably (NH.sub.4).sub.2 SO.sub.4) with a second solution containing an alkali metal silicate (preferably Na.sub.2 SiO.sub.3), wherein the mol ratio of the alkali metal silicate to the aluminum salt is in the range of from about 2:1 to about 20:1, and the concentration of the ammonium salt is chosen so as to afford coprecipitation of silica-alumina hydrogel (preferably at a pH of about 3-6). The thus coprecipitated silica-alumina hydrogel can be separated from the mixture of the two solutions, optionally washed, and calcined so as to prepare acidic silica-alumina suitable as cracking catalyst material.
REFERENCES:
patent: Re23438 (1951-12-01), Ryland
patent: 2395524 (1946-02-01), Weiser et al.
patent: 2428895 (1947-10-01), Shoeld
patent: 2437533 (1948-03-01), Huffman
patent: 2448860 (1951-04-01), Bond, Jr.
patent: 2595339 (1952-05-01), Den Herder et al.
Johnson Marvin M.
Shyr Yen-Shin
Brandes K. K.
Dees Carl F.
Phillips Petroleum Company
LandOfFree
Process for preparing silica-alumina does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for preparing silica-alumina, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for preparing silica-alumina will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-22718