Process for preparing propylene homopolymers and copolymers

Details Process for preparing propylene homopolymers and copolymers Process for preparing propylene homopolymers and copolymers

1998-06-24

2002-09-24

Teskin, Fred (Department: 1713)

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

Polymerizing in two or more physically distinct zones

C526S064000, C526S068000, C526S088000, C526S905000, C525S052000, C525S053000, C525S054000, C525S240000, C525S242000, C525S319000, C525S322000

Reexamination Certificate

active

06455643

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to propylene polymerization. In particular, the present invention concerns a process for preparing homopolymers and copolymers of propylene in a reactor system comprising a combination of at least one slurry reactor and at least one gas phase reactor. The present invention also relates to an apparatus for producing homo- and copolymers of propylene.
2. Description of Related Art
A large number of processes for preparing propylene homo- and copolymers are known in the art. Thus, for example, when MgCl
2
+TiCl
4
, a conventional, supported high-yield catalyst is used for polymerization, numerous different kinds of slurry and gas phase processes can be employed. The bulk process is a slurry process, wherein the reaction takes place in pure monomer or in a reaction medium containing more than 60 wt-% of the monomer. The main advantage of a bulk process is formed by the high catalyst activity due to the fact that polymerization takes place in liquid monomer. This means that to achieve commercially acceptable catalyst productivity (expressed as kg polymer/gram of catalyst), a short residence time in the reactor is sufficient. Short residence time in the reactor means that the reactor can be of small size compared to e.g. fluid-bed gas phase reactor. The small reactor size leads to relatively low polymer inventory in the reactor, which speeds up transitions between different products.
The gas phase processes have lower activity because polymerization takes place in gaseous monomer. This leads to longer residence times, which increases the reactor size and thus polymer inventory required leading to slower grade transitions. On the other hand, the investment cost of gas phase processes is lower (less complicated), especially due to lower unused monomer recycle leading to lower recovery equipment investment costs. Another advantage of gas phase processes is the possibility to produce high comonomer content products. Still another advantage is the better inherent safety of the gas phase processes due to lower monomer inventory and lower pressure compared to bulk processes. In order to draw benefit from and avoid draw-backs of the different features of slurry bulk and gas phase processes, combined bulk and gas phase processes have been suggested in the prior art.
For polymerization of vinyl chloride there has been proposed a slurry/gas phase reactor cascade where the first reactor is a loop reactor, and the polymer content of the loop reactor is concentrated with settling legs and led to a second reactor, which is a fluidized bed reactor. Reference is made to U.S. Pat. No. 3,622,533. The polymerization is continued in the fluidized bed. The outlet is made discontinuously using a settling leg in the loop in order to minimize the reaction medium transported to the gas phase reactor.
Polymerization of propylene is a loop reactor, which can be operated in supercritical conditions, is disclosed in U.S. Pat. No. 4,740,550. The product of the loop reactor is conducted to a gas phase reactor, wherein the reaction is continued. Before entering the gas phase the fines fraction of the polymerization product of the loop reactor is removed and fully or partly circulated back to the loop reactor. Together with the fines, a part of the unreacted monomers from the gas phase reactor is recycled directly to the 1st stage loop reactor.
The main object of U.S. Pat. No. 4,470,550 is to provide a process for preparing a block copolymer of high quality by feeding homopolymer with narrow residence time distribution to the block copolymerization stage. The process disclosed comprises the following stages: first stage homopolymerization in a bulk, loop reactor, fines removal cyclone between the first and second stage, second stage homopolymerization in a gas phase reactor and finally impact copolymerization in an additional gas phase reactor.
One problem with the process in U.S. Pat. No. 4,740,550 is that if all the fines removed from the first stage loop reactor outlet are circulated back to the loop reactor, there is a risk that eventually the loop reactor is filled with inactive dead catalyst or slightly polymerized dead fines. On the other hand if a portion of this fines stream is combined with the product from the last reactor, this might cause inhomogenity problems in the final product. Still further if a portion of this fines stream is collected separately and blended with a separate homopolymer product as also suggested in U.S. Pat. No. 4,470,550, this leads to complicated and economically unacceptable operation. As will be discussed in the detailed description of the present invention, we have found that impact copolymer of high quality can be produced with two-stage homopolymerization followed by an impact copolymerization step without any fines removal and circulation either after the first or second stage homopolymerization.
In the present invention one of the main objects is to minimize the amount of circulation by a specific sequence of reactors and by selecting the relative amounts produced in each reactor with that object in mind. This is an idea, which is clearly not the object of U.S. Pat. No. 4,740,550. This point is further clarified in the detailed description of the invention and in the examples.
For polymerization of olefins a process is known in which the first reaction is made in liquid, and the second reaction in the absence of the liquid (cf. GB Patent No. 1 532 231).
A two-step process has also been suggested for polymerization of ethylene, cf. U.S. Pat. No. 4,368,291.
A slurry prepolymerization connected to the gas phase process is proposed in WO 88/02376.
A gas phase process for polyolefins, where a special catalyst with spherical form is employed, has been proposed in EP-A 0 560 312 and EP-A 0 517 183. The catalyst is prepolymerized in a loop reactor using more than 5 parts polymer and 1 part catalyst up to 10 wt-% of total production.
JP Patent Applications (Laid Open) Nos. 58/065,710, 01/263,107 and 03/084,014 describe the manufacture of propylene-ethylene block copolymers in an apparatus comprising a combination of a slurry reactor and a gas phase reactor. The polymer slurry from the slurry reactor is fed into a classifying system installed between propylene polymerization vessels, and a slurry containing coarse particles is supplied to a flash for gas separation and polymer is then fed to an ethylene-propylene copolymerization vessel, while the slurry containing fines is returned to the slurry vessel.
Some of the disadvantages associated with bulk and gas phase processes, respectively, are avoided by the suggested prior art combination processes. However, none of them meets the requirements for flexibility and low production costs dictated by the commercial production configuration. The recycling of large amounts of unreacted monomers from the the second stage reactor back to the first stage slurry (bulk) reactor increases investment and production costs and prevents independent control of reaction medium composition in the two reactors.
SUMMARY OF THE INVENTION
It is an object of the present invention to eliminate the problems related to the prior art of single and multiple-reactor processes and to provide a novel process for preparing homopolymers and copolymers of propylene (and other alfa-olefin(s)).
It is another object of the invention to provide a highly versatile process which can be used for preparing a wide range of different homopolymer and copolymer products of propylene.
It is a third object of the invention to provide a novel apparatus for producing homo- and copolymers of propylene.
These and other objects, together with the advantages thereof over known processes, which shall become apparent from specification which follows, are accomplished by the invention as hereinafter described and claimed.
The process according to the present invention is based on a combination of at least one slurry reactor and at least one gas phase reactor connected in series, in that order, to form

Affiliated with

Also associated with

Rating

Process for preparing propylene homopolymers and copolymers does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Process for preparing propylene homopolymers and copolymers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for preparing propylene homopolymers and copolymers will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2838128