ABSTRACT:
BACKGROUND OF THE INVENTION
The invention relates to a process for preparing strongly acidic gel-type cation exchangers of high stability by sulfonation, without a swelling agent, of (meth)acrylic ester-containing bead polymers.
Cation exchangers may be obtained by functionalizing crosslinked styrene bead polymers. In the functionalization, by reacting aromatic units of the polymer backbone with a sulfonating agent, for example, sulfuric acid, covalently bound sulfonic acid groups are produced.
Because of the differing polarity of the bead polymer and the sulfonating agent, the reaction of the bead polymer with the sulfonating agent is inhibited or greatly retarded. For this reason, generally, a swelling agent is added to improve the reaction kinetics. Suitable swelling agents in this context are primarily chlorinated swelling agents, such as dichloromethane, dichloroethane, or dichloropropane.
The use of chlorinated compounds as swelling agents in sulfonation is undesirable for economic reasons and particularly for ecological reasons.
There has been no lack of attempts to provide bead polymers that can be sulfonated to give strongly acid cation exchangers without addition of swelling agents. Thus, DE-AS 1,233,143, DE-AS 1,227,431, and GB 997,290 describe acrylonitrile-containing bead polymers for sulfonation free of swelling agent. The use of acrylonitrile as comonomer, however, is less expedient for ecological and toxicological reasons.
Other methods for preparing sulfonated beads are known, such as disclosed in copending application Ser. No. 10/059,650. In addition, U.S. Pat. No. 4,500,652 discloses a process for preparing cation exchangers in which the polymerized suspensions of styrene, divinylbenzene, and (meth)acrylic acid or alkyl (meth)acrylate are sulfonated without swelling agent. However, the process described in U.S. Pat. No. 4,500,652 requires as sulfonating agent sulfuric acid at a concentration of 95 to 100%. The use of sulfuric acid at this high concentration is inexpedient, because the reuse of the waste sulfuric acid produced in the sulfonation, which inherently has a lower concentration, is greatly limited. A further disadvantage is the isothermal temperature profile of, for example, 5 hours at 100° C., which requires high expenditure on control technology and high energy consumption. In addition, the proportion of broken beads in products according to U.S. Pat. No. 4,500,652 at 5 to 10% is considerable.
A problem in known cation exchangers is their sometimes inadequate stability under stress. Thus, cation exchange beads can fracture due to mechanical or osmotic forces. For all applications of cation exchangers it is necessary that in the bead shape they must retain their habit and must not be partially or completely broken down in use or disintegrate into fragments. Fragments and bead polymer splinters can, during purification, pass into the solutions to be purified and themselves contaminate these solutions. In addition, the presence of damaged polymer beads is inexpedient for the functioning of the cation exchangers themselves when used in column processes. Splinters lead to an increased pressure drop over the column system and thus decrease the throughput through the column of liquid to be purified.
It is an object of the present invention, therefore, to provide a simple, robust, and economic process for preparing gel-type cation exchangers of high stability.
SUMMARY OF THE INVENTION
The object is achieved by, and the present invention relates to, a process for preparing gel-type cation exchangers of high stability comprising sulfonating (meth)acrylic ester-containing crosslinked bead polymers in the absence of a swelling agent using sulfuric acid having a concentration of from 90 to 95% by weight, wherein the temperature during the sulfonation is increased by the heat of reaction and/or heat of dilution that occurs during the process up to an end temperature of 150 to 170° C.
DETAILED DESCRIPTION OF THE INVENTION
Suitable (meth)acrylic ester-containing crosslinked bead polymers according to the invention are copolymers of styrene, divinylbenzene, and (meth)acrylic esters.
(Meth)acrylic esters, for the purposes of the present invention, are the esters of acrylic acid or methacrylic acid. Those which are preferred according to the invention are C
1
-C
4
-alkyl or C
1
-C
4
-hydroxyalkyl esters. Particularly preferred (meth)acrylic esters are methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl acrylate, hydroxyethyl acrylate, hydroxypropyl acrylate, methyl methacrylate, ethyl methacrylate, hydroxyethyl methacrylate, and hydroxypropyl methacrylate. Methyl acrylate is particularly preferably used.
The copolymerized divinylbenzene content in the bead polymer is 2 to 20% by weight, preferably 4 to 12% by weight, particularly preferably 6 to 10% by weight. Technical-grade qualities of divinylbenzene can be used to prepare the bead polymer that, in addition to the isomers of divinylbenzene, contain customary by-products such as ethylvinylbenzene. According to the invention, technical-grade qualities having divinylbenzene contents of 55 to 85% by weight are particularly highly suitable.
(Meth)acrylic ester is present in the bead polymer in copolymerized form in amounts of 1 to 8% by weight, preferably 2 to 6% by weight.
The bead polymers that are suitable according to the invention are prepared by the known method of suspension polymerization. In this case, to a mixture of styrene, divinylbenzene, and (meth)acrylic ester is added at least one free-radical former in an aqueous phase that contains a dispersant, and the mixture is divided into droplets with stirring and cured at elevated temperature.
A particular embodiment of the present invention uses a bead polymer in the preparation of which a mixture of free-radical initiators of differing decomposition temperatures was used. Those which are highly suitable are, for example, mixtures of dibenzoyl peroxide or tert-butyl peroxybenzoate or mixtures of tert-butyl peroxy-2-ethylhexanoate and tert-butyl peroxybenzoate. It is particularly advantageous to increase the polymerization temperature with advancing polymerization conversion rate, for example, from an initial temperature of 60 to 70° C. to a final temperature of 90 to 150° C.
A further particular embodiment of the present invention uses a bead polymer in the preparation of which a water-soluble cellulose derivative is used as dispersant. Those which are highly suitable are cellulose esters or cellulose ethers, such as carboxymethyl cellulose, hydroxyethyl cellulose, or hydroxyethyl methyl cellulose. The initial amount of cellulose derivative is generally 0.05 to 1%, based on the water phase, preferably 0.1 to 0.5%.
The particle size of the bead polymer is 100 to 1000 &mgr;m, preferably 200 to 500 &mgr;m. Not only bead polymers having a wide particle size distribution, but also those having a narrow particle size distribution—or monodisperse bead polymers—can be used. Monodisperse in the context of the present invention means that the quotient of the 90% value and the 10% value of the volume distribution function is less than 2, preferably less than 1.5, particularly preferably less than 1.25.
The bead polymers to be used as starting material according to the invention can have a substantially homogeneous network structure. Those which are preferably suitable according to the invention are also bead polymers having what is termed an IPN structure (InterPenetrating Network), which may be produced by the seed/feed process known from the prior art.
The crosslinked bead polymers are converted to cation exchangers by sulfonation. The sulfonating agent is a sulfuric acid having a concentration of 90 to 95%. It is advantageous to adjust the required acid concentration by admixing sulfuric acid of a higher and a lower concentration, in which case the sulfuric acid of lower concentration that is used is recovered sulfuric acid from earlier sulfonation reactions. The sulfuric acid is preferably mixed in the sulfonation reactor in the presence of the bead poly
Dimotsis George L.
Klipper Reinhold
Podszun Wolfgang
Akorli Godfried R.
Bayer Aktiengesellschaft
Eyl Diderico van
Lipman Bernard
LandOfFree
Process for preparing gel-type cation exchangers does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for preparing gel-type cation exchangers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for preparing gel-type cation exchangers will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3315198