Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Polymers from only ethylenic monomers or processes of...
Reexamination Certificate
2001-06-14
2003-07-01
Zitomer, Fred (Department: 1713)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Polymers from only ethylenic monomers or processes of...
C526S247000, C526S250000
Reexamination Certificate
active
06586546
ABSTRACT:
CROSS REFERENCE TO RELATED APPLICATION
This application claims benefit of Japanese application number 2000-182615 filed Jun. 19, 2000.
FIELD OF THE INVENTION
The present invention relates to a process for copolymerizing tetrafluoroethylene (TFE) and perfluoro(alkyl vinyl ether) (PAVE) to give a melt-fabricable copolymer with uniform distribution of the monomers in the polymer. It further relates to a process for manufacture which enables the formation of a melt-fabricable copolymer of tetrafluoroethylene and perfluoro(alkyl vinyl ether) having narrow molecular weight distribution and having excellent mechanical properties such as flex life.
BACKGROUND OF THE INVENTION
TFE/PAVE copolymer (PFA), has the advantage over TFE homopolymer (PTFE) that is melt-fabricable, and yet retains the excellent properties of PTFE such as heat resistance, corrosion resistance, weathering resistance, and the like. By melt-fabricable is meant that the copolymer can be processed into shaped articles such as films, fibers, tubes, wire coatings and the like by conventional melt extruding means. Because of this, PFA finds extensive commercial use.
In PFA it is desirable that the monomer be incorporated uniformly in the polymer chain, as determined by the concentrations and relative reactivities of the monomers toward polymerization. However, because TFE is a more reactive monomer than PAVE, and has a strong tendency to homopolymerize, attempts to copolymerize TFE with PAVE can yield polymer in which the monomers are not incorporated uniformly, but rather with TFE-rich portions and PAVE rich portions, and possibly even some PTFE. The portions of the polymer richer in TFE are higher melting, and PTFE may not melt at all. This can affect the melt-processibility of the polymer, and cause “gel”, bits of unmelted or imperfectly melted polymer, which is especially noticeable in film extrusion or molding.
Nonuniform incorporation of monomer can broaden molecular weight distribution (MWD), with excessive TFE incorporation giving high molecular weight polymer. Because PFA grades are classified by melt viscosity, polymer with too much high molecular weight component will also require excessive low molecular weight component to be in specification with regard to melt viscosity, usually expressed as melt flow rate (MFR). The result is an overbroad molecular weight distribution. The presence of greater amounts of low molecular weight material can affect the durability of articles molded therefrom, for example by reducing flex life. Therefore, as has been disclosed in U.S. Pat. No. 3,635,926, PFA with a broad molecular weight distribution tends to give inferior physical properties compared to PFA with a narrower molecular weight distribution even at equivalent melt viscosities.
Flex life, an indication of strength against repeated flexing, as a function of MFR, PAVE content, and MWD, can be measured by performance testing, such as in accordance with the “MIT Flex Test”, ASTM D 2176, or can be expressed by the equation given below, where the flex life (number of cycles to failure) is [FL]; PAVE content (% by weight) is [PAVE]; MFR (g/10 min) is [MFR]; and molecular weight distribution is represented by the molecular weight distribution index [MWDI], which is defined in the Example Section (“ln” is the natural logarithm):
ln[
FL]=B
1
+B
2
·ln[
MFR]+B
3
·ln[
MWDI]+B
4
·ln[
PAVE]
The equation suggests a high flex life PFA can be obtained by reducing MFR, increasing the PAVE content, and/or increasing MWDI. For example, when coefficients B
1
-B
4
are calculated from observed values from TFE/PPVE copolymer, equation (1) below results.
ln[
FL]=
11.208−1.695·ln[
MFR]−
7.846·ln[
MWDI]+
3.648·ln[
PAVE]
(1)
With TFE/PAVE polymers of other perfluoro(alkyl vinyl ethers), the coefficients are slightly different, but the conclusion is the same. In actual flex life testing, flex life improves as molecular weight distribution narrows (uniformity increases), copolymer composition and melt viscosity being held constant.
MFR must be high enough to permit melt processing of the PFA; the PAVE content must also be limited within a certain narrow range in view of PFA physical properties and for economic reasons. Therefore, with the MFR and PAVE content fixed, MWDI presents an important means for improving the physical properties. For example, if PAVE content is fixed at 5.5% by weight and MFR at 5.0 g/10 minutes, the flex life as a function of MWDI is represented by Equation 2 below, which shows that a small variation of MWDI will significantly affect the flex life.
ln[
FL]=
14.70−7.846·ln[
MWDI]
(2)
The above reasoning leads to the conclusion that one should make a copolymer with as uniform a distribution as possible with respect to TFE and PAVE and a narrow molecular weight distribution by suppressing the homopolymerization of the TFE monomer in the manufacture of PFA.
To increase copolymer uniformity, it has been traditional to polymerize in a chlorofluorocarbon (CFC) solvent such as CFC-113 (CFCl
2
—CF
2
Cl) or CFC-114 (CF
2
Cl—CF
2
Cl). However, the use of CFCs has been restricted for environmental reasons. Aqueous emulsion polymerization is an alternative method, but it is more difficult to obtain uniform copolymer in aqueous polymerization. U.S. Pat. No. 3,635,926 discloses the use of gaseous chain transfer agents such as methane, ethane, and hydrogen as a way to narrow molecular weight distribution in TFE/PAVE copolymers. Improvements are needed in aqueous polymerization of TFE/PAVE copolymers to further narrow molecular weight distribution.
SUMMARY OF THE INVENTION
As a result of studies by the inventors to overcome the above problems and to polymerize so as to generate a more uniform copolymer with a narrower molecular weight distribution for improved flex life, they have discovered that copolymerization of TFE and PAVE in the presence of a terpene in an aqueous polymerization medium produces a melt-fabricable TFE/PAVE copolymer (PFA) having a uniformly distributed PAVE. The small amount of terpene added to the polymerization system does not decrease the rate of polymerization, but is present in an amount that is effective to improve the uniformity of the resin by narrowing the molecular weight distribution.
The present invention is a process for manufacturing PFA, which comprises copolymerizing TFE and PAVE in the presence of a terpene in an aqueous polymerization medium. The resulting PFA copolymer has a narrower molecular weight distribution than obtained heretofore, this narrower molecular weight distribution being characterized by a half-width value in its differential scanning calorimeter (DSC) melting peak which is at least 10% less than the half width value of the copolymer when made without the presence of the terpene.
DETAILED DESCRIPTION
The comonomer PAVE (perfluoro(alkyl vinyl ether)) used in this invention is a compound that is also called perfluoroalkoxytrifluoroethylene, represented by formula 3 below.
CF
2
═CF—O—C
n
F(
2n+1
) (3)
In the PAVE of this invention n=1-10, preferably n=1-3, exemplified by such PAVEs as perfluoro(methyl vinyl ether) (PMVE), perfluoro(ethyl vinyl ether) (PEVE), perfluoro(propyl vinyl ether) (PPVE), more preferably by perfluoro(propyl vinyl ether) (PPVE).
The PAVE content in the PFA of this invention is sufficient to make the copolymer melt-fabricable and is about 0.5-20 mole %, preferably about 1 to 15 mole %, more preferably about 2 to 10 mole %.
Copolymerization of TFE with PAVE is carried out in an aqueous medium. The polymerization medium is essentially deionized water, optionally containing a small amount of other solvents but not more than about 5% by volume of the total volume of solvent.
To control the molecular weight and molecular weight distribution, the aqueous emulsion polymerization process is carried out, preferably
Iwasaki Takahiko
Kino Masahiro
DuPont-Mitsui Fluorochemicals Co. Ltd.
Zitomer Fred
LandOfFree
Process for manufacture of a copolymer of... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for manufacture of a copolymer of..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for manufacture of a copolymer of... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3000890