Process for direct production of cast iron from fine iron...

Details Process for direct production of cast iron from fine iron... Process for direct production of cast iron from fine iron...

1999-12-20

2002-03-05

Andrews, Melvyn (Department: 1742)

Specialized metallurgical processes, compositions for use therei

Processes

Producing or treating free metal

C075S501000, C075S502000

Reexamination Certificate

active

06352574

ABSTRACT:

TECHNICAL FIELD
The invention relates to a process and to an apparatus for direct production of cast iron from iron bearing ore (hereinafter referred to as “iron ore”) having grains of different sizes and from fine coal.
Other processes for producing cast iron from coke and iron ore after pre-treatment processes like sintering or pelletizing are well-known and experimented and are presently the most common industrial way of producing cast iron. Processes for producing cast iron directly from iron and coal are presently under study.
1. Background Art
In the U.S. Pat. No. 3,607,224 a process is described where the whole conversion from iron ore into molten cast iron is carried out in one reactor, by adding some reagents in tangential direction into the reactor's top chamber.
In Malgarini et al. “First results from cleansmelt ironmaking pilot plant”—Iron and Steel Engineer Vol. 74, N
o
1, P.30-31, Jan. 1997 a smelting reduction process is described wherein a reactor including a zone for prereduction and preheating and a zone for final reduction and carburization of liquid metal is described.
EP-690 136 describes a two-stages process for production of iron from iron compounds in a two chamber apparatus.
EP-726 326 describes a two-stages process for the production of pig iron wherein iron ore is directly reduced in a pre-reduction stage followed by a final reduction stage.
2. Disclosure of the Invention
The present invention relates to a process and to an apparatus for the production of molten cast iron in one single reactor from iron ore, fine coal, oxygen and fluxes.
More particularly, the present invention refers to a process for producing cast iron directly from fine iron ore and fine coal in an apparatus comprising one reaction chamber (reactor) only that includes two areas in open communication, one top area and one bottom area, where the process is carried out, this process being characterized by comprising the operations of:
feeding fine iron ore together and simultaneously with oxygen or preferably with a mixture of oxygen and air into the top area of the reactor through its side walls;
feeding fine coal, oxygen, fluxes and a carrier gas into the bottom area of the reactor through its side walls and a stirring gas from its bottom.
The invention provides carrying out the process in one reaction chamber (reactor) where two process stages take place, in two separated areas (hereinafter also referred to as “the dresser” and “the converter” for the top area and the bottom area respectively).
The two process stages are as follows:
in the dresser: iron ore is fed through a plurality of nozzles and carried by a stream of oxygen or preferably by a mixture of oxygen and air. It comes in contact with a hot and reducing gas generated in the bottom area of the reactor (converter), under such conditions that a partial combustion of the gas coming from the converter takes place, which cause a pre-heating and pre-reduction of the iron ore.
The pre-heated and pre-reduced iron ore is fed into the converter. The converter's performances depend on the chemical and thermal performances that are obtained in the dresser, and in particular on the pre-reduction degree and on the pre-heating temperature of the pre-reduced iron ore.
in the converter: the pre-reduced iron ore is completely reduced and molten cast iron is generated. A fuel, e.g. fine coal, and a supporter of combustion, e.g. oxygen, together with fluxes, a carrier gas and a stirring gas are introduced into the converter, where the hot reducing gas, which is fed into the dresser, is produced together with cast iron.
The dresser is connected to a discharge conduit for discharge of process gas. The process gas leaving the discharge conduit is cooled down by water jets and then crosses a Venturi pipe scrubber, where the particulate that may have formed in the gas is made to settle. Finally the gas is released into the utility network.
The process described can produce cast iron by operating the dresser in such a way so to pre-reduce iron ore at least into Fe
3
O
4
, while it is pre-heated to temperatures not lower than 800° C.
It is known that the main component of iron ore is hematite (Fe
2
O
3
) which can be reduced to Fe
3
O
4
at temperatures that are not very high and in environment of relatively low reducing potential (CO/(CO+CO
2
)>0.1 and H
2
/(H
2
O+H
2
)>0.1).
As a consequence, pre-reducing iron ore to Fe
3
O
4
is a feasible target and the finer is iron-ore grain, the quicker the kinetics of the reaction. With a gas temperature around 1600° C. or higher and iron-ore grain of a few millimeters, pre-heating iron ore to approx. 800° C. can take a remarkably short time of around one second of interaction between gas and iron ores.
Preferably the iron ore has a grain size smaller than 8 mm, and has a content of iron at least in part lower than 50%. The velocity of iron ore and oxygen introduction in the reactor top chamber is generally lower than 40 m/s.
The energy required by the chemical reactions and physical transformations taking place in the converter is mainly provided by the post-combustion of the reducing gas with oxygen (the oxygen blown into the converter is hereinafter referred to as “primary” or “secondary” according to whether it is injected to a lower or higher level in the converter, while the oxygen blown in the dresser can be referred to as “tertiary”). The reducing gas is generated from coal gasification when coal interacts either with (primary) oxygen blown together with coal, or with oxygen associated with the pre-reduced iron ore. The gasification reaction requires an adequate temperature in the system in order to be activated. Coal and (primary) oxygen are injected into a molten slag bath, that is composed of mineral gangue and ashes from coal and fluxes and which floats on the molten cast iron bath throughout the bath formation.
The grain size of fine coal and fine fluxes is preferably smaller than 3 mm. In the converter, iron oxides are reduced into metallic iron when they react with the coal scattered in the slag and with carbon monoxide that generates from coal gasification with primary oxygen: at the same time, iron is carburized resulting in molten cast iron. The chemical and thermal energy required by these reactions is provided by oxygen blown in the slag and by coal injected either as fine coal or added partly as fine coal and partly as sized coal that falls down under its own weight.
Simultaneous injection of coal and oxygen under the liquid slag surface by means of co-axial lances, the coal being carried by an inert gas, creates the appropriate temperature conditions and intimate mixing of coal and oxygen for a rapid coal gasification thus allowing to utilize any kind of coal, from low-volatile to high volatile.
Primary oxygen injection is adjusted so as to keep residual non-gasified coal scattered in the slag bath. It contributes to the final reduction of iron ore into metallic iron and to its carburization into cast iron.
Also secondary oxygen is injected under the slag surface so that heat from post-combustion develops inside the slag.
Heat transfer from slag to cast iron and uniformity of temperature and chemical composition within the slag and the metallic phase are assured efficiently by the convective motions induced by injecting coal and primary and secondary oxygen and by blowing the inert gas from the reactor's bottom.
Coal and primary oxygen lances are also used to inject basic fluxes (mainly calcium oxide) together with coal and simultaneously to primary oxygen. Preferably the ratio coal to flux ranges from 3 to 15.
Under these conditions, coal gasification occurs in the presence of a high local concentration of calcium oxide that permits on the one side to improve fixing in the slag—in the form of stable compounds—of sulphur from coal gasification, and on the other side to quickly neutralize silica from the coal ashes.
The process as above described provides for a number of benefits:
the tendency of sulphur to solubilize into cast iron is reduced, thus im

Affiliated with

Also associated with

Rating

Process for direct production of cast iron from fine iron... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Process for direct production of cast iron from fine iron..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for direct production of cast iron from fine iron... will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2837408