Coating processes – With post-treatment of coating or coating material – Heating or drying
Reexamination Certificate
1999-03-19
2002-05-28
Beck, Shrive P. (Department: 1762)
Coating processes
With post-treatment of coating or coating material
Heating or drying
C427S389900, C427S391000, C427S397700
Reexamination Certificate
active
06395338
ABSTRACT:
TECHNICAL FIELD OF THE INVENTION
The field of patent application Ser. No. 09/230,339 commonly owned, is that of silicone compositions which are crosslinkable by activation, which can be used in particular to form an anti-adhesive coating or film for a fibrous or non-fibrous support, for example a support made of paper or the like, or alternatively made of natural or synthetic polymer.
More specifically, the invention relates, in the first of these aspects, to a process for the continuous coating of a travelling support strip (e.g. paper, fabric, polymer), in order to give it anti-adhesion properties, the said coating being carried out using a silicone composition based on polyorganosiloxane (POS).
The anti-adhesive POSs which are of interest in the context of the invention taken in its first aspect are of the type which are crosslinkable rapidly (“fast cure”) and at low temperature (low-temperature cure), by hydrosilylation or by dehydrogenopolycondensation, thermally or by a combination of heat and radiation (UV radiation or an electron beam). Such low-temperature cure and fast cure silicone compositions will be defined by the name: LTC/FC silicone systems.
The invention also relates to the device involved in the continuous coating process.
The anti-adhesive silicone compositions concerned comprise at least one POS A, a crosslinking agent B which is a POS and a catalyst. These ternary compositions can only exist transiently in non-crosslinked form. The reason for this is that, irrespective of the crosslinking mechanism concerned: hydrosilylation or dehydrogenopolycondensation, POSs of SiH type placed in the presence, in the first case, of POSs of SiVi type and of platinum hydrosilylation catalyst, or placed in the presence, in the second case, of POSs of SiOH or SiOR type and of platinum or tin condensation catalyst crosslink relatively quickly. The kinetics of crosslinking depends in particular on the reaction temperature.
These silicone systems are also characterized by bath lifetimes BLTs. The term BLT denotes the time required to double the dynamic viscosity measured at 30° C. The dynamic viscosity can be measured using a Brookfield viscometer according to the indications of AFNOR standard NFT 76102 of May 1982.
For the anti-adhesion treatments of supports (paper, fabric or polymer film), which consist in coating the surface of these supports with the abovementioned silicone compositions, it is imperative to apply and spread the said compositions when they are in non-crosslinked liquid form and thus entirely suited for use in the said operations.
Once the supports are coated with silicone composition, they are subjected to heating so as to accelerate their crosslinking.
The problematics underlying the invention, taken in its first aspect, described and claimed in the patent application of Ser. No. 09/230,339, commonly owned, is the provision of an anti-adhesive silicone coating process which:
1) offers a compromise between the parameters of reactivity; crosslinking temperature; crosslinking kinetics; and bath lifetime; and
2) involves a procedure for accurate metering and the preparation of a homogeneous mixture of the ingredients of the silicone composition, by using suitable means and by opting to vary operating parameters which are carefully selected.
With respect to point 1): as regards the crosslinking temperature, it is desirable to be able to allow low temperatures (which can be less than or equal to 110° C.), thus allowing the coating to be spread and crosslinked on beat-sensitive supports such as, for example, polyethylene, polypropylene, PVC and (to a lesser extent) polyethylene glycol terephthalate; as regards the crosslinking kinetics, it is also desirable to have available a process in which the silicone composition may be crosslinked, even at low temperature, according to high crosslinking kinetics so as to achieve gains in production efficiency and viability; and, as regards the BLT parameter, it is also desirable to have available a process which allows a reduction in the crosslinking temperature, while at the same time retaining bath lifetimes, for the non-crosslinked liquid silicone composition, which are of an acceptable level to allow industrial users a sufficient margin for carrying out the silicone coating at the required industrial rate and scale.
With respect to point 2), the carefully selected operating parameters are:
the bath lifetime, which is controlled by varying the nature and/or proportions of the components A, B and C and/or of their possible premixes,
the homogeneity of the mixture, which is controlled via the DSC signature, allowing calibration relative to a reference mixture, and
the flow rate of production of homogeneous mixture, which is adjusted to the rate of consumption with or without formation of a coating buffer tank, the mixture thus metered and homogenized being conveyed directly to the coating head of the machine, such that only the amount of mixture required to feed the coating head is prepared.
Thus, the invention according to the patent application of Ser. No. 09/230,339, commonly owned, taken in its first aspect, relates more specifically to a process for the continuous coating of a travelling support strip in order to give it anti-adhesion properties, the said coating being carried out using a silicone composition comprising: at least one polyorganosiloxane A, at least one crosslinking agent B which can be crosslinked by hydrosilylation and/or by dehydrogenopolycondensation, and an effective amount of catalyst C,
characterized in that it consists, essentially:
1. in continuously mixing in measured amounts, in particular, the POS(s) A bearing reactive groups RGa, the crosslinking agent(s) B bearing reactive groups RGb, and the catalyst C; by:
optionally preparing at least one premix AB and/or AC and/or BC when this premix can be prepared,
selecting mixing conditions such that:
the bath lifetime (BLT) is less than 10 h,
the bath homogeneity is such that its differential scanning calorimetry DSC signature comprises at least one essentially Gaussian peak showing,
a peak start temperature T1,
a peak summit temperature T2,
a peak end temperature T3,
this peak being characterized by:
i—T3≦110° C.,
ii—&Dgr;T=T3−T1≦30° C., T3 possibly not being able to satisfy the parameter—i—above, and
iii—&Dgr;T=&Dgr;T ref±10° C.,
&Dgr;T ref corresponding to T3ref−T1ref, obtained from the DSC signature peak of a reference ABC mixture prepared according to the procedure Pr defined below in the present specification,
the flow rate of production of the homogeneous mixture is between a value corresponding to the rate of consumption of the mixture on the coating site(s) and a value which determines the constitution of a buffer tank, this flow rate value being such that the duration separating the time at which the components A, B and C are placed together and the time of application of the composition ABC to the travelling support strip is less than or equal to the BLT,
2. in conveying, simultaneously or otherwise, the composition directly from the mixer to the coating site(s),
3. in coating the travelling support strip with the composition,
4. in allowing the crosslinking to take place.
The DSC (Differential Scanning Calorimetry) analysis is carried out, in a manner which is known per se, using a Metler TA 4000 type machine with the following operating parameters: rate of temperature increase: 10.0° C./min; mass of the test sample: 15 mg; working in an open aluminium crucible.
The inventors have, to their credit, developed a continuous coating method which makes it possible industrially to use thermal silicone systems which crosslink (polyaddition or dehydrogeno-polycondensation) at low temperatures and with BLTs as short as values of less than 10 hours.
This innovation requires both expertise in silicone chemistry and, on the one hand, mastery of techniques for precise metering in ratios which can be as low as 1:100 or less than 1:100, and, on the other hand, for continuous intimate mixing of more or l
Benayoun Jean-Paul
Desne Francois
Guyot Christophe
Lievre Andre
Mirabel Bernard
Beck Shrive P.
Crockford Kirsten A.
Rhodia Chimie
LandOfFree
Process and device for coating a support using a... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process and device for coating a support using a..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process and device for coating a support using a... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2852508