Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Mixing of two or more solid polymers; mixing of solid...
Reexamination Certificate
2001-09-17
2003-11-04
Woodward, Ana (Department: 1711)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Mixing of two or more solid polymers; mixing of solid...
C525S165000, C525S166000, C525S179000, C525S199000, C525S200000
Reexamination Certificate
active
06642310
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to extrusion of non-fluorinated melt-processable polymers which contain fluoropolymer processing aids.
BACKGROUND OF THE INVENTION
The melt extrusion of high molecular weight polymers, for example, hydrocarbon polymers and polyamides, into shaped structures such as tubing, pipe, wire coating or film is accomplished by well-known procedures wherein a rotating screw pushes a viscous polymer melt through an extruder barrel into a die in which the polymer is shaped to the desired form and is then subsequently cooled and solidified into a product having the general shape of the die.
In order to achieve low production costs, it is desirable to extrude the polymer at rapid rates. Higher extrusion rates may be readily obtained by increasing the rate of revolution of the extruder screw. However, this technique is subject to limitations imposed by the viscoelastic properties of the polymer substrate. Thus, at very high extrusion rates an unacceptable amount of thermal decomposition of the polymer can result. Further, extrudates having a rough surface are often obtained which can lead to formation of an undesirable pattern on the surface of the extrudate. These surface defects are also known as melt fracture. Extrusion at elevated temperatures obviates this problem but adds to processing costs. Also, cooling of the extrudate becomes problematic. In addition, if polyolefins are extruded at temperatures near their decomposition points, polymer degradation occurs.
It is desirable, therefore, to find highly efficient means of increasing the extrusion rate without raising the melt temperature, while producing articles having smooth surfaces. Changes in extruder and die configuration can improve polymer melt flow, but these modifications are not always practical or economically feasible. Another approach involves the addition of conventional wax-type process aids which reduce bulk viscosity and in some cases improve processing properties. However, the efficiency is marginal and the high levels of additive required often adversely affect other properties.
In Blatz, U.S. Pat. No. 3,125,547, it is disclosed that the use of 0.01-2.0 wt. % of a fluorocarbon polymer that is in a fluid state at the processing temperature (e.g. a fluoroelastomer) will reduce die pressure in extrusions of both high and low density polyethylenes, as well as other polyolefins. Further, use of this additive allows significant increase in extrusion rates without melt fracture.
Kamiya and Inui, in Japanese Examined Patent Application Kokoku 45-30574, cite the use of crystalline fluorocarbon polymers at temperatures below their melting points to eliminate die build-up, but they disclose nothing regarding other extrusion improvements.
Nishida, et al., in Japanese Patent Application Publication Kokai 62-64847, disclose injection molding compositions comprising a mixture of a) an ethylene/alpha olefin copolymer having a melt flow rate (MFR) of 0.2-200 g/10 minutes and a density of 0.850-0.945 g/cm
3
, with b) 0.001-1% by weight of a fluorinated hydrocarbon polymer having a fluorine to carbon ratio of at least 1:2.
Chu, in U.S. Pat. No. 4,740,341, discloses blends having improved extrudability comprising linear polymers of ethylene having incorporated therein small amounts of fluorocarbon polymers and polysiloxanes. The fluorocarbon polymers have fluorine to carbon ratios of at least 1:2 and are fluid at 120°-300° C.
Larsen, in U.S. Pat. No. 3,334,157, discloses polyethylene which has been modified to improve its optical properties by incorporation of 0.015 to greater than 1.7% by wt., based on the mixture, of finely divided polytetrafluoroethylene.
More recently, improved fluoropolymer process aid compositions have been disclosed in for example, U.S. Pat. Nos. 4,855,360; 5,587,429 and 5,707,569. In these fluoropolymer process aid compositions, a second additive, such as a poly(oxyalkylene) or an ionomer resin, is introduced in order to improve extrusion processability of the non-fluorinated polymer.
In order to maximize processability improvements, the prior art has stated that it is desirable that the fluoropolymer process aid compositions be well dispersed in the non-fluorinated polymer which is to be extruded and that the smaller the particle size of the fluoropolymer, the better the dispersion and thus the better the processability. See, for example, “Dynamar™ Polymer Processing Additive Optical Microscopy Method for Dispersion Analysis in Polyolefins ” (Dyneon 1997), which recommends uniform dispersions and fluoropolymer process aid particle sizes 2 microns or less in the extrudate; “Dynamar™ Polymer Processing Additives Direct Addition During Resin Manufacture ” (Dyneon 12/2000), which recommends uniform dispersions and fluoropolymer process aid particle sizes of 3 microns or less in the extrudable composition. Similar recommendations have been made in U.S. Pat. Nos. 3,125,547; 5,010,130; and 6,048,939.
Due to these references which teach that extrusion processability is improved by improving the degree of the dispersion of the fluoropolymer process aid in the melt processable polymer, and by decreasing the particle size of the fluoropolymer, much of the prior work in this field has focused on improving the quality of the dispersion and minimizing the fluoropolymer particle size. Still, there is room for improvement in extrusion processability.
SUMMARY OF THE INVENTION
It has been surprising discovered that extrudable compositions which contain predominantly large particle size fluoropolymer actually process better, exhibiting fewer melt defects and have faster conditioning times, than those compositions which follow the recommendations of the prior art and strive for maximum fluoropolymer dispersion. By “predominantly large particle size fluoropolymer” is meant a weight average particle size (as hereinafter defined) of greater than 2 microns, but less than 10 microns, as measured at a point immediately preceding the die. Extrudable compositions which contain predominantly large particle size fluoropolymer can be achieved by a number of means.
Accordingly, one aspect of the present invention is an extrudable composition for passing through a die, said composition comprising:
A) a non-fluorinated melt processable polymer; and
B) 25 to 2000 parts per million by weight, based on total weight of the extrudable composition, of fluoropolymer, said fluoropolymer having a weight average particle size greater than 2 microns and less than 10 microns, as measured at a point immediately preceding the die; and wherein said composition is substantially free of interfacial agent.
Another aspect of the present invention is an extrudable composition for passing through a die, said composition comprising:
A) a non-fluorinated melt processable polymer;
B) 25 to 2000 parts per million by weight, based on total weight of the extrudable composition, of a fluoropolymer, said fluoropolymer having a weight average particle size greater than 2 microns and less than 10 microns, as measured at a point immediately preceding the die; and
C) at least an effective amount of interfacial agent to achieve a fluoropolymer weight average particle size greater than 2 microns and less than 10 microns, as measured at a point immediately preceding the die, but no more than a 5:1 weight ratio of interfacial agent to fluoropolymer.
Another aspect of the instant invention is a process aid masterbatch comprising:
A) a non-fluorinated melt processable polymer;
B) 1 to 50 weight percent, based on total weight of the masterbatch, of fluoropolymer; and
C) at least an effective amount, to improve processability, of interfacial agent, but no more than a 5:1 weight ratio of interfacial agent to fluoropolymer, with the proviso that if the interfacial agent is a poly(oxyalkylene) polymer, it is present at less than a 1:1 weight ratio of poly(oxyalkylene) polymer to fluoropolymer.
DETAILED DESCRIPTION OF THE INVENTION
The present invention is directed to means for improving the extrusion processability of non-fluorinated m
Chapman, Jr. George Richard
Oriani Steven Richard
DuPont Dow Elastomers L.L.C.
Woodward Ana
LandOfFree
Process aid for melt processable polymers does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process aid for melt processable polymers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process aid for melt processable polymers will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3175193