Pressure resistant and heat-stable insulating coatings for...

Coating processes – With post-treatment of coating or coating material – Heating or drying

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C427S385500, C428S423100, C428S406000, C523S219000

Reexamination Certificate

active

06387447

ABSTRACT:

This application is a 371 of PCT/EP 98/04105 filed on Jul. 3, 1998.
The invention relates to insulating coatings containing polyurethane groups and/or polyisocyanurate groups for hollow bodies, in particular pipes, and a process for the production thereof.
As is known, PUR foams and PUR elastomers, inter alia, are employed for insulating oil and gas pipelines in the offshore sector.
EP-A 636 467 describes how a thick-layered PUR coating of rotational bodies, such as rolls and pipes. can be carried out in one operation. Inter alia, coating of pipes with syntactic PUR slurries for insulation is also known.
The requirements profile of such insulating materials is increased significantly by the opening-up of new oil fields at deeper sea depths. Inter alia, the heat distortion point of these materials must be increased from previously 120° C. to 160° C. and the compressive strength must be increased from previously 50 bar (500 m immersion depth) up to 250 bar (2.500 m immersion depth).
However, the polyurethane materials described above are limited in long-term heat resistance to approx. 120° C.
The object of the present invention was therefore to discover insulating coatings for pipes, which have a heat distortion point above 120° C. and a compressive strength above 50 bar.
Surprisingly, it has been found that by combination of polyisocyanurate reaction compositions with heat- and pressure-stable hollow microbodies, the desired requirements can be met and the economical rotary coating process mentioned in EP-A 636 467 can be used for straight and slightly curved pipes. Pipe bends and connections can be produced by mould casting on the same raw material basis.
The invention therefore relates to a process for the production of insulating coatings containing polyurethane groups and/or polyisocyanurate groups for hollow bodies by reaction of
a) a polyisocyanate component with
b) compounds which contain at least two hydrogen atoms which are active towards isocyanates and
c) catalysts, optionally in the presence of
d) further auxiliary substances and additives,
in which organic or mineral hollow microbeads having an average particle size in the range from 5 to 200 &mgr;m and a density in the range from 0.1 to 0.8 g/cm
3
are added to at least one of components a) to d).
The coatings according to the invention are suitable for rolls or pipes such as are employed in the steel industry, conveying and transportation industry and in the paper industry. Pipes with an external coating for industrial and pipes with an internal coating for hydraulic conveying of abrasive goods can also be produced by this process. If required, the areas to be coated must be provided with an adhesion promoter beforehand.
However, pipes or other hollow bodies can also be produced by the new process by coating a removable core. In this case, a release agent must be applied to the core or a release film must be wound around it. Finally, the new process can also be used to provide pipes with a thermal insulation jacket of rigid polyurethane foam.
It has been found not only that the new process is suitable for internal and external coating of rotationally symmetric bodies, but that bodies which have diameters which differ over the length and/or cross-section can also be coated.
The process according to the invention is particularly suitable for coating pipes for the offshore sector, in particular for pipes for a depth of more than 500 m which are exposed to a pressure load of greater than 50 bar and a temperature of greater than 120° C.
The reaction components are liquid reaction mixtures which react to form massive or foamed, preferably rigid polyurethane plastics, which optionally contain isocyanurate groups. They are mixtures of organic, preferably aromatic polyisocyanates with compounds which contain at least two hydrogen atoms which are active towards isocyanates, in particular organic polyhydroxy compounds, the polyisocyanates being employed in approximately equivalent amounts, based on the hydroxyl groups, for the preparation of pure polyurethanes and being employed in excess amounts for the preparation of isocyanurate-modified polyurethanes. This means that the isocyanate index is in general within the range from 90 to 2,000, preferably 100 to 1,800. “Isocyanate index” here is to be understood as meaning the number of isocyanate groups of the polyisocyanate component per 100 hydroxyl groups of the polyhydroxy component.
Suitable systems which react to give polyurethanes are described. for example, in DE-PS 16 94 138, while systems according to DE-PS 25 34 247 can be employed as casting compositions which react to give isocyanurate-modified polyurethanes.
The customary auxiliary substances and additives, i.e. catalysts for the isocyanate addition reaction, such as dimethylbenzylamine, dibutyltin dilaurate or permethylated diethylenetriamine, catalysts for the trimerization of isocyanate groups of the type described in DE-PS 25 34 247, or fillers, such as, for example, glass fibres, aluminium hydroxide, talc, chalk, dolomite, mica, barite or wollastonite (CaSiO
3
), can be added to the casting compositions.
However, it is essential to the invention that mineral and/or pressure-resistant, heat-stable plastics having a hollow microstructure are present in the reaction components from 0.5% up to a maximum filling, without generation of additional hollow spaces, based on the total weight of the reaction components.
The maximum filling is calculated as follows:
&rgr;
hollow body
=
density of the hollow microbody
&rgr;
bulk
=
mean bulk density of the hollow microbodies
&rgr;
PUR
=
density of the polyurethane matrix
Free space
=
space remaining between the poured hollow bodies
compacted to the maximum
Free space
=
&rgr;
hollow body
− &rgr;
bulk
To achieve flow of the matrix during the reaction, at least 1 wt. % excess matrix must be present with respect to the free space. The maximum filling is thus given by the following formula:
Minimum amount of PUR per 100 g hollow bodies
Minimum amount of matrix=&rgr;
PUR
*(1/&rgr;
bulk
-1/&rgr;
hollow bodies
)*1.01*100
The minimum PUR matrix calculated from the above formula has a preferred index of between 1,000 and 1,600.
Mineral hollow microbeads are preferably employed. Mineral hollow microbeads in the density range from 0.1 to 0.8 g/cm
3
and having an average particle size of 5 to 200 /&mgr;m and a compressive strength greater than 50 bar are particularly preferred here. Such hollow bodies are commercially obtainable, for example, under the name Q-CEL″ (Omya GmbH) and Scotchlite″ Glas Bubbles (3M Deutschland GmbH).
For the preparation of the casting compositions, the additives which are essential to the invention can be added either to the polyisocyanate component or to the polyhydroxy component or to both beforehand, and also directly before the reaction.
The production of the insulating layer, preferably on pipes, is carried out either by the rotary coating process described in EP-A-636 467, or by conventional casting in moulds with the corresponding pipe parts as the insert.
The insulating coatings produced according to the invention usually have a density of less than 0.9 g/cm
3
, preferably a density between 0.5 and 0.8 g/cm
3
. The thermal conductivity for the insulating coatings produced according to the invention is advantageously less than 0.180 W/m.K. The insulating coatings according to the invention furthermore have a very high pressure resistance of greater than 50 bar and a high heat stability of greater than 120° C.
EXAMPLES
Both pipe coatings obtained by the rotary coating process and those obtained by the conventional casting process are described in the following examples.
General Production Instructions
Components A and B listed in the examples were prepared individually by mixing the individual constituents under mild conditions and then evacuating the mixture for the purpose of degassing before metering. The metering was carried out via special filler-capable low-pulsation metering pumps and

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Pressure resistant and heat-stable insulating coatings for... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Pressure resistant and heat-stable insulating coatings for..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Pressure resistant and heat-stable insulating coatings for... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2916411

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.