Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Processes of preparing a desired or intentional composition...
Reexamination Certificate
2001-01-03
2003-04-08
Cain, Edward J. (Department: 1714)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Processes of preparing a desired or intentional composition...
Reexamination Certificate
active
06545074
ABSTRACT:
This application claims priority to Republic of Korea Patent Application 1999-26438 filed Jul. 02, 1999; Republic of Korea Patent Application 2000-35828 filed Jun. 28, 2000 and PCT application PCT/KR00/00678 filed Jun. 29, 2000.
TECHNICAL FIELD
This invention relates to a polyurethaneurea elastic fiber which is excellent in the weather resistance, and a process of preparing the same.
BACKGROUND ART
A polyurethane type elastic fiber is excellent in elasticity and elastic recovery so that it has been used widely in a stockings, an underwear for women, a sportswear, a swimming suit and like. However, if the polyurethane type elastic fiber is exposed to the atmosphere, there are problems that the original properties thereof and the orignal color thereof are changed by the sunlight and easily transformed by the waste gas among the atmosphere; and also it is easy to be oxidized by natural outside air so that the original properties are deteriorated.
To complement these faults, Korean Patent Application No. 90-10867 disclosed the method that phenol type antioxidants, amine type ultraviolet stabilizers and methacrylate type yellowing inhibitors are used as additives, but there is a fault that the methacrylate types are weak in heat resistance so as to be exuded and sublimated outward the polymer when it was spun at high temperature to make troubles in processing.
In U.S. Pat. No. 4548975, the method is disclosed that the stabilizing effect to the oxidation and the heat are increased by using a phenol type antioxidant and an phosphite type antioxidant, but there is a fault that the properties and the colors of the urethane type elastic fiber produced are easily changed by the sunshine.
In Korean Patent Publication No. 93-11337, the method is described that an weatherability elastomer is manufactured by using phenol type antioxidant, phosphite type antioxidant, semicarbazide type yellowing inhibitor and benzotriazol type light stabilizer, but there is a problem that the benzotriazol type light stabilizer has little heat resistance and compatibility with the polyurethane elastomer so that it is exuded and sublimated in a spinning process to give a bad effect to the processing.
Korean Patent Application No. 93-28704 describes the method of preparing a chlorine resistance elastic fiber by using inorganic salts, but there is a problem that the technology does not prevent the properties of the elastomer to the light and the heat from deteriorating.
Korean Patent Publication No. 97-7688 describes the composition of using a phenol type antioxidant and a metal salt chlorine resistant, but there is a problem that the method does not prevent the discoloration and the physical properties degradation due to the light.
In Korean Patent Publication No. 96-11609, the resistances to the ultraviolet and the chlorine are promoted by using a benzophenol type light resistant and the inorganic salt chlorine resistant, but there is a problem that the physical properties degradation and the discoloration due to the heat or the waste gas are not prevented.
As described above, many compositions containing various stabilizers to promote the weatherability of a polyurethane type elastomer have been suggested, but there was no technology describing the whole weatherability of light resistance, waste gas resistance, chlorine resistance, oxidation resistance and like; and the method of preparing a polyurethane elastic fiber for the long run under the stable process.
DISCLOSURE OF THE INVENTION
As the invention is designed to solve the above problems, the object of the invention is to provide the method which can produce the polyurethaneurea elastic fiber with the excellent light resistance by using a new type ultraviolet stabilizer under the stable process.
The invention is to provide the polyurethaneurea elastic fiber which is very excellent in light resistance and processing and also maintains its original properties like elasticity as it is, and the preparing method thereof.
The invention relates to a polyurethaneurea elastic fiber which maintains its original properties and is excellent in processing stability and light resistance, and the preparing method thereof.
Particularly, the invention relates to a polyurethaneurea elastic fiber characterized in that the strength maintenance rate thereof after being leaved for 24 hours at the Fade-O-Meter in which the sunshine carbon arc is installed is over 90%.
Also, the invention relates to a polyurethaneurea elastic fiber characterized in that containing the formamidine type ultraviolet adsorber of the following general formula I.
Also, the invention relates to the method of preparing a polyurethaneurea elastic fiber, characterized in that the formamidine type ultraviolet adsorber of the following general formula I is added to the spinning dope.
Wherein, R
1
and R
2
represent each an alkyl group of 1 to 5 carbon atoms.
The invention is characterized in that the formamidine ultraviolet adsorber of formula I is added to the spinning dope in the conventional process of preparing polyurethaneurea elastic fiber.
Hereinafter, the invention will be described in more detail.
First of all, as the conventional polyurethaneurea elastic fiber preparing method, the mixture of diisocyanate compound and the diol compound in a molar ratio of 1.3~2.0 was reacted to yield prepolymer(isocyanate-terminated polyetherurethane), and then the prepolymer was mixed with an appropriate amount of sdvent to provide the solution of prepolymer.
The high molecular weight diol compounds of number average molecular weight 1,500~3,000 are preferably used in prepolymerizing.
Second, diamine compounds and monoamine compounds are added to the above prepolymerization solution, whereby the chains of the prepolymer are extended and/or terminated to produce the polyurethaneurea polymer solution(spinning dope).
At this time, the addition amount of the diamine compounds is preferably 70~99 equivalent weight % of the prepolymer, the addition amount of the monoamine compounds is preferably 1~30 equivalent weight % of the prepolymer. The viscosity of the above polymer solution is preferably regulated to 1,500~5,000 poises at 40° C. for more profitable spinning process.
Next, to the above polyurethaneurea polymer solution (spinning dope), the formamidine type adsorber of the following general formula I is added, and then they are spun to produce the polyurethaneurea elastic fiber according to the invention.
Wherein, R
1
and R
2
represent each an alkyl group of 1 to 5 carbon atoms.
As specific examples of the formamidine type ultraviolet adsorber of the formula I used in the invention, N
2
-(4-ethoxycarbonylphenyl)-N
1
-methyl-N
1
-phenyl formamidine, N
2
-(4-methoxycarbonylphenyl)-N
1
-methyl-N
1
-phenyl formamidine and N
2
-(4-ethoxycarbonlyphenyl)-N
1
-ethyl-N
1
-phenyl formamidine are included.
The fromamidine type ultraviolet adsorbers of the general formula I are preferably added in the amount of 0.1~3.0 weight %, more preferably 0.5~2.0 weight % to polyurethaneurea polymer(solids). If the amount is below 0.1 weight %, the improving effect of the light resistance of the elastic fiber becomes lowered, if the amount is over 3.0 weight %, the processing of a spinning and like becomes unstable.
The invention includes that to the above polyurethaneurea polymer solution are added the formamidine type ultraviolet adsorber of formula I together with additives such as general antioxidants, chlorine resistants and waste gas resistance stabilizers or pigments such as titanium oxide and like.
As antioxidants, steric-hindered phenol type antioxidants can be mainly used, as chlorine resistants, inorganic salt chlorine resistants like zinc oxide can be used, as waste gas resistance stabilizers, semicarbazide type waste gas resistance stabilizers can be used.
More particularly, to the polyurethaneurea polymer(solids), antioxidant 0.1~1.5 weight %, chlorine resistant 0.1~2.0 weight %, waste gas stabilizer 0.1~2.0 weight %, titanium oxide 0.05~4.0 weight % and blue pigment 0.005~0.002 weight % can be added.
The formamidi
Huh Hyung Don
Kwon Il Cheon
Ryu Seok Chul
Cain Edward J.
Kolon Industries Inc.
LandOfFree
Polyurethaneures elastic fiber, and a process of preparing... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Polyurethaneures elastic fiber, and a process of preparing..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Polyurethaneures elastic fiber, and a process of preparing... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3042598