Chemistry: electrical current producing apparatus – product – and – Current producing cell – elements – subcombinations and... – Separator – retainer or spacer insulating structure
Reexamination Certificate
1998-06-26
2002-04-09
Acquah, Samuel A. (Department: 1711)
Chemistry: electrical current producing apparatus, product, and
Current producing cell, elements, subcombinations and...
Separator, retainer or spacer insulating structure
C429S144000, C429S247000, C429S249000, C521S143000, C521S918000, C264S288400, C264S290200
Reexamination Certificate
active
06368742
ABSTRACT:
FIELD OF THE INVENTION
This invention is directed to a polypropylene microporous membrane, made from a beta-nucleated precursor, for use as a battery separator.
BACKGROUND OF THE INVENTION
Polypropylene microporous membranes, made from beta-nucleated precursors, are known. U.S. Pat. Nos. 5,134,174; 5,231,126; 5,317,035; & 5,594,070; EPO Publication No. 632,095; Japanese Kokai No. 7-118429; Chu, F. et al., “Microvoid formation process during the plastic deformation of Beta-form polypropylene”,
POLYMER
v34 n16, 1994; Chu, F. et al., “Crystal transformation and micropore formation during uniaxial drawing of Beta-form polypropylene film”,
POLYMER
v36 n13, 1995; Ikeda, N. et al., “NJ-Star NU-100: A Novel Beta-Nucleator for Polypropylene”,
Polypropylene & World Congress
, Sep. 18-20, 1996; Zhu, W. et al., “A New Polypropylene Microporous Film”,
Polymers for Advanced Technologies,
v7, 1996. Such membranes have been suggested for use as battery separators. U.S. Pat. No. 5,134,174; EPO Publication No. 632,095; Japanese Kokai No. 7-118429. Beta-nucleating agents for polypropylene are also known. U.S. Pat. Nos. 5,134,174; 5,231,126; 5,317,035; & 5,594,070; EPO Publication Nos. 557,721 & 632,095; Japanese Kokai Nos. 7-118429 & 9-176352; Chu, F. et al., “Microvoid formation process during the plastic deformation of Beta-form polypropylene”,
POLYMER
v34 n16, 1994; Chu, F. et al., “Crystal transformation and micropore formation during uniaxial drawing of Beta-form polypropylene film”,
POLYMER
v36 n13, 1995; Ikeda, N. et al., “NJ-Star NU-100: A Novel Beta-Nucleator for Polypropylene”,
Polypropylene & World Congress,
Sep. 18-20, 1996; Zhu, W. et al., “A New Polypropylene Microporous Film”,
Polymers for Advanced Technologies,
v7, 1996.
Commercially viable battery separators need to have a balance of properties. Two of these properties are electrical resistance (ER) and strength, typically measured as puncture strength (PS). Electrical resistance is a measure of the resistance to electrical flow between the anode and cathode and across the separator, and is generally preferred to be as low as possible. The micropores of the battery separator form channels through which electrolyte is in contact with the anode and cathode. Puncture strength is for withstanding the rigors of battery manufacture, among other things. Battery separators are usually extremely thin (approximately 1 mil or 25 micron), and are sandwiched between the anode and cathode which have sufficient surface roughness to cause puncture during the winding or folding of the sandwich. Puncture of the separator may lead to direct contact between the anode and cathode, which renders the battery unsuitable for use.
In U.S. Pat. No. 5,134,174, EPO Publication No. 632,095, and Japanese Kokai No. 7-118429, polypropylene microporous films, made from beta-nucleated precusors, for use as battery separator are disclosed. These films, while theoretically functional as separators, are limited. For example, the limitation of the films disclosed in the U.S. and the Japanese references arises from poor puncture strength. The puncture strength is apparent from the stretching (or drawing) conditions, as well as, the pore size, and the porosity.
Accordingly, there is a need for a polypropylene microporous membrane, made from a beta-nucleated precursor, that is commercially viable as a battery separator.
SUMMARY OF THE INVENTION
A battery separator is a polypropylene microporous membrane, made from a beta-nucleated precursor, and having an electrical resistance of less than 30 ohms-inches per mil, and a puncture strength of greater than 400 grams-force per mil.
DESCRIPTION OF THE INVENTION
A battery, or an electrochemical cell, is a device generally comprising an anode, a cathode, an electrolyte, and a separator. Batteries may be used in portable devices, such as computers, cellular telephones, or the like, or in electric vehicles.
Battery separator, as used herein, refers to a microporous membrane that is used to separate the anode and the cathode, thereby preventing their direct contact, and to contain, in the micropores, the electrolyte. The separator may be a monolayer or a multilayer structure (i.e., a sandwich in which the individual layers may be the same or different) in which the disclosed film may be one of those layers. Other layers may enhance safety (i.e., low-melting or shutdown function, e.g., U.S. Pat. No. 5,691,077) or enhance strength (i.e., cross-plied, e.g., U.S. Pat. No. 5,667,911). The battery separator has a thickness less than 3 mils and preferable less than 1.5 mils.
The battery separator disclosed herein is a polypropylene microporous membrane made from a beta-nucleated precursor. Polypropylene refers to any polymer (e.g., homo -or co-polymer) of predominantly propylene monomers. Preferably, the polypropylene is an isotactic, homopolymer with a melt flow index (MFI) of less than (<) 10. More preferably, the MFI is less than 5. Exemplary polypropylenes include: Huntsman Chemical Corp. of Woodbury, N.J. product 5550 (MFI-5.5); Exxon Chemical Co. of Houston, Tex. product Escorene PP 4352 FI (MFI-about 3) & PP 4292 (MFI-1.5); Aristech Chemical Corp. of Pittsburgh, Pa. product BEPOL (MFI-0.7).
Beta-nucleated precursor refers to a pre-stretched polypropylene film having a beta-crystal structure. Beta-crystals are meta-stable and will revert to alpha-crystals when subjected to a combination of heat and stress. Beta-crystal may be formed in the polypropylene by any number of known techniques, but, the use of a beta-nucleating agent (or beta-nucleator) is preferred. See: U.S. Pat. Nos. 5,134,174; 5,231,126; 5,317,035; & 5,594,070; EPO Publication No. 632,095; Japanese Kokai Nos. 7-118429 & 9-176352; Chu, F. et al., “Microvoid formation process during the plastic deformation of Beta-form polypropylene”,
POLYMER
v34 n16, 1994; Chu, F. et al., “Crystal transformation and micropore formation during uniaxial drawing of Beta-form polypropylene film”,
POLYMER
v36 n13, 1995; Ikeda, N. et al., “NJ-Star NU-100: A Novel Beta-Nucleator for Polypropylene”,
Polypropylene & World Congress
, Sep. 18-20, 1996; Zhu, W. et al., “A New Polypropylene Microporous Film”,
Polymers for Advanced Technologies,
v7, 1996, each of which is incorporated herein by reference. Beta-nucleating agents are commercially available, for example NJ-STAR NU-100 is available from New Japan Chemical Co., Ltd., Osaka, Japan. The amount of beta-crystals in the precursor should be on the order of 45 to 70% as measured by a differential scanning calorimeter (DSC) technique (sample size-10 milligrams, heating rate-10°/min, heating range-25° C. to 200° C., using Seiko Instrument Inc.'s model 220 C). By this technique, the amount of beta-crystal is reported as the ratio of beta-crystal (measured as the area under the beta-crystal peak of the DSC trace) to the sum of beta- and alpha-crystal (the sum of the areas under the beta-crystal and the alpha-crystal peaks). The beta-crystal content of the precursor is not preferably maximized.
The porosity of the foregoing membranes should be in the range of 40-65%, preferably 45-60%, and more preferably 47-57%. Porosity (%) is: [1-(apparent density of membrane/resin density)]×100.
The average pore size should be on the order of 0.03 to 0.25 microns as measured from scanning electron microscope (SEM) photograph, magnification 20,000×. A preferred average pore size is in the range of 0.04-0.10 with the distribution skewed toward the low end of the range.
The electrical resistance of the separator should be less than 30 ohms-inches per mil of thickness. A more preferred range for electrical resistance is less than 20 ohm-inches per mil. The electrical resistance (or resistivity) is measured as follows: A R.A.I. AC Milliohm Resistance Meter, Model 2401 and R.A.I. test cell electrode (from RAI Research Corp. Hauppauge, N.Y.) are used. A 31% by wt KOH solution is used to wet the sample (samples should be methanol primed to ensure complete wetout then soaked in solution for 8 to 24 hours before testing
Fisher Harold M.
Wensley C. Glen
Acquah Samuel A.
Celgard Inc.
Hammer III Robert H.
LandOfFree
Polypropylene microporous membrane for battery separator does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Polypropylene microporous membrane for battery separator, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Polypropylene microporous membrane for battery separator will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2888262