Polymer non-aqueous dispersion, process for preparing the same a

Details Polymer non-aqueous dispersion, process for preparing the same a Polymer non-aqueous dispersion, process for preparing the same a

1989-07-24

1990-10-16

Schofer, Joseph L.

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

Processes of preparing a desired or intentional composition...

524558, 524816, 524845, 524167, C08K 300, C08K 3300

Patent

active

049636014

ABSTRACT:
A process for preparing polymer non-aqueous dispersions to be formulated together with a binder component in coating compositions, which comprises the steps of: (1) emulsion polymerizing a hydroxy group containing .alpha.,.beta.-ethylenically unsaturated monomer, a polyfunctional .alpha.,.beta.-ethylenically unsaturated monomer and an .alpha.,.beta.-ethylenically unsaturated monomer different therefrom by using a water-soluble polymerization initiator, preferably a persulphate, in a soap free system or in the presence of an ester group containing anionic or cationic surfactant; adding an organic solvent, preferably comprising an amphipathic organic solvent, to a resultant polymer aqueous dispersion; and then adding a basic compound catalyst when anionic surfactant is used or an acidic compound catalyst when the cationic surfactant is used, to thereby hydrolyze completely said surfactant and water-soluble polymerization initiator at a temperature not exceeding 95.degree. C. as in the condition of suspension; (2) adding an acidic or basic compound to said suspension to neutralize said basic or acidic compound catalyst: then after adding dispersion stabilizing resin, further adding an amine salt of organic acid, followed by leaving said suspension to stand to separate into organic and water layers; and isolating the organic layer from the water layer; and (3) removing residual water in the organic layer. The resultant polymer non-aqueous dispersion comprises polymer particles having a total ionic group concentration (I) less than 2.times.10.sup.-5 mol/g particle, a hexane tolerance (HT) from 5 to 40 exclusive and a degree of swelling in acetone (S) less than 10, and used with a binder component comprising a polyol resin and a curing agent for preparing coating compositions.

REFERENCES:
patent: 3880796 (1975-04-01), Christenson et al.
patent: 4055607 (1977-10-01), Sullivan et al.
patent: 4075141 (1978-02-01), Porter, Jr. et al.
patent: 4147688 (1979-04-01), Makhlouf et al.
patent: 4209435 (1980-06-01), Backhouse
patent: 4273695 (1981-06-01), Green et al.
patent: 4290932 (1981-09-01), Wright et al.
patent: 4296013 (1981-10-01), Gibbs
patent: 4322328 (1982-03-01), Graetz et al.
patent: 4324714 (1982-04-01), Gibbs et al.
patent: 4377661 (1983-03-01), Wright et al.
patent: 4414357 (1983-11-01), Wright et al.
patent: 4461870 (1984-06-01), Kanda et al.
patent: 4477536 (1984-10-01), Wright et al.
patent: 4530946 (1985-07-01), Kanda et al.
patent: 4540740 (1985-09-01), Olson et al.
patent: 4563372 (1986-01-01), Kurauchi et al.
patent: 4598111 (1986-07-01), Wright et al.
patent: 4611026 (1986-09-01), Olson et al.
patent: 4677152 (1987-06-01), Allen et al.
Journal of Polymer Science, "Microgel: An Idealized Polymer Molecule", vol. XXXIII, pp. 101-117 (1958), Victor E. Shashoua et al.

Affiliated with

Also associated with

Rating

Polymer non-aqueous dispersion, process for preparing the same a does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Polymer non-aqueous dispersion, process for preparing the same a, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Polymer non-aqueous dispersion, process for preparing the same a will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-850291