Polymer alloys including two or more components with...

Fabric (woven – knitted – or nonwoven textile or cloth – etc.) – Woven fabric – Strand material is composed of two or more polymeric...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C442S301000

Reexamination Certificate

active

06828261

ABSTRACT:

FIELD OF THE INVENTION
The present invention concerns a polymer alloy, filaments made thereof, and fabrics made therefrom, which alloy is comprised of two compatible polymers having sufficient interfacial adhesion so as to remain bonded together as an extrudate, characterized in that one of the two component polymers has a higher melting point temperature than the second. Industrial fabrics in which at least a portion of the component filaments are formed from the polymer alloy exhibit reduced susceptibility to curl along their longitudinal edges.
BACKGROUND OF THE INVENTION
Industrial textiles are well known and have a variety of uses, including carpeting, filtration and papermaking. Industrial textiles which are used in papermaking machines to drain and form the incipient paper web, known in the art as forming fabrics, must simultaneously possess a number of physical characteristics for them to be of value. At a minimum, they must be: resistant to abrasive wear, structurally stable, resistant to dimensional changes due to moisture absorption, resistant to stretch and edge curl under tension, as well as resistant to chemical degradation caused by the various materials present in both the stock and in cleansing solutions which are used to clean the fabrics at the prevailing temperatures of use.
Of the various polymers available for use in forming filaments intended for industrial textile applications, those most commonly used in papermaking fabrics are: polyesters, in particular polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polyethylene naphthalate (PEN), and their various copolymers; and polyamides, particularly polycaprolactam or nylon-6 (hereinafter referred to as polyamide-6), polyhexamethylene adipamide or nylon 6/6 (hereinafter referred to as polyamide-6/6), poly(hexamethylene sebacamide or nylon-6/10 (hereinafter referred to as polyamide-6/10), poly(11-aminoundecanoic acid) or nylon-11 (hereinafter referred to as polyamide-11) and poly(hexamethylene dodecanoamide) or nylon-6/12 (hereinafter referred to as polyamide-6/12); other polyamides are known and used.
Although filaments formed from both polyesters and polyamides are suitable for many industrial textile applications, the physical properties of both polymers can be improved, especially when used in the manufacture of industrial textiles intended for modern, high speed papermaking conditions. Polyester filaments generally provide adequate chemical and dimensional stability, and have good crimping and heatsetting characteristics which make them amenable to the weaving and finishing of industrial textiles; however, their resistance to abrasion could be improved so as to increase the service life of the fabrics into which they have been incorporated. Although polyamides have adequate properties for many applications, polyamide filaments have serious deficiencies for weaving and finishing as they exhibit poor crimpability and heatsetting behaviour, and generally do not possess adequate dimensional stability in the moisture range found in the paper making environment.
A further problem is that forming fabrics woven from either polyester, or alternating polyester and polyamide filaments, are subject to edge curl, a phenomenon in which the longitudinal edges of the fabric will either curl up and out of the plane of use, or will curl downwards and run in abrasive contact with the various stationary elements of the papermaking machine. This phenomenon is frequently observed in textiles following their weaving and removal of the fabric from the loom; it is particularly undesirable in forming fabrics which must be flat and generally macroscopically planar when in use so as to form the sheet uniformly, and resist wear along their marginal edges. Edge curl persists in the textile following heatsetting, and is well documented in the patent literature.
Heatsetting is a process used to stabilize a woven or nonwoven textile structure so as to set filament crimp and thereby prevent any deformation of the textile when in use. This is typically accomplished by applying heat to the fabric while it is under tension in at least one direction; the heat will soften the component filaments and lock them in position about one another during cooling. The temperature to which the fabric is heated during the heatsetting process will normally lie between the glass transition temperature and the melting point temperature of the component filaments. The applied tension and heat will cause the filaments to be permanently deformed and crimped about one another at their cross-over points. However, it is quite common for the edges of the textile to remain curled to some extent either up or down out of the plane of the fabric following this heatsetting process, necessitating further treatment (usually of the edges only) in order to render the textile usable.
Numerous attempts have been made to overcome the problems associated with both edge curl and dimensional stability of polyamide filaments in industrial textiles. These can be broadly broken down into mechanical means, chemical and heat treatment means. In the following discussion and hereinafter, the term “filament” is intended to be construed as synonymous with the terms “yarn”, “fiber”, “monofilament” and the like which are common in the textile arts and which are intended to denote a fundamental unit used in the construction of an industrial textile, generally, a fiber of indefinite length.
There are several known mechanical means to accomplish this objective. One method disclosed in U.S. Pat. No. 4,941,239 requires sanding off approximately ¼ of the fabric mass from its outer, paper side surface edges.
Another method disclosed in U.S. Pat. No. 5,546,643 requires cutting slits into the paper side weft yarn knuckles along the lateral edges of the fabrics. This scoring of the weft yarns reduces the ratio between the cross machine direction shrinkage forces acting on the sides of the fabric to reduce the tendency to curl.
Another method known from U.S. Pat. No. 4,452,284 to reduce edge wear and curl is to weave the warp yarns along the longitudinal edges of the fabric at a lower tension than those in the central portion, or to utilize yarns at the lateral edges which are capable or greater elongation than those used in the central portion, such as polyamide edge yarns and polyester central yarns.
Another method proposed in WO 99/00546 to control edge curl is to score and notch the weft yarns along the longitudinal edges of the fabric by means of an ablation laser.
Yet another method disclosed in U.S. Pat. No. 4,453,573 is to utilize a modified, conventional unbalanced weave wherein every second warp pattern is reversed so as to improve fabric drainage and sheet support, as well as eliminate edge curl.
All of these mechanical methods that sand or score the fabric have an adverse impact on fabric life. As well, the methods which include specialized weaving requirements require additional manufacturing time and/or specialized equipment.
It has also been proposed to reduce fabric edge curl by chemical means. U.S. Pat. No. 5,324,392 teaches that monofilament made from a unique polyamide-6 which is manufactured in the specified manner provides good crimp and shrinkage characteristics. These yarns are used as at least the weft yarns in weaving single or multi-layer forming fabrics which are allegedly stable and resist edge curl. Specialized polyester monofilaments have also been proposed in U.S. Pat. No. 5,116,478 for the same intended end use which have similar crimp and shrinkage characteristics, as well as good wear resistance properties.
Another proposal to control edge curl is disclosed in U.S. Pat. No. 4,281,688 wherein the use of a weave pattern which introduces weft yarn floats and/or knuckles of differing sizes is taught.
GB 2,328,452 discloses controlled cooling of industrial textiles by means of a blower located immediately downstream of the heatsetting chamber, or following the return roll, so as to provide a uniform flow of cooling air across the fabric surface to

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Polymer alloys including two or more components with... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Polymer alloys including two or more components with..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Polymer alloys including two or more components with... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3301137

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.