Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Processes of preparing a desired or intentional composition...
Reexamination Certificate
2000-03-07
2002-09-24
Wu, David W. (Department: 1713)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Processes of preparing a desired or intentional composition...
C524S461000
Reexamination Certificate
active
06455616
ABSTRACT:
TECHNICAL FIELD
This invention relates to polyethylene compositions useful in the preparation of cable insulation, semiconducting shields, and jackets.
BACKGROUND INFORMATION
A typical electric power cable generally comprises one or more conductors in a cable core that is surrounded by several layers of polymeric materials including a first semiconducting shield layer (conductor or strand shield), an insulating layer, a second semiconducting shield layer (insulation shield), a metallic tape or wire shield, and a protective jacket. Additional layers within this construction such as moisture impervious materials are often incorporated. Other cable constructions such as plenum and riser cable omit the shield.
Industry is constantly seeking to find polyethylene compositions, which will impart to power cables long-term heat aging stability.
DISCLOSURE OF THE INVENTION
An object of this invention, therefore, is to provide a polyethylene composition useful in power cables, which composition includes a stabilizer characterized by its capability of providing the power cables with long term heat aging stability. Other objects and advantages will become apparent hereinafter.
According to the invention, such a composition has been discovered. The composition comprises:
(a) polyethylene;
(b) as a stabilizer, (A) 1,6-hexanediamine, N,N′-bis(2,2,6,6-tetramethyl-4-piperidinyl)-polymer with 2,4,6-trichloro-1,3,5-triazine, reaction products with N-butyl-1-butanamine and N-butyl-2,2,6,6-tetramethyl-4-piperidinamine (CAS number 192268-64-7) or (B) poly[(6-morpholino-s-triazine-2,4-diyl) [2,2,6,6-tetramethyl-4-piperidyl)imino]-hexamethylene[(2,2,6,6-tetramethyl-4-piperidyl)imino]] (CAS number 082451-48-7); and
(c) an organic peroxide.
DESCRIPTION OF THE PREFERRED EMBODIMENT(S)
Polyethylene, as that term is used herein, is a homopolymer of ethylene or a copolymer of ethylene and a minor proportion of one or more alpha-olefins having 3 to 12 carbon atoms, and preferably 4 to 8 carbon atoms, and, optionally, a diene, or a mixture or blend of such homopolymers and copolymers. The mixture can be a mechanical blend or an in situ blend. Examples of the alpha-olefins are propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, and 1-octene. The polyethylene can also be a copolymer of ethylene and an unsaturated ester such as a vinyl ester, e.g., vinyl acetate or an acrylic or methacrylic acid ester.
The polyethylene can be homogeneous or heterogeneous. The homogeneous polyethylenes usually have a polydispersity (Mw/Mn) in the range of about 1.5 to about 3.5 and an essentially uniform comonomer distribution, and are characterized by single and relatively low DSC melting points. The heterogeneous polyethylenes, on the other hand, have a polydispersity (Mw/Mn) greater than 3.5 and do not have a uniform comonomer distribution. Mw is defined as weight average molecular weight and Mn is defined as number average molecular weight. The polyethylenes can have a density in the range of 0.860 to 0.950 gram per cubic centimeter, and preferably have a density in the range of 0.870 to about 0.930 gram per cubic centimeter. They also can have a melt index in the range of about 0.1 to about 50 grams per 10 minutes.
The polyethylenes can be produced by low or high pressure processes. They can be produced in the gas phase, or in the liquid phase in solutions or slurries by conventional techniques. Low pressure processes are typically run at pressures below 1000 psi whereas high pressure processes are typically run at pressures above 15,000 psi.
Typical catalyst systems, which can be used to prepare these polyethylenes, are magnesium/titanium based catalyst systems, which can be exemplified by the catalyst system described in U.S. Pat. No. 4,302,565 (heterogeneous polyethylenes); vanadium based catalyst systems such as those described in U.S. Pat. Nos. 4,508,842 (heterogeneous polyethylenes) and 5,332,793, 5,342,907, and 5,410,003 (homogeneous polyethylenes); a chromium based catalyst system such as that described in U.S. Pat. No. 4,101,445; a metallocene catalyst system such as those described in U.S. Pat. Nos. 4,937,299, 5,272,236, 5,278,272, and 5,317,036 (homogeneous polyethylenes); or other transition metal catalyst systems. Many of these catalyst systems are often referred to as Ziegler-Natta catalyst systems or Phillips catalyst systems. Catalyst systems, which use chromium or molybdenum oxides on silica-alumina supports, can be included here. Typical processes for preparing the polyethylenes are also described in the aforementioned patents. Typical in situ polyethylene blends and processes and catalyst systems for providing same are described in U.S. Pat. Nos. 5,371,145 and 5,405,901. The various polyethylenes can include low density homopolymers of ethylene made by high pressure processes (HP-LDPEs), linear low density polyethylenes (LLDPEs), very low density polyethylenes (VLDPEs), medium density polyethylenes (MDPEs), high density polyethylene (HDPE) having a density greater than 0.940 gram per cubic centimeter and metallocene copolymers with densities less than 0.900 gram per cubic centimeter. The latter five polyethylenes are generally made by low pressure processes. A conventional high pressure process is described in Introduction to Polymer Chemistry, Stille, Wiley and Sons, New York, 1962, pages 149 to 151. The high pressure processes are typically free radical initiated polymerizations conducted in a tubular reactor or a stirred autoclave. In the stirred autoclave, the pressure is in the range of about 10,000 to 30,000 psi and the temperature is in the range of about 175 to about 250 degrees C., and in the tubular reactor, the pressure is in the range of about 25,000 to about 45,000 psi and the temperature is in the range of about 200 to about 350 degrees C. Blends of high pressure polyethylene and metallocene resins are particularly suited for use in the application, the former component for its excellent processability and the latter for its flexibility.
Copolymers comprised of ethylene and unsaturated esters are well known, and can be prepared by the conventional high pressure techniques described above. The unsaturated esters can be alkyl acrylates, alkyl methacrylates, and vinyl carboxylates. The alkyl group can have 1 to 8 carbon atoms and preferably has 1 to 4 carbon atoms. The carboxylate group can have 2 to 8 carbon atoms and preferably has 2 to 5 carbon atoms. The portion of the copolymer attributed to the ester comonomer can be in the range of about 5 to about 50 percent by weight based on the weight of the copolymer, and is preferably in the range of about 15 to about 40 percent by weight. Examples of the acrylates and methacrylates are ethyl acrylate, methyl acrylate, methyl methacrylate, t-butyl acrylate, n-butyl acrylate, n-butyl methacrylate, and 2-ethylhexyl acrylate. Examples of the vinyl carboxylates are vinyl acetate, vinyl propionate, and vinyl butanoate. The melt index of the ethylene/unsaturated ester copolymers can be in the range of about 0.5 to about 50 grams per 10 minutes, and is preferably in the range of about 2 to about 25 grams per 10 minutes. One process for the preparation of a copolymer of ethylene and an unsaturated ester is described in U.S. Pat. No. 3,334,081.
The VLDPE can be a copolymer of ethylene and one or more alpha-olefins having 3 to 12 carbon atoms and preferably 3 to 8 carbon atoms. The density of the VLDPE can be in the range of 0.870 to 0.915 gram per cubic centimeter. It can be produced, for example, in the presence of (i) a catalyst containing chromium and titanium, (ii) a catalyst containing magnesium, titanium, a halogen, and an electron donor; or (iii) a catalyst containing vanadium, an electron donor, an alkyl aluminum halide modifier, and a halocarbon promoter. Catalysts and processes for making the VLDPE are described, respectively, in U.S. Pat. Nos. 4,101,445, 4,302,565, and 4,508,842. The melt index of the VLDPE can be in the range of about 0.1 to about 20 grams per 10 minutes and is preferably in the range of about 0
Harlan R.
Union Carbide Chemicals & Plastics Technology Corporation
Wu David W.
LandOfFree
Polyethylene crosslinkable composition does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Polyethylene crosslinkable composition, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Polyethylene crosslinkable composition will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2879930