Polyester heat-shrinkable tube for coating an electrolyte...

Stock material or miscellaneous articles – Hollow or container type article – Shrinkable or shrunk

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C428S036900, C174SDIG008, C264S230000, C264SDIG007

Reexamination Certificate

active

06528133

ABSTRACT:

This application claims priority to Republic of Korean Patent Application 2000-2686 filed Jan. 20, 2000.
1. Field of the Invention
This invention relates to a polyester heat-shrinkable tube for coating an electrolytic condenser.
2. Description of the Related Art
In prior art, polyvinyl chloride (PVC) heat-shrinkable tube has been used in coating an electrolytic condenser for the purpose of the protection and insulation of the condenser. In the above coating process, an electrolytic condenser is coated with polyvinyl chloride heat-shrinkable tube, and then subjected to heat contraction at 230 to 250° C. for 2 to 3 seconds, washed with water at 70 to 80° C. and dry heat treated at 160° C. for about 3 minutes together with dry and heat-resistance test. For the test of the coating layer, pinhole and falling tests have been performed.
However, since the prior polyvinyl chloride heat-shrinkable tube used in coating the electrolytic condenser has a weak heat resistance and strength, serious cracks may occur in the dry heat treatment after the pinhole test. Furthermore, the tube is not completely adhered to the condenser, causing a quality deterioration of the product. Therefore, there has been a strong desire for the development of a heat-shrinkable tube with better heat-resistance, strength, and coating-adhesion property. Furthermore, it has become known that polyvinyl chloride resin cannot be recycled and rather produces dioxin in incineration, causing an environmental pollution to a great extent. In the year of 2000, the use of polyvinyl chloride resin will be strictly prohibited in Europe and Japan.
SUMMARY OF THE INVENTION
The object of the present invention is to provide a polyester heat-shrinkable tube for coating an electrolytic condenser, which has superior heat resistance, strength and coating-adhesion property, so that no cracks may occur in dry-heat treatment after the coating and contraction step, and also that the tube can be tightly adhered to the condenser.
DETAILED DESCRIPTION OF THE INVENTION
The polyester heat-shrinkable tube for coating an electrolytic condenser according to the present invention is molded from a resin composition comprising (a) 80 to 99 wt % of a copolymerized polyester resin having an intrinsic viscosity of 0.65 to 1.0 dl/g, which comprises 1 to 15 mol % of polyethylene naphthalate and 85 to 99 mol % of polyethylene terephthalate, and (b) 1 to 20 wt % of polybutylene terephthalate resin.
As for the above copolymerized polyester resin comprising 1 to 15 mol % of polyethylene naphthalate and 85 to 99 mol % of polyethylene terephthalate, a polyethylene terephthalate copolymer copolymerized with a certain amount of dimethyl ester of naphthalene dicarboxylic acid, or a mixture of copolymerized polyester and polyethylene terephthalate may be used.
The amount of polyethylene naphthalate in the copolymerized polyester resin is preferably in the range of 1 to 15 mol %, so that the copolymerized polyester resin so formed may have a crystallinity enough for easier tube molding. If the amount of polyethylene naphthalate is less than 1 mol %, tube-molding process cannot be properly performed, and in case of exceeding 15 mol %, the crystallization process of the polyester heat-shrinkable tube becomes so slow as to cause a reduction of the heat resistance.
The copolymerized polyester resin used in the present invention can be easily prepared based on a conventional method for manufacturing polyethylene terephthalate. More specifically, when preparing a polyester resin by reacting terephthalic acid or its ester-forming derivative with ethylene glycol or its ester-forming derivative, the copolymerized polyester resin of the present invention can be obtained by substituting 1 to 15 mol % of the acid component with naphthalene carboxylic acid or its ester-forming derivative.
It is preferred that the intrinsic viscosity of the copolymerized polyester resin is in the range of 0.65 to 1.0 dl/g. If the intrinsic viscosity is less than 0.65 dl/g, the resin does not have any favorable mechanical properties but in case of exceeding 1.0 dl/g, a film with thickness of less than 150 &mgr;m cannot be made.
The polybutylene terephthalate resin used in the present invention serves to control the crystallization rate of the total resin composition, thereby contributing much to an easy processing. Further, when the tube thus prepared is coated on the condenser, and then subjected to dry heat treatment at 170° C. for 3 minutes, there can be no space between the tube and the condenser. It is preferred that the amount of polybutylene terephthalate resin is in the range of 1 to 20 wt % of the total composition. If the amount of polybutylene terephthalate is less than 1 wt %, the crystallization process rate remains unchanged, but in case of exceeding 20 wt %, the tube molding process cannot be properly performed due to the increase of the crystallization rate.
The polybutylene terephthalate resin in the present invention may be obtained from a melt mixture of 70 to 90 wt % of polybutylene terephthalate and 0.1 to 30 wt % of pigment.
To control the crystallization rate, 0.01 to 1.0 wt % of metal salt of Benzoic acid or stearic acid may be added to the above composition. The addition of the above metal salt may adjust the crystallization rate to the size of condenser to be coated, thus enhancing its heat resistance.
Further, in order to enhance the flexibility and adhesion property of the heat-shrinkable tube, 1 to 5 wt % of polyester elastomer may be added to the composition.
If desired, it is possible to add stabilizer, pigment, dye, clay, lubricant and flame retardant in preparing the heat-shrinkable tube.
The polyester heat-shrinkable tube for coating an electrolytic condenser according to the present invention can be prepared by molding method such as tube or inflation method in such a manner that the copolymer composition is melted and extruded to form a tube-shaped body, followed by a biaxial drawing.
For example, the polyester heat-shrinkable tube of the present invention can be prepared in the following manner: the copolymer composition is extruded from a cyclic dye of extruder to form an undrawn tube-shaped body. The tube-shaped body so obtained is rapidly cooled in a cool bath and heated at a temperature higher than the second transition point temperature of the copolymer or copolymer mixture, and lower than a fluidized point. Then, the tube-shaped body is subjected to expansion by the addition of a compressed gas such as air or nitrogen gas, and then subjected to drawing in a transversal direction (TD) and a machine direction (MD) of the tube-shaped body using a differential speed roll. This biaxial drawing process may be continuously performed after the Extrusion molding of the tube-shaped body or after winding to a roll in an undrawn state.
As the appropriate thickness of the heat-shrinkable tube after the biaxial drawing is in the range of 50 to 100 &mgr;m, the undrawn tube-shaped body may be prepared considering this.
After the biaxial drawing, it is preferred that the boiling water contraction percentage of a heat-shrinkable tube is in the range of 40 to 60% in a TD and 5 to 15% in a MD. It is also preferred that the drawing ratio is in the range of 1.7 to 2.5 times in a TD and 1 to 1.5 times in a MD.
As mentioned above, when the polyester heat-shrinkable tube according to the present invention is coated and contracted on a condenser (the uneven structure with 24 mm in length and 12.5 mm outer diameter and has a curved surface at 2.5 mm from the bottom and the most deep site has a 11 mm in diameter, which is located at 4 mm from the bottom) with 13.3 mm in inner diameter and 75 &mgr;m in thickness, followed by a drying heat treatment (170° C. for 3 minutes), it is completely adhered to the condenser without producing any actual space between the tube and the condenser.
The polyester heat-shrinkable tube of the present invention, when measured by a differential scanning calorimeter (DSC), has a maximum recrystallization temperature of 110 to 140° C. and exothermic rec

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Polyester heat-shrinkable tube for coating an electrolyte... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Polyester heat-shrinkable tube for coating an electrolyte..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Polyester heat-shrinkable tube for coating an electrolyte... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3034547

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.