Polycarbonate substrates

Details Polycarbonate substrates Polycarbonate substrates

2002-07-10

2004-03-23

Boykin, Terressa (Department: 1711)

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

From phenol, phenol ether, or inorganic phenolate

C359S107000, C369S047360, C369S059110, C369S059240, C428S064700, C528S198000

Reexamination Certificate

active

06710154

ABSTRACT:

The application concerns a method for the production of polycarbonates having high purity and extremely high transmission, particularly with short wavelengths, based on 1,1-bis(4-hydroxyphenyl)-3,3,5-trimethyl cyclohexanone and 4,4-(metaphenylene diisopropyl)diphenol, and use of the polycarbonate thus obtained for the manufacture of optical data stores, and optical data stores manufactured in this way.
Highly pure polycarbonate is required for optical data carriers as the polycarbonate is located in the optical radiation path of the laser and the information structures stored in the polycarbonate exhibit orders of magnitude in the micrometre or submicrometre range. Furthermore, there is a trend towards refining information structures even further—to create more information density—and then to use lasers with shorter wavelengths, e.g. those emitting blue light (<420 nm). The object was therefore to develop data carriers or methods for the manufacture of data carriers that demonstrate elevated transmission in the short-wave light range.
As a further precondition for obtaining high storage densities, the polycarbonate used must have a low refractive index. Such a polycarbonate has previously been described in EP-A-691 361, which refers to the importance of a high light transmission in the polycarbonate. However, this is expressed only as an integrated quantity across the entire wavelength range as >85%. This integrated quantity conveys nothing about the transmission in the significant short-wave range (390 nm to 450 nm), however.
Polycarbonates are generally produced by means of a method known as the phase boundary method, whereby dihydroxydiaryl alkanes in the form of their alkali salts are reacted with phosgene in the heterogeneous phase in the presence of inorganic bases such as caustic soda solution and an organic solvent, in which the product polycarbonate is readily soluble. During the reaction the aqueous phase is emulsified in the organic phase, forming droplets of various sizes. After the reaction the organic phase containing the polycarbonate is conventionally washed several times with an aqueous liquid and separated from the aqueous phase as thoroughly as possible after each washing process.
Aqueous liquids such as dilute mineral acid, particularly HCl or H
3
PO
4
, are used as washing liquids to separate off the catalyst, whereby the concentration of HCl or H
3
PO
4
in the washing liquid is 0.5 to 1.0 wt. %, for example, and demineralised, ultra-finely filtered, low-metal water is used for further cleaning.
Separating vessels, phase separators, centrifuges or coalescers known per se, or combinations of these devices, are used as phase separation devices to separate off the washing liquid.
The polycarbonate is generally removed by evaporating off the solvent at reduced pressure and elevated temperature, or by spray drying. The polycarbonate then accumulates as a powder. The polycarbonate can also be obtained by precipitation out of the organic solution followed by residual drying. Another possibility for evaporation and removal of the (residual) solvent is extrusion, whilst extrusion evaporator technology represents a further alternative.
The object of the present invention is the provision of an improved method for the production of pure polycarbonate that is highly transparent even under short-wave light.
Surprisingly it has now been found that the light transmission of polycarbonate is directly related to the final production stage—removal and evaporation of the solvent—and to further processing. In particular it has been found that the temperature in these process stages has a critical influence on the light transmission property of the polycarbonate with short wavelengths.
The application therefore provides a method for the production and further processing of polycarbonate based on 1,1-bis(4-hydroxyphenyl)-3,3,5-trimethyl cyclohexanone and 4,4-(metaphenylene dilsopropyl)diphenol, characterised in that the polycarbonate is recovered and/or processed further at temperatures of no more than 290° C., preferably no more than 285° C., particularly preferably at temperatures of 240 to particularly no more than 280° C.
The polycarbonate can be produced according to generally known methods. The polycarbonate is preferably produced by means of the phase boundary method, whereby the temperatures according to the invention should not be exceeded in the solvent separation stage nor in any optional subsequent process stages.
In a preferred embodiment, directly after the polycarbonate production reaction, the reaction mixture is filtered and/or the organic polycarbonate phase that has been obtained and separated off is filtered and optionally washed and/or the organic polycarbonate phase separated from the washing liquid is optionally hot-filtered.
Preferably at least two of these filtration process are performed, and in particular all three.
In a preferred variant, especially in the case of hot filtration, the filtration process is performed at least once, preferably twice, particularly preferably at least three times and in particular on a stepwise basis. Stepwise filtration begins with coarser filters and then switches to finer filters. Two-phase media are preferably filtered during the process stage with coarser filters.
In the process stage filters with a small pore size are used for hot filtration. It is important for this that the polycarbonate phase is as homogeneous a solution as possible. This is achieved by heating the organic polycarbonate phase, which generally still contains residues of aqueous washing liquid. The washing liquid is dissolved in the organic solvent and a clear solution formed. The previously dissolved impurities, particularly the dissolved alkali salts, are precipitated out and can be filtered off.
The known freeze-thaw method may also be used in addition to the method described above in order to obtain a homogeneous solution.
Membrane filters and sintered metal filters or bag filters are used as filters to perform the filtration according to the invention. The pore size of the filters is generally 0.05 to 5 &mgr;m, preferably 0.05 to 1.5 &mgr;m, particularly around 0.2 &mgr;m, 0.6 &mgr;m or around 1.0 &mgr;m. Such filters are available commercially, e.g. from Pall GmbH, D-63363 Dreieich, and Krebsboge GmbH, D-42477 Radevormwald (model SIKA-R CU1AS).
Examples of inert organic solvents used in the process are dichloromethane, the various dichloroethanes and chloropropane compounds, chlorobenzene and chlorotoluene; dichloromethane and mixtures of dichloromethane and chlorobenzene are preferably used.
The reaction can be accelerated with catalysts such as tertiary amines, N-alkyl piperidines or onium salts. Tributylamine, triethylamine and N-ethyl piperidine are preferably used. A monofunctional phenol, such as phenol, cumyl phenol, p-tert-butyl phenol or 4-(1,1,3,3-tetramethylbutyl)phenol, can be used as chain terminator and molecular weight regulator. Isatin bis-cresol, for example, can be used as branching agent.
To produce the highly pure polycarbonates the bisphenols are dissolved in the aqueous alkaline phase, preferably caustic soda solution. The chain terminators optionally required to produce copolycarbonates are dissolved in the aqueous alkaline phase in quantities of 1.0 to 20.0 mol % per mol of bisphenol, or are added to it in bulk in an inert organic phase. Phosgene is then introduced into the mixer containing the other reaction components and the polymerisation is performed.
1,1-bis(4-hydroxyphenyl)-3,3,5-trimethyl cyclohexanone and 4,4-(metaphenylene diisopropyl)diphenol (Bisphenol M) and optionally mixtures thereof are used as bisphenols, whereby the 1,1-bis(4-hydroxyphenyl)-3,3,5-trimethyl cyclohexanone is always present in quantities >0.1 mol %. Preferred 1,1-bis(4-hydroxyphenyl)-3,3,5-trimethyl cyclohexanone concentrations are between 40 and 60 mol %. The bisphenol concentrations to be used according to the invention are reacted with carbonic acid components, particularly phosgene.
Optionally used chain terminators includ

Affiliated with

Also associated with

Rating

Polycarbonate substrates does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Polycarbonate substrates, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Polycarbonate substrates will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3243819