ABSTRACT:
The present invention relates to polycarbonate containers, the production and use thereof.
The production of containers from polycarbonate moulding compositions is known. However, the containers exhibit differences in Yellowness Index (YI) and transmission.
Polycarbonates may be produced by the so-called phase interface process. In said process, dihydroxydiarylalkanes are reacted in the form of their alkali salts in aqueous solution with phosgene in the heterogeneous phase in the presence of inorganic bases such as sodium hydroxide solution and an organic solvent, in which the product polycarbonate is readily soluble.
More details relating to the phase interface process are disclosed in Schnell, “
Chemistry and Physics of Polycarbonates
”, Polymer Reviews, Volume 9, Interscience Publishers, New York, London, Sydney 1964.
DE-A 4 129 545 describes a process for producing suspensions of bisphenolates. These may be used in the phase interface process to produce polycarbonate.
Containers made from polycarbonate are used as water bottles, for example. For aesthetic reasons, it is desirable to produce water bottles with a low Yellowness Index (YI) and high transmission. This is the object of the present invention.
This object is achieved by polycarbonate containers with improved light transmission, lower Yellowness Index and improved mechanical properties. These advantageous properties may be achieved if low-oxygen aqueous solutions of alkali salts of bisphenols are used in the production of the polycarbonate.
The present invention thus provides polycarbonate containers, wherein the polycarbonate is produced by the phase interface process and the aqueous solution of an alkali salt of a bisphenol used therein has a content of dissolved oxygen of less than 150 ppb, preferably less than 100 ppb, particularly preferably less than 50 ppb.
The polycarbonate is produced according to the invention in that the other raw materials apart from the aqueous solution of the alkali salt of bisphenol do not contain a noteworthy amount of oxygen. In addition, production is performed with the exclusion of oxygen, as described for example in DE-A 4 227 272.
For example, in a reaction vessel and tubular reactor configuration, the forced circulation loop and the tubular reactors are flooded and the reaction vessel is blanketed with nitrogen, so as to ensure the exclusion of oxygen.
In addition, the present invention provides the production of containers by injection blow moulding or extrusion blow moulding.
Injection blow moulding consists of a combination of injection moulding and blow moulding.
The process proceeds in three stages:
injection moulding of the parison in the plastic temperature range of the polycarbonate
inflation of the parison in the thermoplastic range of the polycarbonate (the core of the injection mould is simultaneously the blowing mandrel)
stripping of the blow moulding and optionally air-cooling of the blowing mandrel
(c.f. S. Anders, A. Kaminski, R. Kappenstein, “Polycarbonate” in Becker/Braun
Kunststoff
-
Handbuch
, Vol. 3/1
, Polycarbonate, Polyacetale, Polyester, Celluloseester
, Carl Hanser Verlag, Munich, Vienna 1992, pages 223 to 225).
In extrusion blow moulding, the pellets are generally melted using a single-screw extruder and moulded by a die to produce a self-supporting tube, which is then surrounded by a blow mould, which pinches the tube at its bottom end. Inside the mould, the tube is inflated, such that the tube is provided with the desired shape. After a period of cooling, the mould is opened and the moulding may be removed (c.f. F. J. Brinkschröder, “Polycarbonate” in Becker/Braun
Kunststoff
-
Handbuch
, Vol. 3/1
, Polycarbonate, Polyacetale, Polyester, Celluloseester
, Carl Hanser Verlag, Munich, Vienna 1992, pages 257 to 264.
For extrusion blow moulding it is advantageous to use a particularly pseudoplastic polycarbonate, so that a high level of melt stability is provided. Branched polycarbonates are particularly pseudoplastic.
To produce the polycarbonate for the containers according to the invention, aqueous solutions of an alkali salt of a bisphenol with a content of dissolved oxygen <150 ppb, preferably <100 ppb, particularly preferably <50 ppb are used, which may be obtained by reacting bisphenols with a dissolved oxygen content <10 ppb with an aqueous alkali hydroxide solution with a dissolved oxygen content <100 ppb under oxygen exclusion.
Preferred alkali salts are the sodium salts of bisphenols.
Bisphenols which may be used according to the invention are those which may be obtained by reacting aromatic hydroxy compounds which are not substituted in the p position and do not contain any second order substituents, such as cyano, carboxy or nitro groups, for example phenol, o- and m-cresol, 2,6-dimethylphenol, o-tert.-butylphenol, 2-methyl-6-tert.-butylphenol, o-cyclohexylphenol, o-phenylphenol, o-isopropylphenol, 2-methyl-6-cyclopentylphenol, o- and m-chlorophenol, 2,3,6-trimethylphenol, preferably phenol, o- and m-cresol, 2,6-dimethylphenol, o-tert.-butylphenol and o-phenylphenol. Phenol and ketones with at least one aliphatic group on the carbonyl function are particularly preferred, for example acetone, methyl ethyl ketone, methyl propyl ketone, methyl isopropyl ketone, diethyl ketone, acetophenone, cyclohexanone, cyclopentanone, methyl-, dimethyl- and trimethylcyclohexanones, which may also comprise geminal methyl groups, e.g. 3,3-dimethyl-5-methylcyclohexanone (hydroisophorone). Acetone, acetophenone, cyclohexanone and the homologues thereof bearing methyl groups are very particularly preferred. Acetone is the most preferable. By providing an inert nitrogen atmosphere throughout the production process, it is ensured that the residual content of dissolved oxygen in the bisphenols is less than 10 ppb.
Bisphenols which may be used according to the invention are, additionally: 3-(4-hydroxyphenyl)-1,1,3-trimethylindan-5-ol; 1,3-di-(2-(4-hydroxyphenyl)-2-propyl)benzene and 1,4-di-(2-(4-hydroxyphenyl)-2-propyl)benzene.
Bisphenols which are particularly preferred are 2,2-bis(4-hydroxyphenyl)propane (i.e. bisphenol A) and 1,1-bis(4-hydroxyphenyl)-3,3,5-trimethylcyclohexane.
The bisphenols or the mixtures thereof are preferably reacted, with the exclusion of oxygen (e.g. by providing an inert nitrogen atmosphere), with aqueous alkali hydroxide solution having a dissolved oxygen content <100 ppb, preferably <20 ppb. The concentration of alkali hydroxide solution is preferably such that the concentration of the resultant solution of an alkali hydroxide is as close as possible to the solubility limit, i.e. in the range of from 15 to 20 wt. %, preferably 16.5 to 18.5 wt. %. The molar ratio of alkali hydroxide to bisphenol is in particular from 1.8:1 to 2.5:1, preferably 1.9:1 to 2.4:1, particularly preferably 2.0:1 to 2.3:1. The bisphenol may be dissolved as a solid in the alkali hydroxide solution. However, it is preferable for it to be added to the alkali hydroxide solution directly as a melt at temperatures of from 20° C. to 90° C., preferably 30° C. to 70° C., without its having to pass through the solid state.
The virtually oxygen-free aqueous alkali hydroxide solution used to produce the aqueous solution of an alkali salt of a bisphenol may be produced by electrolysis. After production, the alkali hydroxide solution should be stored and transported under inert gas. For use in the process according to the invention, the concentration of alkali hydroxide solution obtained during electrolysis is generally reduced by dilution with virtually oxygen-free, fully deionised water. Oxygen is removed from the fully deionised water in a manner known in principle, e.g. catalytically, by degassing or by inert gas stripping.
The aqueous solution thus obtained of an alkali salt of a bisphenol exhibit particularly low colour indexes, which are naturally also dependent on the colour index of the bisphenol used. If a bisphenol is used which has a colour index <10 Hazen (ASTM D 1686), colour indexes of <1.5 Hazen, preferably <1.0 Hazen may be ach
Heydenreich Frieder
Horn Klaus
Hufen Ralf
Kauth Hermann
Kühling Steffen
Bayer Aktiengesellschaft
Gil Joseph C.
Matz Gary F.
Nolan Sandra M.
Preis Aron
LandOfFree
Polycarbonate containers does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Polycarbonate containers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Polycarbonate containers will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3220780