ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a polishing composition useful for finish polishing, particularly final finish polishing, of the surface of a magnetic disk substrate (hereinafter referred to simply as a substrate) in the preparation of a substrate for a magnetic disk to be used for a memory hard disk, i.e. a memory device useful for e.g. a computer. More particularly, the present invention relates to a polishing composition which provides a high stock removal rate in a polishing process for finishing a highly specular surface with a good surface roughness in the preparation of a substrate represented by e.g. a Ni—P disk, a Ni—Fe disk, an aluminum disk, a boron carbide disk or a carbon disk, and which, at the same time, is capable of presenting an excellent polished surface which is useful for a memory hard disk having a large capacity and a high recording density. Further, the present invention relates to a method for producing a memory hard disk by means of such a polishing composition.
2. Discussion of Background
There have been continuing efforts for miniaturization and larger capacity for memory hard disks which are one of memory devices for e.g. computers, and the substrate which is most widely used at present, is one having an electroless Ni—P plating film formed on a blank material. Here, the blank material is one obtained by fairing an aluminum or other base plate by lathe processing by diamond turning, lapping by means of a PVA grindstone prepared by fixing SiC grinding material or other methods, for the purpose of parallelization or planarization. However, by such various fairing methods, a relatively large waviness of the blank material can not completely be removed. And, the electroless Ni—P plating film will be formed along the waviness on the blank material. Accordingly, such a waviness will remain also on the substrate, and nodules or large pits will sometimes be formed on the substrate surface. Here, the “nodules” are bulges having a diameter of at least about 50 &mgr;m, which are formed by bulging of a plating surface at such portions that impurities have been taken into the Ni—P plating film. The “pits” are dents formed by polishing on the surface of the substrate, and “fine pits” are dents having a diameter of less than about 10 &mgr;m, among them.
Accordingly, for the purpose of removing the waviness of the substrate and making the surface smooth and flat, surface polishing is carried out.
On the other hand, along with the increase in the capacity of memory hard disks, the surface recording density is increasing at a rate of a few tens % per year. Accordingly, the space on a memory hard disk occupied by a predetermined amount of recorded information, is narrower than ever, and the magnetic force required for recording tends to be weak. Accordingly, recently, it is required to minimize the flying height of the head, which is a space between the magnetic head and the memory hard disk, and at present, the flying height of the head is reduced to a level of not higher than 1.0 &mgr;inch (about 0.025 &mgr;m).
Further, so-called texturing may sometimes be carried out to impart concentric circular scorelines to the substrate after polishing, for the purposes of preventing sticking of the magnetic head for reading or writing information, to the memory hard disk and preventing nonuniformity of the magnetic field on the memory hard disk due to scorelines in a certain direction different from the rotational direction of the memory hard disk, formed on the substrate surface by polishing. Recently, for the purpose of further reducing the flying height of the head, light texturing is carried out wherein the scorelines formed on the substrate are further reduced, or a non-texture substrate free from scorelines, is employed which is not subjected to texturing. The technology to support such a low flying height of the magnetic head has also been developed, and the reduction of the flying height of the head is being increasingly advanced.
When a memory hard disk surface has a waviness, the magnetic head moves up and down following the waviness of the memory hard disk which is rotated at a very high speed. However, if the waviness exceeds a certain height, or if the width of waviness is small relative to the height, the head will no longer be able to follow the waviness, and the head will collide against the substrate surface, thus resulting in so-called “head crush”, whereby the magnetic head or the magnetic medium on the memory hard disk surface may be damaged, which may cause a trouble to the memory hard disk device, or which may cause an error in reading or writing information.
On the other hand, head crush may occur also when a micro protrusion of a few &mgr;m is present on the memory hard disk surface. Further, when a pit is present on a memory hard disk, it is likely that information can not completely be written in, thus leading to a defect of information so-called a “bit defect” or failure in reading the information, which causes an error.
Accordingly, it is important to minimize the surface roughness of the substrate in the polishing step i.e. the step prior to forming a memory hard disk, and at the same time, it is necessary to completely remove a relatively large waviness as well as micro protrusions, fine pits and other surface defects.
For such a purpose, it used to be common to carry out finishing by one polishing step by means of a polishing composition (hereinafter sometimes referred to as a “slurry” from its nature) comprising aluminum oxide or other various abrasives and water as well as various polishing accelerators. However, by a single polishing step, it has been difficult to satisfy all of the requirements for removing a relatively large waviness as well as surface defects such as nodules and large pits on the substrate surface and for minimizing the surface roughness within a certain period of time. Accordingly, a polishing process comprising two or more steps, has been studied.
In a case where the polishing process comprises two steps, the main purpose of the polishing in the first step will be to remove a relatively large waviness as well as surface defects such as nodules and large pits on the substrate surface, i.e. fairing. Accordingly, a polishing composition is required which has a high ability of correcting the waviness and surface defects without forming deep scratches which can not be removed by polishing in the second step, rather than minimizing the surface roughness. Therefore, as the abrasive in the polishing composition, one having a relatively large particle size is employed for the purpose of increasing the stock removal rate
The purpose of polishing in the second step i.e. finishing or final polishing, is to minimize the surface roughness of the substrate. Accordingly, it is required that the polishing composition is capable of minimizing the surface roughness and capable of preventing formation of micro protrusions, fine pits or other surface defects rather than it has a high ability for correcting a large waviness or surface defects as required for polishing in the first step. Further, from the viewpoint of the productivity, it is also required that the stock removal rate is high. The degree of the surface roughness is determined depending upon the process for producing the substrate, the final recording capacity as a memory hard disk and other conditions. However, depending upon the desired degree of surface roughness, a polishing process comprising more than two steps, may be employed.
Recently, an improvement has been made in processing a blank material by means of a PVA grinder in order to reduce the processing cost, whereby it is intended to reduce the surface roughness of a blank material prior to the use of the main polishing composition so the quality relating to the surface roughness or waviness of the substrate prior to the polishing, is brought to a level after the conventional first polishing step. If such a processing is carried out, the conventional first polishin
Fujimi Incorporated
Marcheschi Michael
Oblon & Spivak, McClelland, Maier & Neustadt P.C.
LandOfFree
Polishing composition and method for producing a memory hard... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Polishing composition and method for producing a memory hard..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Polishing composition and method for producing a memory hard... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2615876