Semiconductor device manufacturing: process – Chemical etching – Combined with the removal of material by nonchemical means
Reexamination Certificate
2001-03-13
2003-01-21
Goudreau, George (Department: 1763)
Semiconductor device manufacturing: process
Chemical etching
Combined with the removal of material by nonchemical means
C438S693000, C216S088000, C216S089000
Reexamination Certificate
active
06509272
ABSTRACT:
FIELD OF THE INVENTION
The present invention pertains to planarization fluid compositions and planarization methods in the fabrication of semiconductor devices. More particularly, the present invention is directed to the use of chelating agents in such fluid compositions and methods.
BACKGROUND OF THE INVENTION
A large fraction of yield losses in wafer fabrication or processing of semiconductor devices is attributed to microcontamination. Contaminants can be organic or inorganic particles, films or molecular compounds, ionic materials, or atomic species. Examples of ionic contaminants are sodium, potassium, lithium, calcium, boron, manganese, sodium, titanium, zirconium, aluminum, sulfur and magnesium. Other damaging elemental impurities include heavy metals, for example, such as iron, copper, nickel, and gold.
The presence of contaminants during wafer processing has become particularly problematic in high density, large scale integration (LSI) technology. For example, contaminants can cause a device to fail by improperly defining patterns, creating unpredictable surface topography, inducing leakage currents through insulating layers, or accelerating device wearout.
Silicon wafers may be exposed to metallic or semimetallic contaminants during, for example, chemical mechanical planarization or polishing (CMP) or during other cleaning operations. CMP may, for example, involve holding or rotating a wafer of semiconductor material against a wetted polishing surface under controlled chemical fluid (i.e. slurry), pressure, and temperature conditions. The fluid typically consists of an abrasive component such as alumina or silica (unless it is utilized with a pad including an abrasive component) and a chemical etchant that chemically interacts with the surface. Generally, such fluid or slurries are quite pure; however, they are not free of contaminants such as the ionic contaminants listed above.
Chemical-mechanical planarization or polishing may be used to produce a surface with the desired end point or thickness. However, metal ions create contamination problems. For example, such contaminants may diffuse into the surface of the wafer and down fracture paths.
It has been reported that phosphonic acid chelating agents added to SC-1 wet cleaning solution (a mixture of NH
4
OH, H
2
H
2
O
3
, and H
2
O) of an RCA clean commonly used to remove particles and organic contaminants on silicon surfaces, reduces certain metallic contamination deposition on a silicon wafer. This conclusion was reached in the article entitled “Thin-Oxide Dielectric Strength Improvement by Adding a Phosphonic Acid Chelating Agent into NH
4
OH—H
2
O
2
Solution” by Akiya et al.,
J. Electrochem. Soc., Vol.
141, No. 10, October 1994. However, such wet cleaning procedures are performed after CMP processing and contamination may have already caused significant contamination problems to the wafer during the CMP process.
For the above reasons, improvements in the CMP process to reduce metal ion contamination of the wafer being processed are needed. The present invention as described below provides such improvements and overcomes the problems described above and those problems which will become apparent to one skilled in the art from the detailed description below.
SUMMARY OF THE INVENTION
The planarization method of the present invention includes providing a wafer having a wafer surface. A pad is positioned for contact with the wafer surface and the wafer surface is planarized using the pad and a fluid composition including a chelating agent. The chelating agent may be one of any water soluble multidentate chelating agent, preferably a water soluble bidentate ionic chelating agent, and more preferably 1,2-ethylenediphosphonic acid (EDP). Further, in one embodiment, the fluid composition may include an abrasive component and in another embodiment, the pad may include an abrasive component.
REFERENCES:
patent: 4193226 (1980-03-01), Gill, Jr. et al.
patent: 4811522 (1989-03-01), Gill, Jr.
patent: 4963283 (1990-10-01), Lapham et al.
patent: 5290361 (1994-03-01), Hayashida et al.
patent: 5366542 (1994-11-01), Yamada et al.
patent: 5391258 (1995-02-01), Brancaleoni et al.
patent: 5421769 (1995-06-01), Schultz et al.
patent: 5476606 (1995-12-01), Brancaleoni et al.
patent: 5480476 (1996-01-01), Cook et al.
patent: 5759917 (1998-06-01), Grover et al.
patent: 5827781 (1998-10-01), Skrovan et al.
patent: 5858813 (1999-01-01), Scherber et al.
patent: 5861054 (1999-01-01), Miyashita et al.
patent: 5876490 (1999-03-01), Ronay
patent: 5916819 (1999-06-01), Skrovan et al.
patent: 6030491 (2000-02-01), Vaartstra
patent: 6060395 (2000-05-01), Skrovan et al.
patent: 6095161 (2000-08-01), Vaartstra
patent: 6136218 (2000-10-01), Skrovan et al.
patent: 6207630 (2001-03-01), Vaartstra
patent: 6280924 (2001-08-01), Skrovan et al.
patent: 39 39 661 (1991-06-01), None
patent: 3-256665 (1991-11-01), None
Achuthan et al., “Uniformity of Removal Rate in the CMP of Silicon Dioxide Films,”Dielectrics for ULSI Multilevel Interconnection Conference (DUMIC) Conference, Feb. 21-22:177-179 (1995).
Akiya et al., “Thin-Oxide Dielectric Strength Improvement by Adding a Phosphonic Acid Chelating Agent into NH4OH-H2O2Solution,”Journal of the Electrochemical Society, 141(10): L139-L142 (1994).
Ernsberger, “Attach of Glass by Chelating Agents,”Journal of the American Ceramic Society, 42(8): 373-375 (1959).
Fang et al., “Determination of the Composition of Viscous Liquid Film on Electropolishing Copper Surface By XPS and AES,”Journal of the Electrochemical Society, 136(12): 3800-3803 (1989).
Meikle Scott
Skrovan John
Goudreau George
Mueting Raasch & Gebhardt, P.A.
LandOfFree
Planarization method using fluid composition including... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Planarization method using fluid composition including..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Planarization method using fluid composition including... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3062878