Pitch fiber bundle and pitch type carbon fiber bundle and...

Plastic and nonmetallic article shaping or treating: processes – Carbonizing to form article – Filaments

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C057S310000, C057S350000, C264S029600, C264S029700, C264S103000, C264S129000, C264S130000, C264S210800, C264S211110, C423S447400, C423S447600, C423S447700, C423S447800, C423S448000

Reexamination Certificate

active

06524501

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to a pitch fiber bundle which is one kind of the precursor of carbon fibers, a pitch type carbon fiber bundle, and a method for the production thereof. Particularly, this invention relates to a pitch fiber bundle which is one kind of the precursor of carbon fibers of a small size fit for the production of woven fabrics of carbon fibers and a carbon fiber prepreg of a low areal weight (“Metsuke” in Japanese), a pitch type carbon fiber bundle, and a method for the production of carbon fibers of a small size, i.e., a method for producing, at low cost and with high operational efficiency, a pitch fiber bundle which is one kind of the precursor of carbon fibers of a small size, a pitch type carbon fiber bundle, and carbon fibers of a small size. The pitch type carbon fibers which are obtained by this invention are fit for the production of lightweight woven fabrics of carbon fibers and carbon fiber prepreg and are used advantageously in various industrial fields covering sports, leisure, and aerospace technology.
2. Description of the Related Art
The pitch type carbon fibers, like pitch fibers which are the precursor thereof, infusibilized fibers, and carbonized fibers, are weak and very difficult to handle as compared with the PAN type carbon fibers which have acrylic fibers as the precursor.
Heretofore, the production of pitch type carbon fibers of a small size has required decreasing the number of filaments during the process of spinning (or extrusion), with the result that the productivity will be conspicuously lowered and, at the same time, the necessity of handling feeble fibers of a small size will be incurred. The production of carbon fibers of a small size on a commercial scale, therefore, embraces factors for degrading productivity and boosting cost. It, therefore, has entailed the problem that lightweight woven fabrics of carbon fibers and carbon fiber prepreg have become highly expensive.
As a measure to cope with this problem, a method which obtains carbon fibers of a small size by producing a carbon fiber bundle provisionally and then dividing this bundle into several bundles has been proposed. The pitch type carbon fibers generally stretch only meagerly, however, because they possess a higher modulus of elasticity than the PAN type carbon fibers. The carbon fiber bundle, therefore, is incapable of being stably divided into smaller bundles of a prescribed size because it copiously produces broken fibers during the course of division.
JP-A-01-250,417 proposes a method which comprises paralleling and twisting not less than two fiber bundles as the precursor of the PAN type carbon fibers into a cord, doubling such cords and firing the doubled cords, and thereafter dividing the fired doubled cords into the individual carbon fiber bundle cords. The carbon fibers produced by this method, however, have the problem that they will not fit fabrication into lightweight prepregs, though they are suitable as sewing threads. Similarly JP-A-09-273,032 and EP-A-0835953 propose a fiber bundle for use in the PAN type carbon fibers, which retains the shape of one tow and permits division into a plurality of small tows prior to use. This fiber bundle, however, encounters great difficulty in being adapted for pitch type carbon fibers because it is required to allow impartation of crimps never attainable with pitch fibers and endure the impact of a winder to be used for doubling small tows.
Then, JP-A-01-229,820 proposes pitch type carbon fibers which have the number of filaments of less than 1,000. The method used for producing these fibers, however, has the problem that the component fibers are fated to succumb to agglutination. It has another problem that the productivity is prominently impaired because extremely brittle pitch fibers are doubled after the spinning which can be carried out at a relatively high speed.
SUMMARY OF THE INVENTION
This invention, with the object of improving the productivity of each of the spinning, infusibilizing, and carbonizing steps which govern the cost of production of carbon fibers of a small size, thereby allowing inexpensive production of pitch type carbon fibers of a small size, has the task of providing a pitch fiber bundle as the precursor of carbon fibers, a pitch type carbon fiber bundle, and a method for the production thereof.
The first mode of this invention provides a pitch fiber bundle which is characterized by forming a second pitch fiber bundle with not less than two first pitch fiber bundles possessing a degree of intertwining of not more than 100 mm and having the first pitch fiber bundles bound in the second pitch fiber bundle at a degree of intertwining in the range of 100 mm-5000 mm.
The second mode of this invention provides a pitch type carbon fiber bundle which is characterized by forming a second carbon fiber bundle with not less than two first carbon fiber bundles possessing a degree of intertwining of not more than 200 mm, having the first carbon fiber bundles bound in the second carbon fiber bundle at a degree of intertwining of not less than 200 mm, and enabling the second carbon fiber bundle to be divided into the first carbon fiber bundles; or a pitch type carbon fiber bundle characterized by being a first fiber bundle resulting from division of the second carbon fiber bundle.
The third mode of this invention provides a method for the production of pitch type carbon fibers by an operation of drawing pitch fibers, characterized by the steps of dividing a plurality of pitch fibers into not less than two fiber bundles, then imparting an intertwining action to the fiber bundles with a current of air thereby forming first fiber bundles, binding a plurality of first fiber bundles together, again imparting an intertwining action to the bound pitch fiber bundles with a current of air, and drawing bound pitch fibers as a second fiber bundle.
This invention, in the production of carbon fibers of a small size, manifests a veritably prominent effect of allowing carbon fibers of a small size to be produced inexpensively with high operational efficiency on a commercial scale by maintaining the same productivity as carbon fibers of a large size at the spinning, infusibilizing, and carbonizing steps which govern the cost of production of carbon fibers and eventually rendering production of carbon fibers of a small size feasible.
The above and other objects, features, and advantages of the present invention will become clear from the following description of the preferred embodiments.


REFERENCES:
patent: 4186179 (1980-01-01), Katsuki et al.
patent: 4466949 (1984-08-01), Mori
patent: 4895712 (1990-01-01), Komine et al.
patent: 5183603 (1993-02-01), Kitajima et al.
patent: 5425931 (1995-06-01), Arai et al.
patent: 0 825 953 (1998-04-01), None
patent: 1-229820 (1989-09-01), None
patent: 1-250417 (1989-10-01), None
patent: 05295620 (1993-11-01), None
patent: 6-146119 (1994-05-01), None
patent: 9-273032 (1997-10-01), None
patent: 10-121325 (1998-05-01), None

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Pitch fiber bundle and pitch type carbon fiber bundle and... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Pitch fiber bundle and pitch type carbon fiber bundle and..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Pitch fiber bundle and pitch type carbon fiber bundle and... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3168665

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.