ABSTRACT:

BACKGROUND OF THE INVENTION AND RELATED ART STATEMENT
The present invention relates to unimorph- and bimorph-type piezoelectric/electrostrictive elements used as various transducers and various actuators.
A piezoelectric/electrostrictive element is used in various fields such as various transducers for converting electrical energy into mechanical energy, that is, electrical energy into mechanical displacement, force, or vibration, and vice versa, various actuators, frequency-region functional components including various actuators and filters, various display devices including displays, sounding bodies including loudspeakers, microphones, and sensors including ultrasonic sensors.
For example, there are disclosed a piezoelectric/electrostrictive element comprising a film-type piezoelectric/electrostrictive operating portion
5
constituted with a ceramic substrate
1
serving as a diaphragm and a first electrode film
2
, a piezoelectric/electrostrictive film
3
, and a second electrode film
4
formed on the ceramic substrate
1
(Japanese Patent Application Laid-Open No. 3-128681) as shown in FIG.
1
(
a
), and a piezoelectric/electrostrictive element in which a ceramic substrate has a cavity, the bottom of the cavity is constituted so as to be a thin-wall portion, and a piezoelectric/electrostrictive operating portion is integrated on the outer surface of the thin-wall portion (Japanese Patent Application Laid-Open No. 5-49270) as shown in FIG
1
(
b
).
Moreover, a ceramic substrate using zirconium oxide partially stabilized with yttrium oxide is generally known as the ceramic substrate constituting a piezoelectric/electrostrictive element
7
(Japanese Patent Application Laid-Open Nos. 5-29675, 5-97437, and 5-270912).
In the case of the above piezoelectric/electrostrictive element, however, when forming a piezoelectric/electrostrictive operating portion
5
on the ceramic substrate
1
and firing the piezoelectric/electrostrictive operating-portion
5
in the fabrication process of the piezoelectric/electrostrictive element, a crack maybe recognized at a specific portion, that is, at a portion of ceramic-substrate
1
near the boundary of the first electrode film
2
as shown in FIGS.
2
(
a
) and
2
(
b
) particularly through heat treatment (firing) for integrating the piezoelectric/electrostrictive film
3
with the first electrode film
2
and the ceramic substrate
1
depending on the firing condition, and thereby a problem occurs that the production yield is lowered.
As a result of observing the vicinity of the portion where the crack occurs with an electron-probe microanalyzer (EPMA), it is found that the amount of yttrium oxide serving as a stabilizer for zirconium oxide is small as compared with other portions. Though the reason why the yttrium oxide is decreased is not known, it is estimated that, because the above portion is a portion which piezoelectric/electrostrictive film
3
directly contacts the ceramic substrate
1
when the piezoelectric/electrostrictive film
3
protrudes over the first electrode film
2
on the ceramic substrate
1
in order to prevent a short circuit from occurring between upper and lower electrodes, the yttrium oxide selectively diffuses to the piezoelectric/electrostrictive film
3
when the film
3
is sintered and integrated. Moreover, from the viewpoint of device structure, the vicinity of the boundary of the first electrode film
2
on the ceramic substrate
1
is a portion to which a large stress is easily applied to integrate the piezoelectric/electrostrictive film
3
, first electrode film
5
, and ceramic substrate
1
through heat treatment. Particularly, when the substrate has a cavity structure as shown in FIG.
1
(
b
) or FIG.
2
(
b
), it is estimated that the stress under the heat treatment causes a decrease in the yttrium oxide because the stress becomes high particularly in the cavity structure. However, this is not clear. In any case, however, it is strongly estimated that crystal phase transformation of zirconium oxide is induced due to a decrease in the yttrium oxide and this results in the crack formation.
To prevent a crack from occurring, it is considered to fabricate the ceramic substrate
1
with fully stabilized zirconium oxide in an attempt to prevent crystal phase transformation. However, fully stabilized zirconium oxide is inferior to partially stabilized zirconium oxide in mechanical strength. Therefore, for example, even when decreasing the thickness of the ceramic substrate
1
in order to improve the displacing characteristic of an actuator or the sensitivity of a sensor, a problem occurs that the thickness of the ceramic substrate
1
cannot be effectively or sufficiently decreased.
Therefore, though the partially stabilized zirconium oxide, particularly the zirconium oxide partially stabilized with 2 to 4 mol % of yttrium oxide, is superior in diaphragmatic characteristic, the partially stabillized zirconium oxide is susceptible to crystal phase transformation and cracking if the amount of yttrium oxide serving as a stabilizer is decreased due to any factor while sintering the piezoelectric/electrostrictive film
3
as described above. Moreover, the above problem is peculiar to a piezoelectric/electrostrictive element constituted by integrating a ceramic substrate serving as a diaphragm with a film-type piezoelectric/electrostrictive operating portion through heat treatment without using an adhesive or the like.
SUMMARY OF THE INVENTION
The present invention is made to solve the above problems and its object is to provide an advanced-functional and high-performance piezoelectric/electrostrictive element that uses the strength of a ceramic substrate (diaphragm) and preventing a crack from being produced due to an internal factor when firing a piezoelectric/electrostrictive film.
That is, the present invention provides a piezoelectric/electrostrictive-film-type element comprising: a ceramic substrate having a material whose main component is zirconium oxide and at least one film-type piezoelectric/electrostrictive operating portion comprising a first electrode film, a piezoelectric/electrostrictive film, and a second electrode film on the ceramic substrate; wherein the ceramic substrate comprises a base layer and a surface layer, and the crystal phase of the zirconium oxide of the base layer is a tetragonal phase or a mixed crystal phase of tetragonal and cubic phase, tetragonal and monoclinic phase, or tetragonal, cubic, and monoclinic phase, and the crystal phase of the zirconium oxide of the surface layer is mainly a cubic phase, and the piezoelectric/electrostrictive operating portion is formed on the surface layer.
In the piezoelectric/electrostrictive element of the present invention, it is preferable that the zirconium oxide of the surface layer is stabilizedwith 6 to 20 mol % of yttrium oxide. Moreover, it is preferable that the zirconium oxide of the base layer is partially stabilized with 2 to 4 mol % of yttrium oxide. Furthermore, it is preferable that the crystal grain size of the zirconium oxide in the base layer is held within a range of 0.1 and 1.5 &mgr;m.
Furthermore, in the piezoelectric/electrostrictive element of the present invention, it is preferable that only that portion of the ceramic substrate forming a piezoelectric/electrostrictive operating portion is thin-walled. As described later, in the present invention, the thickness of a ceramic substrate is preferably set to 50 &mgr;m or less. Therefore, it is possible to thicken the portion where the diaphram is not present, that is, where, a piezoelectric/electrostrictive operating portion is not formed, and thereby, advantageously handle the ceramic substrate. Moreover, even when arranging devices adjacent to one another, it is possible to set a thick wall portion between elements and this is advantageous in preventing mutual interference between characteristics of the elements.


REFERENCES:
patent: 5126615 (1992-06-01), Takeuchi
patent: 5210455 (1993-05-01), Takeuchi
patent: 5430344 (1995-07-01), Takeuchi
patent: 0 526 048 A1 (1

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Piezoelectric/electrostrictive element does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Piezoelectric/electrostrictive element, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Piezoelectric/electrostrictive element will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2458884

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.