Radiation imagery chemistry: process – composition – or product th – Transfer procedure between image and image layer – image... – Diffusion transfer process – element – or identified image...
Reexamination Certificate
1999-06-17
2001-10-16
Schilling, Richard L. (Department: 1752)
Radiation imagery chemistry: process, composition, or product th
Transfer procedure between image and image layer, image...
Diffusion transfer process, element, or identified image...
C430S227000, C430S248000
Reexamination Certificate
active
06303262
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a photomask material, a photomask and methods for the production thereof. More specifically, it relates to a photomask material for preparing a photomask for fabricating a circuit pattern, which mask is excellent in heat resistance, ultraviolet resistance and image strength and does not cause an environmental pollution, and a method for the production thereof, and it also relates to a photomask having the above properties and a method for the production thereof by a simple method.
2. Related Art Statement
Photomask are frequently used for forming circuit patterns in the production of semiconductor devices, liquid crystal display devices, and the like. The photomask for forming circuit patterns include an emulsion mask prepared by applying a photographic emulsion containing silver halide to a transparent substrate such as a film or a glass and a hard mask prepared by forming a light shielding film of a metal such as chromium, and these masks are generally used. In the emulsion mask, a photosensitive emulsion layer containing silver halide is irradiated with light, and an image is developed to form a black image. The emulsion mask using the above silver halide photography can be easily intensified in sensitivity, and the process for preparing the photomask is very easy. Since, however, the emulsion mask uses gelatin as a main binder for a photosensitive layer, it has defects that it is easily scratched when it is used a plurality of times as a contact photomask and that it is apt to be thermally deteriorated or colored due to heat generated by an exposure light source, or easily optically deteriorated and colored due to an ultraviolet light source.
In the hard mask, generally, a photoresist is applied to a glass substrate (blank) having a metal thin film as a light shielding film, followed by many steps of pre-baking, exposure, development, post-baking, descumming, etching, descumming, resist peeling and washing, to form an image. The hard mask is excellent in image strength, heat resistance and ultraviolet light durability. However, not only the steps of producing the photomask are complicated, but also the hard mask successfully attained no high sensitivity sufficient for a laser light source. Moreover, chromium is a main stream as a material for forming the light shielding film, and in recent years, it is demanded to employ other method eliminating an environmental problem caused by the use of chromium.
Besides the above method, further, as a method for preparing a photomask having a light shielding film formed of a metal thin film on a glass substrate, while using no organic binder such as gelatin, various methods have been proposed in which a silver halide photographic emulsion which can easily attain a high sensitivity is applied.
For example, U.S. Pat. No. 4,168,168 discloses a method in which a photosensitive material having a silver halide emulsion layer on a glass substrate, a so-called emulsion mask structure, is exposed and treated for development, then, the emulsion layer of an exposed portion or an unexposed portion is removed and silver ion or copper ion is supplied to form a metal image in a portion from which the emulsion layer has been removed. In the above heat treatment. U.S. Pat. No. 4,309,495 discloses a method in which a photosensitive material having the above emulsion mask structure is exposed and treated for development and then a developed silver is moved into a glass substrate by the application of a voltage and an increase in temperature, to form an image.
JP-B-53-2727, JP-B-60-41340, JP-A-6-273867, U.S. Pat. No. 3,960,560, U.S. Pat. No. 3,966,473, U.S. Pat. No. 4,113,486, U.S. Pat. No. 4,246,828 and U.S. Pat. No. 4,284,713 disclose methods in which a photosensitive material having a light shielding film formed of a metal or a metal oxide as a masking layer between a glass substrate and a silver halide emulsion layer is exposed and treated for development, a resist is formed on the light shielding film by an etch-bleaching or other method and is etched to peel a mask imagewise.
Further, JP-A-49-9975, JP-A-52-111382 and JP-A-57-26852 disclose methods in which a photosensitive material formed of a glass substrate, a mask layer, a photopolymer layer and a silver halide emulsion layer is exposed to photo-react the silver halide emulsion first, the silver halide emulsion layer is treated for development, then the material is exposed to photo-react the photopolymer and the photopolymer is treated for development and etched, to peel a mask imagewise.
As described above, the above conventional methods of forming a metal thin film by applying a silver halide emulsion requires complicated steps of exposure, heating after development, etching, application of a voltage, and the like, and there is desired a photomask having a light shielding film formed of a metal thin film on a glass substrate, which can be produced by a simple method.
DISCLOSURE OF THE INVENTION
It is a first object of the present invention to provide a photomask material for forming a photomask, which is excellent in heat resistance, ultraviolet light durability and image strength and is free from environmental pollution, and which can be obtained by a simple process.
It is a second object of the present invention to provide a method for the production of the above photomask material.
It is a third object of the present invention to provide a photomask, which has the above excellent properties.
It is a fourth object of the present invention to provide a method for the production of the above photomask with a high sensitivity by a simple method.
The present inventors have made diligent studies for achieving the above objects, and as a result, have found the following.
A desired photomask material can be obtained by forming a physical development nucleus layer on a transparent substrate and applying an emulsion containing silver halide thereon to form a photosensitive layer, whereby the above first and second object of the present invention are achieved.
A desired photomask can be obtained by exposing imagewise the photosensitive layer of the above photomask material; treating the photosensitive layer for development to reduce silver halide of an exposed portion in the photosensitive layer and to dissolve the silver halide of the unexposed portion; forming a desired pattern of a silver film on the physical development nucleus layer by the action of the physical development nucleus; and further, removing the photosensitive layer, whereby the above third and fourth objects of the present invention are achieved. The present invention has been completed on the above findings.
That is, according to the present invention, the above first object of the present invention is achieved by a photomask material, which comprises a glass substrate, a physical development nucleus layer and a photosensitive layer containing silver halide, the layers being consecutively formed on the transparent substrate.
According to the present invention, the above second object of the present invention is achieved by a method for the production of a photomask material, which comprises applying a coating liquid containing a physical development nucleus to a transparent substrate to form a physical development nucleus layer, and then applying an emulsion containing silver halide thereto to form a photosensitive layer.
According to the present invention, further, the above third object of the present invention is achieved by a photomask, which comprises a transparent substrate, a physical development nucleus layer and a light shielding film formed of a predetermined pattern of a silver film derived from silver halide, the silver film being formed by the action of the physical development nucleus in said layer during development treatment, the physical development nucleus layer and the light shielding film being consecutively formed on the transparent substrate.
Further, according to the present invention, the fourth object of the present inve
Hyodo Kenji
Kawai Noriyuki
Takaoka Kazuchiyo
Mitsubishi Paper Mills Ltd.
Nixon & Vanderhye
Schilling Richard L.
LandOfFree
Photomask material, photomask and methods for the production... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Photomask material, photomask and methods for the production..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Photomask material, photomask and methods for the production... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2590618